Process for saturating a fiber mat of open structure
Assignee: Tarkett AB
•
Filing: 1978-06-02
•
Granted: 1980-01-22
•
Expires: 1998-06-02
Abstract
Abstract Heat curable liquid polyvinylchloride plastisol or organosol resin is coated onto a porous fiber web in an amount sufficient to saturate the web. Liquid resin on one surface of the web is gelled by passing the web around a heated roll which, together with another heated roll, forms a compression nip. The web passes through the nip and around the second heated roll to gell the resin on the other surface of the web, after which the curing of the resin is completed in an oven.
Inventors
- 👤 Douglas C. Woerner
- 👤 Andrew J. Manning
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:28
CPC Classifications
B; B29; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29B15/122; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/504; B32; B32B; B32B27/00; B32B27/04; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C03C25/28; D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/64; D06; D06B; D06B21/00; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/244; D06N; D06N3/00; D06N3/0002; D06N3/0015; D06N3/0022; D06N3/04; D06N3/06; D06N7/00; D06N7/0005; D06N7/006; B29K; B29K2027/00; B29K2027/06; B29K2105/00; B29K2105/0076; B29K2105/06; B29K2105/08; B29K2105/0854; D06N2205/00; D06N2205/02; D06N2205/026; D06N2205/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
145 words
A method for encapsulating an open structure fiber web in polyvinylchloride resin comprising: (a) coating heat-curable liquid polyvinylchloride plastisol or organosol onto an open structure fiber web in an amount sufficient to saturate and encapsulate the web; (b) gelling resin on a first surface of the web by passing the web around a first heated roll with the first surface of the web in contact with the surface of the heated roll; (c) then feeding the web, still in contact with the first heated roll, into a compression nip formed by said first roll and a second heated roll; (d) then passing the web around the second heated roll with the second surface of the web in contact with the surface of the second heated roll to thereby gell resin on the second surface of the web; and (e) thereafter completing curing of the resin.
Claim 2
Independent Claim
145 words
A method for encapsulating an open structure fiber web in polyvinylchloride resin comprising: (a) coating heat-curable liquid polyvinylchloride plastisol or organosol onto an open structure fiber web in an amount sufficient to saturate and encapsulate the web; (b) gelling resin on a first surface of the web by passing the web around a first heated roll with the first surface of the web in contact with the surface of the heated roll; (c) then feeding the web, still in contact with the first heated roll, into a compression nip formed by said first roll and a second heated roll; (d) then passing the web around the second heated roll with the second surface of the web in contact with the surface of the second heated roll to thereby gell resin on the second surface of the web; and (e) thereafter completing curing of the resin.
Claim 3
Dependent Claim
18 words
Method according to claim 1 wherein the web is saturated with resin during step (a) of claim 1.
Claim 4
Dependent Claim
34 words
Method according to claim 2 wherein the surface of the web passed in contact with the surface of the first heated roll is opposite the surface on which the plastisol or organosol is coated.
Claim 5
Dependent Claim
27 words
Method according to claim 1 wherein the web is subjected to a pressure between about 15 and about 45 pounds per lineal inch in the compression nip.
Claim 6
Dependent Claim
50 words
Method according to claim 1 wherein the quantity and viscosity of the plastisol or organosol coated onto the web is selected to maintain a bead of resin in the compression nip to act as a reservoir of resin to fill voids or depressions on the second surface of the web.
Claim 7
Dependent Claim
15 words
Method according to claim 5 wherein the web is a non-woven mat of glass fibers.
Claim 8
Dependent Claim
96 words
Method according to claim 6 wherein: (a) the mat has a void volume of at least about 98% and weighs between about 1 and about 4 pounds per 100 square feet; (b) openings in the mat average between about 1 and about 20 mils in the smallest linear dimension with at least 50% of such openings having smallest linear dimensions between about 2 and about 10 mils; and (c) the glass fibers making up the mat have average diameters between about 0.2 and about 0.8 mils and fiber lengths between about 0.2 and about 1.5 inch.
Claim 9
Dependent Claim
23 words
Method according to claim 1 wherein viscosity of the resin as coated onto the web is between about 500 and about 10,000 centiposes.
Claim 10
Dependent Claim
211 words
Method according to claim 1 wherein: (a) the web is saturated with resin during coating of the web according to step (a) of the claim 1; (b) the web is subjected to a pressure between about 15 and about 45 pounds per lineal inch in the compression nip; (c) the quantity and viscosity of the plastisol or organosol coated onto the web is selected to maintain a bead of such plastisol or organosol in the compression nip to act as a reservoir of coating material to fill depressions in the second surface of the web; (d) the viscosity of the plastisol or organosol coated onto the web is between about 500 and about 10,000 centiposes; and (e) the web is a non-woven web of glass fibers of average diameter between about 0.2 and about 0.8 mils and average fiber lengths between about 0.2 and about 1.5 inch, the mat having a weight between about 1 and about 4 pounds per hundred square feet, a void volume of at least about 98% and openings the smallest linear dimensions of which average between about 1 and about 20 mils in the smallest linear dimension with at least about 50% of such openings having smallest linear dimensions between about 2 and about 10 mils.
References Cited (Backward Citations)
CA778336A
Cited
US2772181A
Cited
US2956917A
Cited
US3554851A
Cited
US3272643A
Cited
US3551269A
Cited
US3519460A
Cited
US3573964A
Cited
US3694927A
Cited
US3773545A
Cited
US3968275A
Cited
CA997632A
Cited
US4041197A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |