Method of fabricating liquid cooled gas turbine components
Assignee: General Electric Co
•
Filing: 1978-07-17
•
Granted: 1980-01-15
•
Expires: 1998-07-17
Abstract
Abstract A method of fabricating complex, composite components for water-cooled, high temperature gas turbines is provided. The method utilizes hot isostatic pressure with molten glass as a pressure transmitting medium. Metal tubing and cladding are bonded to a component core under conditions such that the ends of the tubing extend above the molten glass whereby the pressure inside and outside of the tubing is maintained at equilibrium to prevent collapsing thereof during the application of hot isostatic pressure.
Inventors
- 👤 William F. Schilling
- 👤 Adrian M. Beltran
- 👤 Myron C. Muth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:38
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/14; B23P; B23P15/00; B23P15/04; F; F01; F01D; F01D5/00; F01D5/12; F01D5/14; F01D5/18; F01D5/185; F01D5/28; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49336; Y10T29/49339; Y10T29/49341
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
163 words
A method of making a water-cooled, high temperature turbine bucket comprising the steps of: (a) disposing a plurality of metal tubing sections on a preselected interface portion of a gas turbine bucket in such a manner that at least one end of each tubing section extends external to the airfoil portion of the bucket, (b) placing a preformed cladding over both the airfoil portion and the tubing whereby the said extending tube ends also project beyond the cladding and affixing the cladding to said airfoil portion to form an assembly, (c) masking exposed portions of the interface between the cladding and the airfoil portions, (d) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections open to said pressure such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are metallurgically bonded to the turbine bucket.
Claim 2
Independent Claim
163 words
A method of making a water-cooled, high temperature turbine bucket comprising the steps of: (a) disposing a plurality of metal tubing sections on a preselected interface portion of a gas turbine bucket in such a manner that at least one end of each tubing section extends external to the airfoil portion of the bucket, (b) placing a preformed cladding over both the airfoil portion and the tubing whereby the said extending tube ends also project beyond the cladding and affixing the cladding to said airfoil portion to form an assembly, (c) masking exposed portions of the interface between the cladding and the airfoil portions, (d) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections open to said pressure such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are metallurgically bonded to the turbine bucket.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein both ends of each tubing section extend external to the airfoil.
Claim 4
Dependent Claim
17 words
The method of claim 2, wherein the tubing sections pass through a platform of the turbine bucket.
Claim 5
Dependent Claim
24 words
The method of claim 1, wherein only one end of said tubing section extends external to the airfoil and the other end is closed.
Claim 6
Dependent Claim
19 words
The method of claim 4, wherein said closed tube end is embedded in a platform of the turbine bucket.
Claim 7
Independent Claim
184 words
A method of making a water-cooled, high temperature turbine bucket comprising the steps of: (a) preparing for vacuum brazing a gas turbine bucket having a plurality of channels formed therein, (b) disposing a plurality of metal tubing sections into said channels in such a manner that both ends of each tubing section extend external to the airfoil portion of the bucket, and vacuum brazing said sections in said channels, (c) placing a preformed cladding over the airfoil portion including the tubing disposed in channels formed therein and whereby the ends of said tubing extend beyond the cladding and affixing the cladding to said airfoil portion to form an assembly, (d) masking exposed portions of the interface between the cladding and the airfoil portion of the bucket, (e) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections extending above said liquid such that the same pressure exists inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are bonded to the turbine bucket.
Claim 8
Independent Claim
184 words
A method of making a water-cooled, high temperature turbine bucket comprising the steps of: (a) preparing for vacuum brazing a gas turbine bucket having a plurality of channels formed therein, (b) disposing a plurality of metal tubing sections into said channels in such a manner that both ends of each tubing section extend external to the airfoil portion of the bucket, and vacuum brazing said sections in said channels, (c) placing a preformed cladding over the airfoil portion including the tubing disposed in channels formed therein and whereby the ends of said tubing extend beyond the cladding and affixing the cladding to said airfoil portion to form an assembly, (d) masking exposed portions of the interface between the cladding and the airfoil portion of the bucket, (e) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections extending above said liquid such that the same pressure exists inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are bonded to the turbine bucket.
Claim 9
Dependent Claim
11 words
The method of claim 6, wherein said liquid is molten glass.
Claim 10
Dependent Claim
11 words
The method of claim 7, wherein said glass is soda-lime glass.
