Process for producing a metastable precursor powder and for producing sialon from this powder
Assignee: United States Department of the Interior
•
Filing: 1978-10-23
•
Granted: 1980-01-22
•
Expires: 1998-10-23
Abstract
Abstract There is disclosed a process for producing a metastable precursor powder having about 20 to 60 percent of the silicon thereof in the nitride form. This process includes a controlled nitriding step using silicon, alumina, and either aluminum or aluminum nitride as starting materials. There is also disclosed a process for producing sialon from this precursor powder. This process includes the steps of doping the precursor powder, cold pressing or slip casting the doped powder, and then carrying out a controlled sintering step under a nitrogen atmosphere.
Inventors
- 👤 Bing W. Jong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
132 words
A process for producing sialon comprising: (a) producing a metastable precursor powder by nitriding a mixture of about 97.0 to 77.4 mole percent of silicon, about 1.5 to 11.3 mole percent of alumina and about 1.5 to 11.3 mole percent of aluminum nitride at a temperature and for a time sufficient to convert about 20 to 60 percent of the silicon to the nitride form, (b) doping said precursor powder with an additive present in an amount sufficient to promote sintering, (c) cold pressing or slip casting the doped powder, and (d) sintering the cold pressed or slip cast powder under a nitrogen atmosphere at a temperature and for a time sufficient to produce a substantially single phase of sialon, said nitrogen atmosphere being at a pressure sufficient to prevent sialon decomposition.
Claim 2
Dependent Claim
132 words
A process for producing sialon comprising: (a) producing a metastable precursor powder by nitriding a mixture of about 97.0 to 77.4 mole percent of silicon, about 1.5 to 11.3 mole percent of alumina and about 1.5 to 11.3 mole percent of aluminum nitride at a temperature and for a time sufficient to convert about 20 to 60 percent of the silicon to the nitride form, (b) doping said precursor powder with an additive present in an amount sufficient to promote sintering, (c) cold pressing or slip casting the doped powder, and (d) sintering the cold pressed or slip cast powder under a nitrogen atmosphere at a temperature and for a time sufficient to produce a substantially single phase of sialon, said nitrogen atmosphere being at a pressure sufficient to prevent sialon decomposition.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein said temperature for the nitriding step is in the range of about 1300° to 1400° C.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein said time for the nitriding step is about 2 to 6 hours.
Claim 5
Dependent Claim
12 words
The process of claim 3 wherein said time is about 4 hours.
Claim 6
Dependent Claim
27 words
The process of claim 1 wherein the starting materials comprise about 86.0 mole percent silicon, about 7.0 mole percent alumina, and about 7.0 mole percent aluminum nitride.
Claim 7
Dependent Claim
18 words
The process of claim 1 wherein said temperature for the sintering step is about 1650° to 1750° C.
Claim 8
Dependent Claim
18 words
The process of claim 1 wherein said time for the sintering step is about 30 to 90 minutes.
Claim 9
Dependent Claim
16 words
The process of claim 6 wherein said temperature for the sintering step is about 1700° C.
Claim 10
Dependent Claim
13 words
The process of claim 8 wherein said sintering time is about one hour.
Claim 11
Dependent Claim
17 words
The process of claim 1 wherein said nitrogen atmosphere is at a pressure of about 5 psi.
Claim 12
Dependent Claim
22 words
The process of claim 1 wherein the doping additive is an oxide of yttrium or of an element of the Lanthanide series.
Claim 13
Dependent Claim
25 words
The process of claim 11 wherein said additive is selected from the group consisting of Y 2 O 3 and Gd 2 O 3 .
Claim 14
Dependent Claim
16 words
The process of claim 1 wherein said amount of dopant additive is about 5 weight percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |