Method for curing photo-curable composition
Assignee: Japan Storage Battery Co Ltd
•
Filing: 1978-09-18
•
Granted: 1980-01-08
•
Expires: 1998-09-18
Abstract
Abstract A photo-curable composition with high covering power provides the coating film with a glossy smooth surface when such composition is exposed firstly to light radiation having wavelengths of from about 350 nm to about 460 nm, and then to light radiation having wavelengths of from about 230 nm to about 400 nm with a specific ratio of the intensity of the former light radiation to the intensity of the latter light radiation.
Inventors
- 👤 Hiroaki Mibu
- 👤 Tadashi Ishihara
- 👤 Chiaki Tanaka
- 👤 Shingo Esaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:27
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/81; C08G18/8141; C08G18/815; C08G18/8158; C08G18/8175; B; B05; B05D; B05D3/00; B05D3/06; B05D3/061; B05D3/065; B05D3/067; B29; B29C; B29C35/00; B29C35/02; B29C35/08; B29C35/10; C08G18/28; C08G18/67; C08G18/68; C08G18/683; C08G18/686; C09; C09D; C09D175/00; C09D175/04; C09D175/14; C09D175/16; G; G03; G03F; G03F7/00; G03F7/20; G03F7/2022; B29C35/0805; B29C2035/0827; B29C2035/0833; B29C2791/00; B29C2791/001; C08L; C08L75/00; C08L75/04; C08L75/14; C08L75/16; G03B; G03B2215/00; G03B2215/05; G03B2215/0514; G03B2215/0517; G03B2215/0525; G03B2215/0528
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
194 words
A method for curing a photo-curable composition consisting essentially of a resin having a α,β-ethylenically unsaturated bond, a polymerizable monomer and a photosensitizer, said method comprising the sequential steps of: 1. irradiating said photo-curable composition with a light source A emitting radiation predominantly across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm, for a period of time sufficient to cure the interior portion of said photo-curable composition and then in a second step, 2. irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm, for a period of time sufficient to cure the surface portion of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 400 nm on the surface of said photocurable composition.
Claim 2
Independent Claim
194 words
A method for curing a photo-curable composition consisting essentially of a resin having a α,β-ethylenically unsaturated bond, a polymerizable monomer and a photosensitizer, said method comprising the sequential steps of: 1. irradiating said photo-curable composition with a light source A emitting radiation predominantly across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm, for a period of time sufficient to cure the interior portion of said photo-curable composition and then in a second step, 2. irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm, for a period of time sufficient to cure the surface portion of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 400 nm on the surface of said photocurable composition.
Claim 3
Dependent Claim
24 words
The method according to claim 1, wherein the irradiation intensity ratio E A /E B is in the range of from 0.1 to 15.
Claim 4
Dependent Claim
33 words
The method according to claim 1, wherein the irradiation intensity E A is not less than 55 W/m 2 and the irradiation intensity E B is not less than 135 W/m 2 .
Claim 5
Dependent Claim
27 words
The method according to claim 1, wherein the light source A is a metal halide lamp and the light source B is a high pressury mercury lamp.
Claim 6
Dependent Claim
41 words
The method according to claim 1, wherein the irradiations with the light source A and with the light source B are respectively carried out for a period of 10 to 30 seconds and for a period of 30 to 300 seconds.
Claim 7
Dependent Claim
76 words
The method according to claim 1, wherein the light sources A is an electric discharge lamp being a mercury lamp in which a metal and/or a metal halide is added to the mercury, the metal and the metal of the metal halide being a member or a combination of members selected from the group comprising gallium, indium, lead, aluminum, tin, cadmium, chromium, cerium, cobalt, lanthanum, magnesium, manganese, molybdenum, niobium, nickel, scandium, strontium and thorium vanadium zinc.
Claim 8
Dependent Claim
38 words
A method as set forth in claim 1, wherein said light source A comprises at least one discharge lamp including a light emitting tube which contains one or more of Ga, In, Al, Sn, and Cd sealed therein.
Claim 9
Dependent Claim
25 words
A method as set forth in claim 1, wherein said light source B comprises at least one of medium-pressure mercury lamp or high-pressure mercury lamp.
Claim 10
Dependent Claim
33 words
The method of claim 1 wherein said resin is a member selected from the group consisting of unsaturated polyester resins, unsaturated polyurethane resins, unsaturated acrylic resins, unsaturated epoxide resins and unsaturated alkyd resins.
