US4177235A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing electrically fused corundum
Assignee: Dynamit Nobel AG
•
Filing: 1977-12-14
•
Granted: 1979-12-04
•
Expires: 1997-12-14
Abstract
Abstract A composition comprising α-alumina in a concentration of at least 99.95 weight percent and process for producing such α-alumina wherein alumina having an alkali metal content between 0.05 and 0.60 weight percent and Al 2 O 3 content of more than 95 weight percent is electrically fused with silica and additional alkali, if desired, in an electric arc furnace, the heated composition is cooled, comminuted and the so-formed glass phase is removed from an alumina containing phase by mechanical or chemical means.
Inventors
- 👤 Manfred Neidhardt
- 👤 Gerhard Rehfeld
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:21
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1427; C01; C01F; C01F7/00; C01F7/02; C01F7/46; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/107; C01P; C01P2002/00; C01P2002/02; C01P2004/00; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/32; C01P2006/33; C01P2006/36
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
114 words
A method for preparing an α-corundum composition having an α-corundum content of at least 99.95 weight percent from an alumina containing at least one impurity of the group consisting of TiO 2 , Fe 2 O 3 , CaO and MgO which comprises heating said alumina which has an alkali content of between 0.05 and 0.60 weight percent and an Al 2 O 3 content of more than 95 weight percent with SiO 2 in an electric arc furnace at a temperature sufficient to form a melt thereof, cooling said melt whereby to form a composition comprising an α-corundum phase in a siliceous matrix and thereafter separating said siliceous matrix from said α-corundum phase.
Claim 2
Independent Claim
114 words
A method for preparing an α-corundum composition having an α-corundum content of at least 99.95 weight percent from an alumina containing at least one impurity of the group consisting of TiO 2 , Fe 2 O 3 , CaO and MgO which comprises heating said alumina which has an alkali content of between 0.05 and 0.60 weight percent and an Al 2 O 3 content of more than 95 weight percent with SiO 2 in an electric arc furnace at a temperature sufficient to form a melt thereof, cooling said melt whereby to form a composition comprising an α-corundum phase in a siliceous matrix and thereafter separating said siliceous matrix from said α-corundum phase.
Claim 3
Dependent Claim
36 words
A method according to claim 1 wherein at least a stoichiometric amount of SiO 2 relevant to the alkali content is employed such that the alkali is bound by the SiO 2 as alkali metal silicate.
Claim 4
Dependent Claim
42 words
A method according to claim 1 wherein the SiO 2 is present in an amount greater than the stoichiometric amount relative to the alkali content up to 10 times the stoichiometric amount whereby to bind alkali metal present as alkali metal silicate.
Claim 5
Dependent Claim
38 words
A method according to claim 3 wherein the SiO 2 content of the mixture subjected to temperature in the electric arc furnace is up to 5 times the stoichiometric amount relative to the amount of alkali metal present.
Claim 6
Dependent Claim
36 words
A method according to claim 1 wherein the SiO 2 is supplied as quartz sand and the alumina is supplied as an alkali containing Bayer alumina having an alkali content of 0.2 to 0.6 weight percent.
Claim 7
Dependent Claim
29 words
A method according to claim 5 wherein a mixture of alumina and quartz sand are employed which supply silica in an amount of between 0.25 and 3.30 weight percent.
Claim 8
Dependent Claim
33 words
A method according to claim 1 wherein the mixture which is heated in the electric arc furnace has a total alkali oxide content of greater than 0.6 and up to 5% by weight.
Claim 9
Dependent Claim
28 words
A method according to claim 7 wherein the mixture which is heated in the electric arc furnace has a total alkali oxide of up to 3 weight percent.
Claim 10
Dependent Claim
22 words
A method according to claim 7 wherein the mixture contains more than 3.3 and up to 15 weight percent SiO 2 .
Claim 11
Dependent Claim
22 words
A method according to claim 1 wherein the melt is cooled in a controlled manner to provide α-corundum crystals of desired size.
Claim 12
Dependent Claim
26 words
A method according to claim 1 wherein the siliceous phase is separated from the α-corundum phase by subjecting the resultant composition to comminuting followed by sieving.
Claim 13
Dependent Claim
30 words
A method according to claim 1 wherein the siliceous phase is separated from the α-corundum by subjecting the resultant composition to washing with aqueous hydrochloric acid or aqueous hydrofluoric acid.
Claim 14
Dependent Claim
27 words
A method according to claim 12 wherein the comminuted material is washed with aqueous hydrochloric acid, thereafter washed with aqueous hydrofluoric acid and thereafter washed with water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-03 | 1983-06-04 | 1983-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-03 | 1987-06-04 | 1987-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-03 | 1991-06-04 | 1991-12-04 | $7700.00 | Window Closed / Lapsed |