High temperature compressible support and gasket material
Assignee: CARBOSPHERES Inc A CORP OF VIRGINIA
•
Filing: 1974-05-30
•
Granted: 1979-12-25
•
Expires: 1994-05-30
Abstract
Abstract A high-temperature compressible material especially useful in rocket motors to support nozzle ring inserts, the material including a binder which when pyrolyzed leaves a char having substantial strength, and fillers including carbonaceous fillers such as carbon fibers, wools, powders, etc., plus a special filler comprising hollow carbon microspheres which can crush to provide a compressibility to the material when it is confined in a volume-limiting environment, plus other fillers which may be added to obtain special yield characteristics.
Inventors
- 👤 Eugene L. Olcott
- 👤 Edwin F. Abrams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:22
CPC Classifications
F; F02; F02K; F02K9/00; F02K9/97; Y; Y10; Y10S; Y10S277/00; Y10S277/935; Y10S277/936; Y10S60/00; Y10S60/909; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/30
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
134 words
A high-temperature gasket material for filling and sealing a volume-limited space, the gasket material being crushable under high loading without requiring the exit of material from said space, comprising: (a) a binder material of a type which pyrolyzes to leave a carbonaceous char which retains substantial strength, the binder material comprising 15 to 30% by weight of the gasket material and the binder material being selected from a group including phenolics, polyimides and furanes; (b) crushable filler material in said binder comprising hollow carbon microspheres whose diameters fall within the range of 5 to 150 microns and whose wall thicknesses approximate several microns; and (c) other filler materials in said binder and fully occupying the interstices between the microspheres so that substantially the only voids in the uncrushed gasket material are within the microspheres.
Claim 2
Dependent Claim
134 words
A high-temperature gasket material for filling and sealing a volume-limited space, the gasket material being crushable under high loading without requiring the exit of material from said space, comprising: (a) a binder material of a type which pyrolyzes to leave a carbonaceous char which retains substantial strength, the binder material comprising 15 to 30% by weight of the gasket material and the binder material being selected from a group including phenolics, polyimides and furanes; (b) crushable filler material in said binder comprising hollow carbon microspheres whose diameters fall within the range of 5 to 150 microns and whose wall thicknesses approximate several microns; and (c) other filler materials in said binder and fully occupying the interstices between the microspheres so that substantially the only voids in the uncrushed gasket material are within the microspheres.
Claim 3
Dependent Claim
28 words
The material as set forth in claim 1, wherein said other filler materials comprise carbonaceous materials selected from a group including mattes, wools, fibers, cloth, particles and powders.
Claim 4
Dependent Claim
51 words
The material as set forth in claim 1, wherein said other filler materials comprise carbonaceous materials blended with other materials which change state within the temperature range required to pyrolyze said binder material, and said other materials being selected from a group including glass spheres, silicas, soft metals and subliming salts.
Claim 5
Dependent Claim
143 words
In a rocket assembly including a housing and a nozzle insert therein and a back-up space between the insert and the housing, a high temperature gasket material completely filling and sealing said back-up space and crushable by expansion of said nozzle insert without having material of the gasket leave said space, comprising: (a) a binder material of a type which pyrolyzes to leave a carbonaceous char which retains substantial strength, the binder material comprising 15 to 30% by weight of the gasket material; (b) crushable filler material in said binder comprising hollow carbon microspheres whose diameters fall within the range of 5 to 150 microns and whose wall thicknesses approximate several microns; and (c) other filler materials in said binder and fully occupying the interstices between the microspheres so that substantially the only voids in the uncrushed gasket material are within the microspheres.
Claim 6
Dependent Claim
143 words
In a rocket assembly including a housing and a nozzle insert therein and a back-up space between the insert and the housing, a high temperature gasket material completely filling and sealing said back-up space and crushable by expansion of said nozzle insert without having material of the gasket leave said space, comprising: (a) a binder material of a type which pyrolyzes to leave a carbonaceous char which retains substantial strength, the binder material comprising 15 to 30% by weight of the gasket material; (b) crushable filler material in said binder comprising hollow carbon microspheres whose diameters fall within the range of 5 to 150 microns and whose wall thicknesses approximate several microns; and (c) other filler materials in said binder and fully occupying the interstices between the microspheres so that substantially the only voids in the uncrushed gasket material are within the microspheres.
Claim 7
Dependent Claim
21 words
The material as set forth in claim 4, wherein the binder is selected from a group including phenolics, polyimides, and furanes.
Claim 8
Dependent Claim
51 words
The material as set forth in claim 4, wherein said other filler materials comprise carbonaceous materials blended with other materials which change state within the temperature range required to pyrolyze said binder material, and said other materials being selected from a group including glass spheres, silicas, soft metals and subliming salts.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-24 | 1983-06-25 | 1983-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-24 | 1987-06-25 | 1987-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-24 | 1991-06-25 | 1991-12-25 | $7700.00 | Window Closed / Lapsed |