High solids coating composition with acrylic hydroxyphosphate catalyst-III
Assignee: EIDP Inc
•
Filing: 1978-12-26
•
Granted: 1979-12-11
•
Expires: 1998-12-26
Abstract
Abstract A fast curing, high solids coating composition that is adapted for use as an automotive topcoat and which upon curing forms a hard, glossy, durable coating exhibiting excellent resistance to solvents and water. The coating composition contains greater than about 50 percent by weight of nonvolatile solids and, exclusive of pigments, solvents and other nonreactive components, consists essentially of: (A) a polyepoxide resin having a number average molecular weight (Mn) of between about 140 and about 3,000; (B) a hydroxy functional acrylic organophosphate reactive catalyst; (C) an amine-aldehyde crosslinking agent; and (D) optionally, a hydroxy functional additive. The hydroxy functional acrylic organophosphate reactive catalyst is included in the composition in an amount sufficient to provide between about 0.9 and about 1.5 equivalents of acid functionality for each equivalent of epoxy functionality on the polyepoxide resin and the amino resin crosslinking agent is included in the composition in an amount sufficient to provide at least about 0.4 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in the composition.
Inventors
- 👤 Mohinder S. Chattha
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 07:25
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4071; C09; C09D; C09D163/00; C08L; C08L43/00; C08L43/02; C08L61/00; C08L61/20
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
307 words
A thermosetting coating composition adapted for low temperature bake applications which contains greater than about 50% by weight of nonvolatile solids, and which, exclusive of pigments, solvents and other nonreactive components, consists essentially of: (A) a polyepoxide resin having a number average molecular weight (M n ) of between about 140 and about 3,000; (B) a hydroxy functional acrylic organophosphate reactive catalyst consisting essentially of the reaction product of: (1) a hydroxy functional acrylic copolymer which (a) has a number average molecular weight (Mn) of between about 1500 and about 6000, (b) has a glass transition temperature of between about -25° C. and about 70° C., and (c) bears between about 2 and about 10 pendant hydroxy groups per molecule; and (2) sufficient phosphorus pentoxide to produce a reaction product having an acid equivalent weight of between about 500 and about 3000; (C) an amine aldehyde crosslinking agent; and (D) up to about 45 weight percent based on the total weight of (A), (B), (C) and (D) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150 and about 6000, said hydroxy functional acrylic organophosphate reactive catalyst being included in said composition in an amount sufficient to provide between about 0.9 and about 1.5 equivalents of acid functionality for each equivalent of epoxy functionality on said polyepoxide resin, and said amine aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.4 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in ssaid composition either as (i) an organic hydroxyl group on said hydroxy functional acrylic organophosphate reactive catalyst, (ii) a hydroxyl group on said hydroxy functional additive, or (iii) as a result of esterification of said epoxy functionality of said polyepoxide resin during cure of said coating composition.
Claim 2
Dependent Claim
307 words
A thermosetting coating composition adapted for low temperature bake applications which contains greater than about 50% by weight of nonvolatile solids, and which, exclusive of pigments, solvents and other nonreactive components, consists essentially of: (A) a polyepoxide resin having a number average molecular weight (M n ) of between about 140 and about 3,000; (B) a hydroxy functional acrylic organophosphate reactive catalyst consisting essentially of the reaction product of: (1) a hydroxy functional acrylic copolymer which (a) has a number average molecular weight (Mn) of between about 1500 and about 6000, (b) has a glass transition temperature of between about -25° C. and about 70° C., and (c) bears between about 2 and about 10 pendant hydroxy groups per molecule; and (2) sufficient phosphorus pentoxide to produce a reaction product having an acid equivalent weight of between about 500 and about 3000; (C) an amine aldehyde crosslinking agent; and (D) up to about 45 weight percent based on the total weight of (A), (B), (C) and (D) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150 and about 6000, said hydroxy functional acrylic organophosphate reactive catalyst being included in said composition in an amount sufficient to provide between about 0.9 and about 1.5 equivalents of acid functionality for each equivalent of epoxy functionality on said polyepoxide resin, and said amine aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.4 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in ssaid composition either as (i) an organic hydroxyl group on said hydroxy functional acrylic organophosphate reactive catalyst, (ii) a hydroxyl group on said hydroxy functional additive, or (iii) as a result of esterification of said epoxy functionality of said polyepoxide resin during cure of said coating composition.
Claim 3
Dependent Claim
36 words
A composition in accordance with claim 1 wherein said polyepoxide resin is selected from the group consisting of aliphatic, cycloaliphatic and aromatic polyepoxides having a number average molecular weight of between about 300 and about 2,000.
Claim 4
Dependent Claim
50 words
A composition in accordance with claim 1 wherein said hydroxy functional acrylic copolymer used to prepare said hydroxy functional acrylic organophosphate reactive catalyst is a copolymer prepared from at least about 50 weight percent of acrylate monomers and sufficient hydroxy functional monoethylenically unsaaturated monomers to provide the desired hydroxy functionality.
Claim 5
Dependent Claim
81 words
A composition in accordance with claim 3 wherein said copolymer has a glass transition temperature of between about -10° C. and about 50° C. and is prepared from at least 50 weight percent of acrylate monomers, sufficient hydroxy functional monoethylenically unsaturated monomers to provide the desired hydroxy functionality, and a remainder of monomers selected from C 8 -C 12 monovinyl hydrocarbons and vinyl modifying monomers, said vinyl modifying monomers comprising less than 10 weight percent of the monomers in said copolymer.
Claim 6
Dependent Claim
31 words
A composition in accordance with claim 1, wherein said hydroxy functional acrylic organophosphate reactive catalyst is the reaction product of an excess of said hydroxy functional acrylic copolymer and phosphorus pentoxide.
Claim 7
Dependent Claim
63 words
A composition in accordance with claim 1 wherein said amine-aldehyde crosslinking agent selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoguanamine, and substituted benzoguanamine, and mixtures of said condensation products, and is included in an amount sufficient to provide between about 0.6 and about 2.1 equivalents of nitrogen crosslinking of functionality per equivalent of hydroxy functionality.
Claim 8
Dependent Claim
77 words
A composition in accordance with claim 1 wherein said hydroxy functional additive is selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 30 weight percent of said copolymer, and (vi) mixtures of (i)-(v).
Claim 9
Dependent Claim
46 words
A composition in accordance with claim 1 wherein said hydroxy functional acrylic organophosphate reactive catalyst is included in said composition in an amount sufficient to provide between about 1.0 and about 1.2 equivalents of acid functionality for each equivalent of epoxy functionality on said polyepoxide resin.
References Cited (Backward Citations)
US2732367A
Cited
US2528360A
Cited
US2528359A
Cited
US2541027A
Cited
US2849418A
Cited
US3198850A
Cited
US3133838A
Cited
US3260622A
Cited
US3524903A
Cited
US3651169A
Cited
US4055607A
Cited
US3936416A
Cited
US3960979A
Cited
US4018848A
Cited
US4027066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-10 | 1983-06-11 | 1983-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-10 | 1987-06-11 | 1987-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-10 | 1991-06-11 | 1991-12-11 | $7700.00 | Window Closed / Lapsed |