Production of ceramic powders for ferrite, spinel, titanate and garnet production
Assignee: Huntington Alloys Corp
•
Filing: 1977-01-17
•
Granted: 1979-11-20
•
Expires: 1997-01-17
Abstract
Abstract A process and products produced thereby, e.g., ferrites, in which ceramic powder particles are subjected to high transmissive energy milling under dry conditions and with given ratios of impacting media to powder, the milling being conducted for a period beyond the threshold point of the powder constituents, whereby dense, composite powder particles are obtained having an interdispersion of initial constituent particles, a large internal interfacial surface within individual product powder particles, etc.
Inventors
- 👤 Brian Hill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:11
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/09; C; C04; C04B; C04B33/00; C04B33/02; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/26; C04B35/46; C04B35/48; C04B35/50; C04B35/51; H01F1/0302; H01F1/0306
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
227 words
A process for producing dense, composite ceramic product powder particles, the product particles being characterized by (i) an intimate interdispersion of initial constituent particles, (ii) a large internal interfacial surface within individual product powder particles with the individual constituent particles being distributed substantially uniformly at close interparticle spacings within the product powder particles, which comprises forming a charge composed of milling impacting elements and the ceramic powder particles to be milled, the ceramic powder charge particles being formulated to provide composite product powder particles which upon heating react to form a member from the group consisting of spinels, ferrites, titanates and garnets, with the weight ratio of impacting elements to powder being greater than 3:1, subjecting the charge under dry conditions to high transmissive energy milling such that the individual constituent powder particles are continuously brought into contact with the compressive energies of the milling impacting elements, and continuing the milling for a period beyond the threshold point of the powder constituents such that the constituent powder particles undergo substantial mechanical cold bonding in the solid state and such that the surface area of the composite product powder particles is less than the constituent powders with the particle size being markedly increased, whereby dense, composite, mechanically cold bonded ceramic product powder particles are produced, the composite product particles being further characterized by a high degree of homogeneity.
Claim 2
Dependent Claim
227 words
A process for producing dense, composite ceramic product powder particles, the product particles being characterized by (i) an intimate interdispersion of initial constituent particles, (ii) a large internal interfacial surface within individual product powder particles with the individual constituent particles being distributed substantially uniformly at close interparticle spacings within the product powder particles, which comprises forming a charge composed of milling impacting elements and the ceramic powder particles to be milled, the ceramic powder charge particles being formulated to provide composite product powder particles which upon heating react to form a member from the group consisting of spinels, ferrites, titanates and garnets, with the weight ratio of impacting elements to powder being greater than 3:1, subjecting the charge under dry conditions to high transmissive energy milling such that the individual constituent powder particles are continuously brought into contact with the compressive energies of the milling impacting elements, and continuing the milling for a period beyond the threshold point of the powder constituents such that the constituent powder particles undergo substantial mechanical cold bonding in the solid state and such that the surface area of the composite product powder particles is less than the constituent powders with the particle size being markedly increased, whereby dense, composite, mechanically cold bonded ceramic product powder particles are produced, the composite product particles being further characterized by a high degree of homogeneity.
Claim 3
Dependent Claim
17 words
A process in accordance with claim 1 in which nickel oxide forms one of initial powder constituents.
Claim 4
Dependent Claim
20 words
The process in accordance with claim 1 in which nickel oxide and ferric iron oxide comprise the initial powder constituents.
Claim 5
Dependent Claim
22 words
The process in accordance with claim 1 in which at least nickel oxide and zinc oxide are used as initial powder constituents.
Claim 6
Dependent Claim
19 words
The process in accordance with claim 1 in which the initial powder particles are selected to give barium ferrite.
Claim 7
Dependent Claim
19 words
The process in accordance with claim 1 in which the initial powder particles are selected to give barium titanate.
Claim 8
Dependent Claim
20 words
The process in accordance with claim 1 in which the initial powder particles are selected to give yttrium iron garnet.
Claim 9
Dependent Claim
21 words
A process for producing ferrite particles in which the product powder particles of claim 2 are reacted to form ferrite particles.
Claim 10
Dependent Claim
21 words
A process for producing ferrite particles in which the product powder particles of claim 4 are reacted to form ferrite particles.
Claim 11
Dependent Claim
24 words
A process for producing a ferrite body in which the ferrite particles of claim 8 are consolidated and fired to produce the ferrite body.
Claim 12
Dependent Claim
24 words
A process for producing a ferrite body in which the ferrite particles of claim 9 are consolidated and fired to produce the ferrite body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-19 | 1983-05-21 | 1983-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-19 | 1987-05-21 | 1987-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-19 | 1991-05-21 | 1991-11-20 | $7700.00 | Window Closed / Lapsed |