Process for manufacturing sand cores or molds
Assignee: Ashland Inc
•
Filing: 1978-01-24
•
Granted: 1979-11-27
•
Expires: 1998-01-24
Abstract
Abstract Sand molds or cores are prepared by coating sand particles with an acid-curing condensation type resin consisting of poly furfuryl alcohol or admixtures of poly furfuryl alcohol with other acid-curing resins. The resin composition is formed into a desired shape and is cured at ambient temperature over a period of between a few seconds and a few minutes by means of an acid produced by in situ oxidation of sulfur dioxide. Sulfur dioxide is introduced into the molding composition together with an oxidizing agent which effects oxidation of the sulfur dioxide within the mold or core composition. Preferably, the oxidizing agent is an organic peroxide incorporated on the sand or introduced with the resin composition. The formation of sand cores or molds from resins comprising poly furfuryl alcohol results in products having improved tensile strengths, improved hardness, and characterized by virtually no migration or furfuryl alcohol polymers to or coating of the molds or patterns used in sand core or mold preparation.
Inventors
- 👤 Patrick H. Stewart
- 👤 Wayne D. Woodson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:34
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; B22C1/224; C; C08; C08L; C08L61/00; C08L61/34; C08L71/00; C08L71/08; C08L71/14
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
76 words
A process for the manufacture of sand cores or molds which comprises mixing sand with an acid-curing condensation-type resin comprising high viscosity poly furfuryl alcohol, adding a liquid or solid oxidant to said sand, forming said resin-sand-oxidant mixture into a predetermined shape, treating said shaped resin composition with sulfur dioxide at ambient temperature for a period between a few seconds and a few minutes to form sulfuric acid in situ and effect a rapid resin cure.
Claim 2
Dependent Claim
76 words
A process for the manufacture of sand cores or molds which comprises mixing sand with an acid-curing condensation-type resin comprising high viscosity poly furfuryl alcohol, adding a liquid or solid oxidant to said sand, forming said resin-sand-oxidant mixture into a predetermined shape, treating said shaped resin composition with sulfur dioxide at ambient temperature for a period between a few seconds and a few minutes to form sulfuric acid in situ and effect a rapid resin cure.
Claim 3
Dependent Claim
50 words
A process according to claim 1 in which said condensation type resin consists essentially of poly furfuryl alcohol or an admixture of poly furfuryl alcohol with a phenol-formaldehyde or urea-formaldhyde or phenol-urea-formaldehyde precondensate resin or a cocondensate of poly furfuryl alcohol with a phenol-formaldehyde or urea-formaldehyde or phenol-urea-formaldehyde precondensate resin.
Claim 4
Dependent Claim
52 words
A process according to claim 1 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer to a temperature of about 130°-200° F. and a pH of 1-3 in the substantial absence of water until a polymer having a viscosity greater than 400 cp. at 80° F. is obtained.
Claim 5
Dependent Claim
34 words
A process according to claim 1 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer in admixture with a minor amount of formaldehyde until a high viscosity polymer is obtained.
Claim 6
Dependent Claim
51 words
A process according to claim 2 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer to a temperature of about 130°-200° F. and a pH of 1-3 in the substantial absence of water until a polymer having viscosity greater than 400 cp. at 80° F. is obtained.
Claim 7
Dependent Claim
34 words
A process according to claim 2 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer in admixture with a minor amount of formaldehyde until a high viscosity polymer is obtained.
Claim 8
Dependent Claim
23 words
A process according to claim 1 in which said resin consists essentially of poly furfuryl alcohol containing less than 15% furfurfuryl alcohol monomer.
Claim 9
Dependent Claim
50 words
A process according to claim 7 in which said condensation type resin consists essentially of poly furfuryl alcohol or an admixture of poly furfuryl alcohol with a phenol-formaldehyde or urea-formaldehyde or phenol-urea-formaldehyde precondensate resin or a cocondensate of poly furfuryl alcohol with a phenol-formaldehyde or urea-formaldehyde or phenol-urea-formaldehyde precondensate resin.
Claim 10
Dependent Claim
51 words
A process according to claim 7 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer to a temperature of about 130°-200° F. and a pH of 1-3 in the substantial absence of water until a polymer having viscosity greater than 400 cp. at 80° F. is obtained.
Claim 11
Dependent Claim
26 words
A process according to claim 1 in which said resin composition is an admixture of poly furfuryl alcohol and a phenol-formaldehyde, urea-formaldehyde or phenol-urea-formaldehyde precondensate resin.
Claim 12
Dependent Claim
51 words
A process according to claim 10 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer to a termperature of about 130°-200° F. and a pH of 1-3 in the substantial absence of water until a polymer having viscosity greater than 400 cp. at 80° F. is obtained.
Claim 13
Dependent Claim
34 words
A process according to claim 10 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer in admixture with a minor amount of formaldehyde until a high viscosity polymer is obtained.
Claim 14
Dependent Claim
25 words
A process according to claim 1 in which said resin comprises a cocondensate of poly furfuryl alcohol with a phenol-formaldehyde, urea-formaldehyde or phenol-urea-formaldehyde precondensate resin.
Claim 15
Dependent Claim
51 words
A process according to claim 13 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer to a temperature of about 130°-200° F. and a pH of 1-3 in the substantial absence of water until a polymer having viscosity greater than 400 cp. at 80° F. is obtained.
Claim 16
Dependent Claim
34 words
A process according to claim 13 in which said poly furfuryl alcohol is prepared by heating furfuryl alcohol monomer in admixture with a minor amount of formaldehyde until a high viscosity polymer is obtained.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-26 | 1983-05-28 | 1983-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-26 | 1987-05-28 | 1987-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-26 | 1991-05-28 | 1991-11-27 | $7700.00 | Window Closed / Lapsed |