Claim 11
Dependent Claim
24 words
The method according to claim 7, wherein the diffusion bonding step is performed according to the time-temperature-pressure schedule as set forth in FIG. 6.
Claim 12
Dependent Claim
36 words
The method of claim 7, wherein said cladding is a composite layer consisting of an inner skin in contact with said tubing to provide high thermal conductivity and an outer skin to provide hot corrosion resistance.
Claim 13
Dependent Claim
37 words
The method of claim 10, wherein said tubing is copper and said inner skin is a member selected from the group consisting of copper and oxide dispersion strengthened copper and said outer skin is a nickel-base alloy.
Claim 14
Independent Claim
148 words
A method of making an article of manufacture comprising the steps of: (a) disposing a plurality of metal tubing sections at a preselected interface portion of said article in such a manner that at least one end of each tubing section extends external to said portion, (b) placing a preformed cladding over both said portion and the tubing whereby the said extending tube ends also project beyond the cladding and affixing the cladding to said portion to form an assembly, (c) masking exposed interfaces between the cladding and said portion, (d) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections open to said pressure such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are metallurgically bonded to the article.
Claim 15
Independent Claim
148 words
A method of making an article of manufacture comprising the steps of: (a) disposing a plurality of metal tubing sections at a preselected interface portion of said article in such a manner that at least one end of each tubing section extends external to said portion, (b) placing a preformed cladding over both said portion and the tubing whereby the said extending tube ends also project beyond the cladding and affixing the cladding to said portion to form an assembly, (c) masking exposed interfaces between the cladding and said portion, (d) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections open to said pressure such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are metallurgically bonded to the article.
Claim 16
Dependent Claim
17 words
The method of claim 12, wherein both ends of each tubing section extend external to said portion.
Claim 17
Dependent Claim
24 words
The method of claim 12, wherein only one end of said tubing section extends external to said portion and the other end is closed.
Claim 18
Independent Claim
170 words
A method of making a water-cooled, high temperature turbine nozzle comprising the steps of: (a) preparing for vacuum brazing a gas turbine nozzle having a plurality of channels formed therein, (b) disposing a plurality of metal tubing sections into said channels in such a manner that both ends of each tubing section extend external to a portion of said nozzle, and vacuum brazing said sections in said channels, (c) placing a preformed cladding over said portion including the tubing disposed in channels formed therein and whereby the ends of said tubing extend beyond the cladding to said portion to form an assembly, (d) masking exposed interfaces between the cladding and said portion, (e) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections extending above said liquid such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are bonded to the turbine nozzle.
Claim 19
Independent Claim
170 words
A method of making a water-cooled, high temperature turbine nozzle comprising the steps of: (a) preparing for vacuum brazing a gas turbine nozzle having a plurality of channels formed therein, (b) disposing a plurality of metal tubing sections into said channels in such a manner that both ends of each tubing section extend external to a portion of said nozzle, and vacuum brazing said sections in said channels, (c) placing a preformed cladding over said portion including the tubing disposed in channels formed therein and whereby the ends of said tubing extend beyond the cladding to said portion to form an assembly, (d) masking exposed interfaces between the cladding and said portion, (e) subjecting the assembly to hot isostatic pressure in a pressure transmitting liquid at a sufficient temperature and pressure, while maintaining said tubing sections extending above said liquid such that the same pressure exist inside and outside of said sections preventing said section from collapsing, and whereby the tubing and the cladding are bonded to the turbine nozzle.
Claim 20
Dependent Claim
11 words
The method of claim 15, wherein said liquid is molten glass.
Claim 21
Dependent Claim
11 words
The method of claim 16, wherein said glass is soda-lime glass.
Claim 22
Dependent Claim
25 words
The method according to claim 16, wherein the diffusion bonding step is performed according to the time-temperature pressure schedule as set forth in FIG. 6.
Claim 23
Dependent Claim
36 words
The method of claim 16, wherein said cladding is a composite layer consisting of an inner skin in contact with said tubing to provide high thermal conductivity and an outer skin to provide hot corrosion resistance.
Claim 24
Dependent Claim
37 words
The method of claim 19, wherein said tubing is copper and said inner skin is a member selected from the group consisting of copper and oxide dispersion strengthened copper and said outer skin is a nickel-base alloy.
References Cited (Backward Citations)
DE816686C
Cited
US3041040A
Cited
US3773506A
Cited
US4024620A
Cited
US3928901A
Cited
US3952939A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |