US4178339A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laminated electrode
Assignee: Department of National Defence
•
Filing: 1977-10-25
•
Granted: 1979-12-11
•
Expires: 1997-10-25
Abstract
Abstract The invention disclosed is a multi-layer silver/silver chloride electrode structure for use in electrolytic cells, particularly at low temperatures. Each layer includes an evenly dispersed matrix of metallic silver bonded to silver chloride particles, compressed onto a metal grid. A method for the manufacture of the electrode is also disclosed.
Inventors
- 👤 Peter J. Powell
- 👤 Gerard D. Nagy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:14
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/04; H01M4/0402; H01M4/0404; H01M4/043; H01M4/0471; H01M4/06; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
181 words
A method for the manufacture of a silver/silver chloride electrode, said electrode comprising a plurality of layers of a porous material comprising an evenly dispersed matrix of metallic silver bonded to silver chloride particles, on both major surfaces of a metal grid, said method comprising: (a) preparing a homogeneous mixture, in the form of a finely divided powder, of a major amount of silver chloride and a minor amount of a silver compound reducible to metallic silver at a temperature below the melting point of silver chloride, which silver compound is selected from the group consisting of silver oxides, silver carbonate, disilver fluoride, silver sulfide and mixtures thereof, (b) individually compressing a plurality of layers of said mixture, one on top of another onto a metal grid at pressures of about 800 to about 1500 psi, (c) subjecting the assembly so formed to a final pressing step at pressures of about 3,000 to about 5,000 psi, and (d) sintering, at a temperature below the melting point of silver chloride, for a time sufficient to reduce the silver compound to metallic silver.
Claim 2
Independent Claim
181 words
A method for the manufacture of a silver/silver chloride electrode, said electrode comprising a plurality of layers of a porous material comprising an evenly dispersed matrix of metallic silver bonded to silver chloride particles, on both major surfaces of a metal grid, said method comprising: (a) preparing a homogeneous mixture, in the form of a finely divided powder, of a major amount of silver chloride and a minor amount of a silver compound reducible to metallic silver at a temperature below the melting point of silver chloride, which silver compound is selected from the group consisting of silver oxides, silver carbonate, disilver fluoride, silver sulfide and mixtures thereof, (b) individually compressing a plurality of layers of said mixture, one on top of another onto a metal grid at pressures of about 800 to about 1500 psi, (c) subjecting the assembly so formed to a final pressing step at pressures of about 3,000 to about 5,000 psi, and (d) sintering, at a temperature below the melting point of silver chloride, for a time sufficient to reduce the silver compound to metallic silver.
Claim 3
Dependent Claim
21 words
A method according to claim 1, wherein the metal grid is in the form of a mesh or an expanded metal.
Claim 4
Dependent Claim
18 words
A method according to claim 2, wherein the metal of the grid is selected from silver and nickel.
Claim 5
Dependent Claim
21 words
A method according to claim 3, wherein said major amount is about 90%/w and wherein said minor amount is about 10%/w.
Claim 6
Dependent Claim
18 words
A method according to claim 4, wherein the silver compound is selected from silver oxides and silver carbonate.
Claim 7
Dependent Claim
16 words
A method according to claim 5, wherein said layers are individually compressed at about 1000 psi.
Claim 8
Dependent Claim
18 words
A method according to claim 6, wherein said final pressing step is carried out at about 3600 psi.
Claim 9
Dependent Claim
24 words
A method according to claim 7, wherein the sintering step is effected at about 350° C. to about 430° C. for about two hours.
Claim 10
Dependent Claim
15 words
A method according to claim 8, wherein the sintering step is effected at 410°±5° C.
Claim 11
Dependent Claim
15 words
A method according to claim 8, wherein the mixture is moistened before the compressing step.
Claim 12
Dependent Claim
28 words
A method according to claim 10, wherein the homogeneous mixture is in the form of a finely divided powder of a particle size of 60 mesh or smaller.
Claim 13
Dependent Claim
25 words
A method according to claim 11, wherein the amount of metallic silver in the electrode is about 10%/w, based on the weight of the electrode.
Claim 14
Dependent Claim
22 words
A method according to claim 12, wherein each of the plurality of layers includes silver chloride particles of different ranges of sizes.
Claim 15
Dependent Claim
32 words
A method according to claim 13, wherein each of the plurality of layers includes amounts of metallic silver within the range of about 5-15%/w, based on the weight of the specific layer.
Claim 16
Dependent Claim
31 words
A method according to claim 14, wherein the amount of metallic silver in each layer is selected from about 5, 10 and 15%/w based on the weight of the specific layer.
Claim 17
Dependent Claim
22 words
A method according to claim 15, wherein said three layers include silver chloride particle size ranges selected from <125μ, 125-250μ and 250-500μ.
Claim 18
Dependent Claim
42 words
A method according to claim 16, wherein the inner layer includes silver chloride of particle size <125μ, wherein the middle layer includes silver chloride of particle size of 125-250μ and wherein the outer layer includes silver chloride of particle sizes of 250-500μ.
Claim 19
Dependent Claim
57 words
A method according to claim 17, wherein the inner layer includes metallic silver in an amount of about 15%/w, wherein the middle layer includes metallic silver in an amount of about 10%/w, and wherein the outer layer includes silver in an amount of about 5%/w, all weight percentages being based on the weight of the specific layer.
Claim 20
Dependent Claim
58 words
A method according to claim 18, wherein the inner layer includes metallic silver in an amount of about 5%/w, wherein the middle layer includes metallic silver in an amount of about 10%/w, and wherein the outer layer includes metallic silver in an amount of about 15%/w, all weight percentages being based on the weight of the specific layer.
Claim 21
Dependent Claim
16 words
A method according to claim 1 or 18, wherein the silver compound is silver I oxide.
References Cited (Backward Citations)
US3332801A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-10 | 1983-06-11 | 1983-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-10 | 1987-06-11 | 1987-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-10 | 1991-06-11 | 1991-12-11 | $7700.00 | Window Closed / Lapsed |