Process for the production of methane-containing gases and catalyst used in process
Assignee: British Gas PLC
•
Filing: 1978-02-15
•
Granted: 1980-01-29
•
Expires: 1998-02-15
Abstract
Abstract Steam reforming catalysts which are suitable for the gasification of hydrocarbons, particularly heavier hydrocarbons such as kerosene and gas oils, consist of calcined and reduced forms of a basic mixed carbonate of nickel, aluminium and chromium produced by coprecipitation. The catalysts are further characterized in that they have a pore size distribution such that at least 55% by volume of the pores of the calcined but unreduced catalyst which have a pore radius of 12-120A is in the range 12-30A. The catalysts are produced by coprecipitation, preferably at temperatures of not more than 60° C., by using an alkali carbonate as the precipitant and by adding the precipitant to a mixed solution of alumium, nickel and chromium III compounds. The catalysts which have good sinter and polymer resistance may be used for the production of methane-containing gases, e.g., for the production of substitute natural gas.
Inventors
- 👤 Costa Komodromos
- 👤 Alan Williams
- 👤 Norman Parkyns
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:24
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05; B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J23/86; B01J23/866; C01; C01B; C01B3/00; C01B3/02; C01B3/32; C01B3/34; C01B3/38; C01B3/40; B01J35/00; B01J35/60; C01B2203/00; C01B2203/10; C01B2203/1041; C01B2203/1047; C01B2203/1052; C10G2400/00; C10G2400/26; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
69 words
A catalyst precursor for use in the steam reforming of hydrocarbons which consists of a calcined form of a coprecipitated basic carbonate of the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; and wherein at least 55% by volume of the pores therein having a pore radius of from 12-120 A have a pore radius in the range of from 12-30 A.
Claim 2
Dependent Claim
69 words
A catalyst precursor for use in the steam reforming of hydrocarbons which consists of a calcined form of a coprecipitated basic carbonate of the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; and wherein at least 55% by volume of the pores therein having a pore radius of from 12-120 A have a pore radius in the range of from 12-30 A.
Claim 3
Dependent Claim
16 words
A catalyst precursor as claimed in claim 1, wherein the ratio of b/c equals about 9:1.
Claim 4
Dependent Claim
26 words
A catalyst precursor as claimed in claim 1, wherein sodium and/or potassium are present in amounts not exceeding 0.01% by weight and 0.4% by weight, respectively.
Claim 5
Dependent Claim
117 words
A process for preparing a catalyst for use in the steam reforming of hydrocarbons, said process consisting of precipitating a basic carbonate from an aqueous solution of an alkali carbonate and a mixture of water-soluble compounds of nickel, aluminum and chromium (III), said basic carbonate having the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; drying said precipitate; calcining said dried precipitate, said calcined precipitate having at least 55% by volume of the pores therein having a pore radium of from 12-120 A have a pore radius in the range of from 12-30 A; and contacting said calcined precipitate with hydrogen at a temperature sufficient to reduce said calcined precipitate.
Claim 6
Dependent Claim
117 words
A process for preparing a catalyst for use in the steam reforming of hydrocarbons, said process consisting of precipitating a basic carbonate from an aqueous solution of an alkali carbonate and a mixture of water-soluble compounds of nickel, aluminum and chromium (III), said basic carbonate having the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; drying said precipitate; calcining said dried precipitate, said calcined precipitate having at least 55% by volume of the pores therein having a pore radium of from 12-120 A have a pore radius in the range of from 12-30 A; and contacting said calcined precipitate with hydrogen at a temperature sufficient to reduce said calcined precipitate.
Claim 7
Dependent Claim
23 words
A process as claimed in claim 4, wherein said precipitation step is carried out at a temperature of not more than 60° C.
Claim 8
Dependent Claim
30 words
A process as claimed in claim 4, wherein said precipitation step is effected by adding said alkali carbonate to said aqueous solution containing the nickel, aluminum and chromium (III) compounds.
Claim 9
Dependent Claim
17 words
A process as claimed in claim 4, wherein said precipitation step is carried out at constant temperature.
Claim 10
Dependent Claim
27 words
A process as claimed in claim 4, wherein said drying step is carried out at substantially the same temperature as the temperature employed during said precipitation step.
