Method for the manufacture of foamed glass
Assignee: Individual
•
Filing: 1978-01-16
•
Granted: 1979-12-11
•
Expires: 1998-01-16
Abstract
Abstract A method for the manufacture of foamed glass includes providing a mixture of a finely divided glass and a bonding agent. The bonding agent is selected from the group of aqueous solutions of the oxygen acids of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and phosphorous, the aqueous solutions of the anhydrides of the oxygen acids, and the aqueous solutions of the salts formed by the oxygen acids and the basic oxides, and basic hydroxides of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and of the transition metals having a variable oxidation number. The mixture is dried at a temperature from 20° to 600° C. to thereby transform the bonding agent into a gel having water bound thereto. The dried mixture is heated to a temperature from 800° to 1,000° C. to thereby melt the mixture and release the bound water from the gel. The released water forms a vaporous cellulating agent which effects the foaming of the molten glass.
Inventors
- 👤 Claus Wustefeld
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:21
CPC Classifications
C; C03; C03C; C03C11/00; C03C11/007; Y; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
190 words
In a method for the manufacture of foamed glass, the improvement comprising the steps of: providing a mixture of a finely divided glass and a bonding agent in a weight ratio of glass to bonding agent of 100 parts glass to 5-10 parts bonding agent, the bonding agent being an agent selected from the group of (1) the aqueous solutions of the oxygen acids of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and phosphorus, and (2) the aqueous solutions of the salts formed by said oxygen acids neutralized with basic oxides, or basic hydroxides of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and of the transition metals having a variable oxidation number; drying the mixture at a temperature from 20° to 600° C. to thereby transform the bonding agent into a gel having water bound thereto; and heating the dried mixture to a temperature from 800° to 1,000° C. to thereby melt the mixture and release the bound water from the gel, the released water forming a vaporous cellulating agent which effects the foaming of the molten glass, whereby the molten glass is foamed.
Claim 2
Dependent Claim
190 words
In a method for the manufacture of foamed glass, the improvement comprising the steps of: providing a mixture of a finely divided glass and a bonding agent in a weight ratio of glass to bonding agent of 100 parts glass to 5-10 parts bonding agent, the bonding agent being an agent selected from the group of (1) the aqueous solutions of the oxygen acids of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and phosphorus, and (2) the aqueous solutions of the salts formed by said oxygen acids neutralized with basic oxides, or basic hydroxides of beryllium, boron, aluminum, silicon, germanium, arsenic, antimony, tellurium, polonium, astatine and of the transition metals having a variable oxidation number; drying the mixture at a temperature from 20° to 600° C. to thereby transform the bonding agent into a gel having water bound thereto; and heating the dried mixture to a temperature from 800° to 1,000° C. to thereby melt the mixture and release the bound water from the gel, the released water forming a vaporous cellulating agent which effects the foaming of the molten glass, whereby the molten glass is foamed.
Claim 3
Dependent Claim
32 words
The method according to claim 1 in which the bonding agent is selected from the group of the aqueous solutions of phosphoric acid, boric acid, silicic acid, arsenious acid and antimonious acid.
Claim 4
Dependent Claim
41 words
The method according to claim 1 in which the bonding agent is selected from the group of the aqueous solutions of the salts of the said oxygen acids with the oxides and hydroxides of vanadium, manganese, iron cobalt, arsenic, and antimony.
Claim 5
Dependent Claim
26 words
The method according to claim 1 in which the bonding agent is selected from the group of the aqueous solutions of manganese phosphate and vanadium phosphate.
Claim 6
Dependent Claim
17 words
The method according to claim 1 in which a sodium phosphate is used in the bonding agent.
Claim 7
Dependent Claim
32 words
The method according to claim 1 in which further an oxidation agent selected from the group of secondary and tertiary manganese phosphates and H 2 O 2 is introduced into the mixture.
Claim 8
Dependent Claim
45 words
The method according to claim 1 in which further at least one additional composition selected from the group of the acid oxides of the transition metals, and difficultly soluble secondary and tertiary salts of the components of the bonding agent is introduced into the mixture.
Claim 9
Dependent Claim
70 words
The method according to claim 7 in which the additional composition is an amorphous mineral of the class AB 2 .nH 2 O of the cristallo-chemical mineral system, in which A and B each designate one atom and n is an integral number, and the said amorphous mineral is introduced into the mixture in a quantity up to approximately 25% by weight related to the total weight of the mixture.
Claim 10
Dependent Claim
29 words
The method according to claim 8 in which the amorphous mineral is essentially comprised of manganese black, and is used in a quantity of 0.2 to 2.5% by weight.
Claim 11
Dependent Claim
24 words
The method according to claim 8 in which the amorphous mineral is opal, and is used in a quantity of approximately 5% by weight.
Claim 12
Dependent Claim
45 words
The method according to claim 6 in which further at least one additional composition selected from the group of the acid oxides of the transition metals, and difficultly soluble secondary and tertiary salts of the components of the bonding agent is introduced into the mixture.
Claim 13
Dependent Claim
26 words
The method according to claim 1 in which in the bonding agent the ratio of acid to metal hydroxide is 3:1 to 1:1 parts by weight.
Claim 14
Dependent Claim
31 words
The method according to claim 1 in which, prior to the heating step, the dried mixture is ground to a fineness resulting in a BET area of 1 m 2 /g.
Claim 15
Dependent Claim
99 words
The method according to claim 1 in which the quantity of the bonding agent which is introduced into the mixture is a function of the surface area of the finely divided glass material according to the formula y=100(M/F.sub.M)·2F in which y is the quantity of the bonding agent in g per 100 g of the glass, M is the quantity of the bonding agent in Mol which spreads in a monomolecular layer over a surface area of F M =20000 m 2 , and F is the surface area evaluated by the BET-method of 100 g of the glass.
Claim 16
Dependent Claim
47 words
The method according to claim 1 in which the mixture of the finely divided glass and the bonding agent is given a plastic consistency, is continuously extruded to an endless strand having the cross-section of plates, and is then both dried and subsequently heated in the strand.
Claim 17
Dependent Claim
37 words
The method according to claim 1 in which, prior to the drying of the mixture, the components dissolved in the aqueous solution are precipitated by adding boric acid, in order to increase the surface of the mixture.
Claim 18
Dependent Claim
34 words
The method according to claim 16 in which, after the precipitation of the dissolved components, glass powder is added to the mixture in such a quantity as is required for rendering the mixture mouldable.
Claim 19
Dependent Claim
51 words
The method according to claim 1 in which approximately 1% lamellar minerals is further added to the mixture to thereby increase the surface area of the mixture, said lamellar minerals forming an aggregate of two-dimensional crystals when they pass the temperature range from 600° to 800° C. during the heating step.
Claim 20
Dependent Claim
14 words
The method according to claim 5 in which the sodium phosphate is sodium metaphosphate.
Claim 21
Dependent Claim
21 words
The method according to claim 1 in which the glass is selected from the group of waste glass and volcanic glass.
References Cited (Backward Citations)
US2337672A
Cited
US2399225A
Cited
GB623806A
Cited
US2596669A
Cited
US3342572A
Cited
US3325264A
Cited
US3546061A
Cited
US3663249A
Cited
US3870496A
Cited
US3867156A
Cited
US3932140A
Cited
US3951632A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-10 | 1983-06-11 | 1983-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-10 | 1987-06-11 | 1987-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-10 | 1991-06-11 | 1991-12-11 | $7700.00 | Window Closed / Lapsed |