Crystallizable vinylidene chloride polymer powders and acrylic fibers containing same
Assignee: Dow Chemical Co
•
Filing: 1978-09-15
•
Granted: 1980-01-29
•
Expires: 1998-09-15
Abstract
Abstract A crystallizable vinylidene chloride polymer powder is recovered from a latex obtained by emulsion polymerizing in sequence (a) a first monomer mixture comprising a predominant amount of vinylidene chloride and an ethylenically unsaturated comonomer which is copolymerizable therewith, such as acrylonitrile; (b) a minor amount of a polyfunctional monomer for providing graft sites on the product of (a); and (c) a second monomer mixture which is predominantly acrylonitrile, the amount of the second monomer mixture being in the range of about 10 to about 25 percent of the weight of the first monomer mixture. The so-formed solvent is admixed with an acrylic polymer and a suitable solvent and then spun into fibers having improved flame-retardancy.
Inventors
- 👤 Dale S. Gibbs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:28
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/44; D01F6/54; C; C08; C08L; C08L33/00; C08L33/18; C08L33/20; D01F1/00; D01F1/02; D01F1/07
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
137 words
A crystallizable vinylidene chloride polymer powder which can be incorporated in acrylic fibers as a flame-retardant additive, said powder being recovered from a latex obtained by emulsion polymerizing in sequence (a) a first monomer mixture comprising about 85 to about 95 weight percent vinylidene chloride and about 5 to about 15 weight percent of a copolymerizable ethylenically unsaturated comonomer; (b) a minor amount of a polyfunctional comonomer for providing graft sites on the product of (a); and (c) about 10 to about 25 weight percent, based on the weight of the first monomer mixture, of a second monomer mixture comprising about 85 to about 95 weight percent acrylonitrile and about 5 to about 15 weight percent of a copolymerizable ethylenically unsaturated comonomer; wherein the particles in the resulting latex have a diameter less than about 1 micron.
Claim 2
Dependent Claim
137 words
A crystallizable vinylidene chloride polymer powder which can be incorporated in acrylic fibers as a flame-retardant additive, said powder being recovered from a latex obtained by emulsion polymerizing in sequence (a) a first monomer mixture comprising about 85 to about 95 weight percent vinylidene chloride and about 5 to about 15 weight percent of a copolymerizable ethylenically unsaturated comonomer; (b) a minor amount of a polyfunctional comonomer for providing graft sites on the product of (a); and (c) about 10 to about 25 weight percent, based on the weight of the first monomer mixture, of a second monomer mixture comprising about 85 to about 95 weight percent acrylonitrile and about 5 to about 15 weight percent of a copolymerizable ethylenically unsaturated comonomer; wherein the particles in the resulting latex have a diameter less than about 1 micron.
Claim 3
Dependent Claim
26 words
A powder according to claim 1 wherein the proportion of vinylidene chloride in the first monomer mixture ranges from about 90 to about 95 weight percent.
Claim 4
Dependent Claim
35 words
A powder according to claim 1 wherein the copolymerizable ethylenicaly unsaturated comonomer of (a) is selected from the group consisting of alkyl esters of acrylic and methacrylic acids and nitriles of ethylenically unsaturated carboxylic acids.
Claim 5
Dependent Claim
16 words
A powder according to claim 1 wherein the copolymerizable ethylenically unsaturated comonomer of (a) comprises acrylonitrile.
Claim 6
Dependent Claim
18 words
A powder according to claim 1 wherein the polyfunctional comonomer of (b) comprises a conjugated diolefinically unsaturated monomer.
Claim 7
Dependent Claim
33 words
A powder according to claim 1 wherein the amount of the polyfunctional comonomer of (b) ranges from about 1 to about 5 weight percent, based on the weight of the first monomer mixture.
Claim 8
Dependent Claim
12 words
A powder according to claim 1 wherein the polyfunctional comonomer comprises 1,3-butadiene.
Claim 9
Dependent Claim
25 words
A powder according to claim 1 wherein the amount of acrylonitrile in the second monomer mixture ranges from about 85 to about 90 weight percent.
Claim 10
Dependent Claim
27 words
A powder according to claim 1 wherein the ethylenically unsaturated comonomer of (c) is selected from the group consisting of alkyl esters of acrylic and methacrylic acids.
Claim 11
Dependent Claim
26 words
A powder according to claim 1 wherein the particles in the resulting latex have a diameter in the range of about 0.1 to about 0.5 micron.
Claim 12
Dependent Claim
41 words
A spinning solution for the preparation of flame-retardant acrylic fibers comprising (a) a fiber-forming polymer containing at least 85 weight percent acrylonitrile; (b) a solvent for the fiber-forming polymer; and (c) a crystallizable vinylidene chloride polymer powder according to claim 1.
Claim 13
Dependent Claim
38 words
A process for forming the spinning solution of claim 11 which comprises (a) forming a generally uniform dispersion of the solvent and the crystallizable vinylidene chloride polymer powder; and (b) admixing the fiber-forming polymer with the so-formed dispersion.
Claim 14
Dependent Claim
11 words
An acrylic fiber obtained by spinning the solution of claim 11.
References Cited (Backward Citations)
US2949437A
Cited
US3288888A
Cited
US4145380A
Cited
US3963790A
Cited
US4081498A
Cited
US4101621A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-28 | 1983-07-30 | 1984-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-28 | 1987-07-30 | 1988-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-28 | 1991-07-30 | 1992-01-29 | $7700.00 | Window Closed / Lapsed |