Polyisocyanurate foam comprising reaction product of a polyisocyanate and a polyol mixture comprising a carboxylic ester polyol and a resole polyether polyol using a catalyst comprising dimethylethanolamine and an alkali metal salt of a carboxylic acid
Assignee: Owens Corning
•
Filing: 1978-09-15
•
Granted: 1980-01-15
•
Expires: 1998-09-15
Abstract
Abstract Rigid cellular urethane-modified polyisocyanurate foam products, a cocatalyst system and manufacturing methods are disclosed. The foams are the reaction product of polynuclear aromatic polyisocyanate material and polyol material with the polyisocyanate material being present in sufficient amount to provide isocyanurate groups as the major recurring polymer unit. The polyol comprises a mixture of diethylene glycol esters of biphenyl di and tri carboxylic acids and a resole-type polyether polyol. A catalytic amount of a binary catalyst comprising dimethyl ethanolamine and commercially available E9403 is incorporated in the reaction mixture along with a halocarbon blowing agent; a cell modifier; and a flame retardant material; to produce a cured foam having low flame spread rate and low smoke evolution.
Inventors
- 👤 Russell R. Lawyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:44
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4205; C08G18/4208; C08G18/4227; C08G18/08; C08G18/16; C08G18/161; C08G18/163; C08G18/18; C08G18/1825; C08G18/4009; C08G18/4027; C08G2110/00; C08G2110/0025; C08G2115/00; C08G2115/02; Y; Y10; Y10S; Y10S521/00; Y10S521/902
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
100 words
A rigid cellular urethane-modified polyisocyanurate foam product comprising the reaction product of polynuclear aromatic polyisocyanate material and polyol material; said polyol comprising a biphenyl di and tri carboxylic acid ester of a low molecular weight alkanediol and a resole-type polyether polyol; said polyisocyanate material being present in sufficient amount to provide isocyanurate groups as the major recurring polymer unit; a catalytic amount of a binary catalyst comprising dimethyl ethanolamine and an alkali metal salt of carboxylic acid; a halocarbon blowing agent; a cell modifier; and a flame retardant material; said foam having low flame spread rate and low smoke evolution.
Claim 2
Dependent Claim
100 words
A rigid cellular urethane-modified polyisocyanurate foam product comprising the reaction product of polynuclear aromatic polyisocyanate material and polyol material; said polyol comprising a biphenyl di and tri carboxylic acid ester of a low molecular weight alkanediol and a resole-type polyether polyol; said polyisocyanate material being present in sufficient amount to provide isocyanurate groups as the major recurring polymer unit; a catalytic amount of a binary catalyst comprising dimethyl ethanolamine and an alkali metal salt of carboxylic acid; a halocarbon blowing agent; a cell modifier; and a flame retardant material; said foam having low flame spread rate and low smoke evolution.
Claim 3
Dependent Claim
46 words
The foam product of claim 1 wherein the total polyol comprises about 10-20 weight percent of the foam product; the polyisocyanate comprises about 65-75% of the product; the flame-retardant material comprises about 2-10% of the product; and the blowing agent comprises about 6-15% of the product.
Claim 4
Dependent Claim
38 words
The foam product of claim 2 having a density of about 2 pounds per cubic foot, a flame spread rate no greater than 25, and a smoke evolution value below 450, as determined by standard test method ASTM-84-75.
Claim 5
Dependent Claim
17 words
The foam product of claim 2 comprising tris(2-chloroethyl)phosphate flame retardant, fluorotrichloromethane blowing agent, and silicone-type cell modifier.
Claim 6
Dependent Claim
38 words
The foam product of claim 1 wherein said polyether-polyol consists essentially of a reaction product of oxypropylated resole-type phenol-formaldehyde, and wherein the polyester-polyol consists essentially of the diethylene glycol esters of mixed biphenyl di and tri carboxylic acids.
Claim 7
Dependent Claim
38 words
In a urethane-modified isocyanurate foam reaction mixture, the improvement which comprises: a cocatalyst system consisting essentially of about 2 to 3 parts by weight of N,N-dimethyl ethanol amine per part of an alkali metal salt of carboxylic acid.
Claim 8
Dependent Claim
38 words
In a urethane-modified isocyanurate foam reaction mixture, the improvement which comprises: a cocatalyst system consisting essentially of about 2 to 3 parts by weight of N,N-dimethyl ethanol amine per part of an alkali metal salt of carboxylic acid.