Claim 11
Dependent Claim
23 words
A process as claimed in claim 4 wherein said alkali carbonate is selected from the group consisting of sodium carbonate and potassium carbonate.
Claim 12
Dependent Claim
27 words
A process as claimed in claim 4 wherein said water-soluble compounds of nickel, aluminum and chromium (III) are, respectively, nickel nitrate, aluminum nitrate and chromium (III) nitrate.
Claim 13
Dependent Claim
133 words
A process for the production of methane-containing gases which comprises contacting a catalyst precursor which consists of a calcined form of a coprecipitated basic carbonate of the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19.1, 2a+3b+3c=18 and x=3.5-55, with hydrogen at a temperature sufficient to reduce said calcined catalyst precursor, said catalyst precursor thus being formed into a catalyst bed; and passing a vapor of a hydrocarbon feedstock having a boiling point of not more than about 360° C. and steam over said catalyst bed to form said methane-containing gases, the temperature of said catalyst bed being maintained at from 350° 650° C. where first contacted by said vapor, the temperature of the remainder of said catalyst bed being maintained by catalyzed vapor reactions at at least 450° C.
Claim 14
Dependent Claim
133 words
A process for the production of methane-containing gases which comprises contacting a catalyst precursor which consists of a calcined form of a coprecipitated basic carbonate of the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19.1, 2a+3b+3c=18 and x=3.5-55, with hydrogen at a temperature sufficient to reduce said calcined catalyst precursor, said catalyst precursor thus being formed into a catalyst bed; and passing a vapor of a hydrocarbon feedstock having a boiling point of not more than about 360° C. and steam over said catalyst bed to form said methane-containing gases, the temperature of said catalyst bed being maintained at from 350° 650° C. where first contacted by said vapor, the temperature of the remainder of said catalyst bed being maintained by catalyzed vapor reactions at at least 450° C.
Claim 15
Dependent Claim
21 words
A process as claimed in claim 11, wherein said hydrocarbon feedstock is naphtha, kerosene, light gas oil or heavy gas oil.
Claim 16
Dependent Claim
19 words
A process as claimed in claim 11, wherein the steam to hydrocarbon feedstock ratio is at least 1.5:1 (w/w).
Claim 17
Dependent Claim
124 words
A catalyst for use in the steam reforming of hydrocarbons which is formed by the steps consisting of coprecipitating a basic carbonate from an aqueous solution of water-soluble compounds of nickel, aluminum and chromium (III) by adding an alkali carbonate precipitant thereto, said basic carbonate having the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; drying said precipitate consisting solely of said basic carbonate; calcining said dried precipitate, said calcined precipitate having at least 55% by volume of the pores therein having a pore radius of from 12-120 A have a pore radius in the range of from 12-30 A; and contacting said calcined precipitate with hydrogen gas at a temperature sufficient to reduce said calcined precipitate.
Claim 18
Dependent Claim
124 words
A catalyst for use in the steam reforming of hydrocarbons which is formed by the steps consisting of coprecipitating a basic carbonate from an aqueous solution of water-soluble compounds of nickel, aluminum and chromium (III) by adding an alkali carbonate precipitant thereto, said basic carbonate having the empirical formula Ni.sub.a Al.sub.b Cr(III).sub.c CO.sub.3 (OH).sub.16 xH.sub.2 O wherein a=4-6.4, b/c=3-19:1, 2a+3b+3c=18 and x=3.5-5.5; drying said precipitate consisting solely of said basic carbonate; calcining said dried precipitate, said calcined precipitate having at least 55% by volume of the pores therein having a pore radius of from 12-120 A have a pore radius in the range of from 12-30 A; and contacting said calcined precipitate with hydrogen gas at a temperature sufficient to reduce said calcined precipitate.
References Cited (Backward Citations)
US3418093A
Cited
US3423194A
Cited
GB1342020A
Cited
US3950368A
Cited
US3990866A
Cited
US4046869A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-28 | 1983-07-30 | 1984-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-28 | 1987-07-30 | 1988-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-28 | 1991-07-30 | 1992-01-29 | $7700.00 | Window Closed / Lapsed |