Claim 11
Independent Claim
80 words
A method for curing a photo-curable composition consisting essentially of a resin having an α,β-ethylenically unsaturated bond, a polymerizable monomer, a photosensitizer and a pigment, said method comprising the sequential steps of: 1. irradiating said photo-curable composition with a light source A emitting radiation predominantly across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm, for a period of time sufficient to cure the interior of said photo-curable composition, and then,
Claim 12
Independent Claim
80 words
A method for curing a photo-curable composition consisting essentially of a resin having an α,β-ethylenically unsaturated bond, a polymerizable monomer, a photosensitizer and a pigment, said method comprising the sequential steps of: 1. irradiating said photo-curable composition with a light source A emitting radiation predominantly across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm, for a period of time sufficient to cure the interior of said photo-curable composition, and then,
Claim 13
Dependent Claim
109 words
irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm, for a period of time sufficient to cure the surface of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 460 nm on the surface of said photocurable composition.
Claim 14
Dependent Claim
109 words
irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm, for a period of time sufficient to cure the surface of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 460 nm on the surface of said photocurable composition.
Claim 15
Dependent Claim
24 words
The method according to claim 10, wherein the irradiation intensity ratio E A /E B is in the range of from 0.1 to 15.
Claim 16
Dependent Claim
33 words
The method according to claim 10, wherein the irradiation intensity E A is not less than 55 W/m 2 and the irradiation intensity E B is not less than 135 W/m 2 .
Claim 17
Dependent Claim
27 words
The method according to claim 10, wherein the light source A is a metal halide lamp and the light source B is a high pressure mercury lamp.
Claim 18
Dependent Claim
41 words
The method according to claim 10, wherein the irradiations with the light source A and with the light source B are respectively carried out for a period of 10 to 300 seconds and for a period of 30 to 300 seconds.
Claim 19
Dependent Claim
33 words
The method of claim 10, wherein said resin is a member selected from the group consisting of unsaturated polyester resins, unsaturated polyurethane resins, unsaturated acrylic resins, unsaturated epoxide resins and unsaturated alkyd resins.
Claim 20
Dependent Claim
13 words
The method of claim 15 wherein said resin is an unsaturated polyester resin.
Claim 21
Independent Claim
42 words
A method of curing a photo-curable composition consisting essentially of a resin having an α,β-ethylenically unsaturated bond, a polymerizable monomer, a pigment and at least one of a filler, an additive and a photo-inactive diluent said method comprising the sequential steps of:
Claim 22
Independent Claim
42 words
A method of curing a photo-curable composition consisting essentially of a resin having an α,β-ethylenically unsaturated bond, a polymerizable monomer, a pigment and at least one of a filler, an additive and a photo-inactive diluent said method comprising the sequential steps of:
Claim 23
Dependent Claim
158 words
irradiating said photo-curable composition with a light source A emitting radiation predominately across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm for a period of time sufficient to cure the interior of the said photo-curable composition, and then, 2. irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm for a period of time sufficient to cure the surface of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 460 nm on the surface of said photo-curable composition.
Claim 24
Dependent Claim
158 words
irradiating said photo-curable composition with a light source A emitting radiation predominately across the range of from about 350 to about 460 nm and substantially no wavelength shorter than 300 nm for a period of time sufficient to cure the interior of the said photo-curable composition, and then, 2. irradiating said photo-curable composition with a light source B emitting radiation predominantly across the range of from about 230 to about 400 nm for a period of time sufficient to cure the surface of said photo-curable composition, with the irradiation intensity ratio E A /E B being in the range of from 0.01 to 20 where E A is the irradiation intensity of light source A for wavelengths in the range of from about 350 to about 460 nm and E B is the irradiation intensity of light source B for wavelengths in the range of about 230 to about 460 nm on the surface of said photo-curable composition.
Claim 25
Dependent Claim
33 words
The method of claim 17 wherein said resin is a member selected from the group consisting of unsaturated polyester resins, unsaturated polyurethan resins, unsaturated acrylic resins, unsaturated epoxide resins and unsaturated alkyd resins.
Claim 26
Dependent Claim
13 words
The method of claim 18, wherein said resin is an unsaturated polyester resin.
Claim 27
Dependent Claim
13 words
The method of claim 9 wherein said resin is an unsaturated polyester resin.
References Cited (Backward Citations)
US3556794A
Cited
US3594160A
Cited
US3591378A
Cited
US3649268A
Cited
US3809686A
Cited
US3784527A
Cited
US3807999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-07 | 1983-07-09 | 1984-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-07 | 1987-07-09 | 1988-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-07 | 1991-07-09 | 1992-01-08 | $7700.00 | Window Closed / Lapsed |