Claim 9
Independent Claim
153 words
A method for manufacturing rigid urethane-modified isocyanurate foam product comprising the steps of: admixing component streams to form a fluent reaction mixture thereof; flowing the reaction mixture from admixing step to a curing zone and containing said reaction mixture until a rigid foam product is obtained; said component streams comprising a first, polyol-containing reactant stream comprising a major portion of polyether-polyol, a minor portion of polyol ester of aromatic polyacid and alkanediol, and a catalyst component consisting essentially of dimethylethanolamine; a second, polyisocyanate reactant stream comprising a major portion of polynuclear aromatic polyisocyanate in sufficient amount to provide isocyanurate as the major recurring polymer unit; a third stream comprising sufficient alkali metal salt of carboxylic acid solution to constitute an effective co-catalyst when mixed with the amine catalyst of the first stream; at least one of said streams containing a reaction-promoting amount of water, blowing agent, and cell modifier; and flame retardant material.
Claim 10
Independent Claim
153 words
A method for manufacturing rigid urethane-modified isocyanurate foam product comprising the steps of: admixing component streams to form a fluent reaction mixture thereof; flowing the reaction mixture from admixing step to a curing zone and containing said reaction mixture until a rigid foam product is obtained; said component streams comprising a first, polyol-containing reactant stream comprising a major portion of polyether-polyol, a minor portion of polyol ester of aromatic polyacid and alkanediol, and a catalyst component consisting essentially of dimethylethanolamine; a second, polyisocyanate reactant stream comprising a major portion of polynuclear aromatic polyisocyanate in sufficient amount to provide isocyanurate as the major recurring polymer unit; a third stream comprising sufficient alkali metal salt of carboxylic acid solution to constitute an effective co-catalyst when mixed with the amine catalyst of the first stream; at least one of said streams containing a reaction-promoting amount of water, blowing agent, and cell modifier; and flame retardant material.
Claim 11
Dependent Claim
15 words
The foam product of claim 1 wherein said catalyst contains a reaction-promoting amount of water.
Claim 12
Dependent Claim
23 words
The foam product of claim 8 wherein the amount of water is about 0.1 to 0.2 weight percent, based on the foam product.
Claim 13
Dependent Claim
46 words
The foam product of claim 1 wherein said polyol material has an average hydroxyl functionality of about 2.5 to 3, and wherein said binary catalyst consists essentially of about 2 to 3 parts of N,Ndimethylethanolamine per part by weight of alkali metal salt of carboxylic acid.
Claim 14
Dependent Claim
19 words
The foam product of claim 10 wherein said polyisocyanate material has an average functionality of about 2.1 to 3.2.
Claim 15
Dependent Claim
59 words
The foam product of claim 1 wherein the binary catalyst comprises about 0.5 to 1.5 weight percent of the foam and N,N-dimethylethanolamine is present in a weight ratio of 2:1 to 3:1 based on alkali metal salt of carboxylic acid cocatalyst and wherein water is present in the amount of about 0.1 to 0.2 percent based on total foam.
Claim 16
Dependent Claim
98 words
In a rigid, thermally-insulating urethane-modified polyisocyanurate foam obtained by reacting sufficient polynuclear aromatic polyisocyante with a minor amount of polyol in the presence of a blowing agent to form a polymeric foam having isocyanurate as the dominant recurring polymer unit; the improvement which comprises: a polyol reactant containing a major amount of alkoxylated resole-based phenol-formaldehyde type polyether-polyol and a minor amount of a polyester-polyol consisting essentially of the diethylene glycol ester of mixed bi phenyl di and tri carboxylic acids; and a water-promoted cocatalyst system consisting essentially of tertiary amine and an alkali metal salt of carboxylic acid.
Claim 17
Dependent Claim
98 words
In a rigid, thermally-insulating urethane-modified polyisocyanurate foam obtained by reacting sufficient polynuclear aromatic polyisocyante with a minor amount of polyol in the presence of a blowing agent to form a polymeric foam having isocyanurate as the dominant recurring polymer unit; the improvement which comprises: a polyol reactant containing a major amount of alkoxylated resole-based phenol-formaldehyde type polyether-polyol and a minor amount of a polyester-polyol consisting essentially of the diethylene glycol ester of mixed bi phenyl di and tri carboxylic acids; and a water-promoted cocatalyst system consisting essentially of tertiary amine and an alkali metal salt of carboxylic acid.
Claim 18
Dependent Claim
90 words
The foam of claim 13 wherein polyol having an average OH functionality of about 2.5 to 3 comprises a total of 10 to 20 weight percent of the foam, wherein the polyether-polyol and polyester-polyol are present in a weight ratio of about 1.7:1 to 2:1, wherein dimethylethanolamine and an alkali metal salt of carboxylic acid are present in a weight ratio of about 2:1 to 3:1, with the co-catalyst comprising about 0.5 to 1.5 percent of the foam, and wherein water comprises about 0.1 to 0.5 percent of the foam.
References Cited (Backward Citations)
US3180846A
Cited
US3516950A
Cited
US3531415A
Cited
US3580868A
Cited
US3745133A
Cited
US3644232A
Cited
US3581826A
Cited
US3725319A
Cited
US3770671A
Cited
US3940517A
Cited
US3876568A
Cited
US3899443A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |