Method of removing surface ionic impurities on inorganic photoconductive material
Assignee: Canon Inc
•
Filing: 1977-09-30
•
Granted: 1980-01-15
•
Expires: 1997-09-30
Abstract
Abstract This invention is directed to photosensitive material for electrophotography and more particularly it is directed to the improvement of the properties with respect to humidity of photosensitive material by using photoconductive material in combination with ion exchange resin or by using photoconductive material which is previously washed in an aqueous solution in the presence of ion exchange resin.
Inventors
- 👤 Keiichi Murai
- 👤 Takehiko Matsuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:18
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
122 words
A method of improving particles of an electrophotographic photoconductive material selected from the group consisting of Cu 2 O, CuI, ZnO, ZnS, ZnSe, CdS, Se-Te, CdSe, CdTe, PbS, Sb 2 S 3 , In 2 Te 3 , GeS, GeSe, Tl 2 S, (Cd.Zn)S, CdS.CdSe and CdS, which are rendered electrically conductive by exposure to actinic radiation, by removing substantially all surface ionic impurities which might cause deterioration of the photoconductive properties of the particles due to temperature and humidity conditions, said method comprising the steps of washing said particles in an aqueous solution containing at least one type of ion exchange resin to solubilize said ionic impurities from the surface of said particles and then separating said particles from said solution.
Claim 2
Independent Claim
122 words
A method of improving particles of an electrophotographic photoconductive material selected from the group consisting of Cu 2 O, CuI, ZnO, ZnS, ZnSe, CdS, Se-Te, CdSe, CdTe, PbS, Sb 2 S 3 , In 2 Te 3 , GeS, GeSe, Tl 2 S, (Cd.Zn)S, CdS.CdSe and CdS, which are rendered electrically conductive by exposure to actinic radiation, by removing substantially all surface ionic impurities which might cause deterioration of the photoconductive properties of the particles due to temperature and humidity conditions, said method comprising the steps of washing said particles in an aqueous solution containing at least one type of ion exchange resin to solubilize said ionic impurities from the surface of said particles and then separating said particles from said solution.
Claim 3
Dependent Claim
24 words
A method according to claim 1, wherein said electrophotographic photoconductive material is selected from the group consisting of CdS, CdSe, ZnS, (Cd.Zn)S and CdS.CdSe.
Claim 4
Dependent Claim
31 words
The method of claim 1, wherein said washing is conducted for a period of time to reduce the electrical conductivity of said aqueous solution, after said washing, to below 10 μmho/cm.
Claim 5
Dependent Claim
17 words
The method of claim 3, wherein said aqueous solution comprises pure water substantially free of ionic impurities.
Claim 6
Dependent Claim
29 words
The method of claim 3, wherein the amount of ion exchange resin is from 1/2 to 1/10 part by weight per 1 part by weight of said photoconductive particles.
Claim 7
Dependent Claim
31 words
The method of claim 1, wherein said washing is conducted for a period of time to reduce the electrical conductivity of said aqueous solution, after said washing, to below 2 μmho/cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |