Method of making expandable polystyrene beads
Assignee: BASF Corp
•
Filing: 1978-07-21
•
Granted: 1979-11-13
•
Expires: 1998-07-21
Abstract
Abstract Expandable-polystyrene beads suitable for use in making impervious containers are made from a recipe including styrene, free-radical initiator and polyvinyl pyrrolidone, and this practice includes a step of washing the beads in a warm aqueous solution to which an alkoxylated nonionic surfactant having 70-90 percent of its molecular weight accounted for by oxyethylene units is added in an amount effective to cause the washing to remove contaminating grafted polyvinyl pyrrolidone from the surface of the beads and cause them to become expandable into impervious product containers.
Inventors
- 👤 Pauls Davis
- 👤 Herbert H. Gahmig
- 👤 Irving R. Schmolka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:46
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/22; C08J2325/00; C08J2325/02; C08J2325/04; C08J2325/06; Y; Y10; Y10S; Y10S521/00; Y10S521/905; Y10S521/911; Y10S521/918
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
116 words
In making beads of expandable-polystyrene destined for container use from a recipe including styrene, free-radical initiator, and polyvinyl pyrrolidone, the improvement comprising washing the beads for about 3 to 10 hours at a temperature of about 40-55 degrees Centigrade in an aqueous solution of a hydrophilic alkoxylated nonionic surfactant which is solid at room temperature and has a molecular weight, 70-90 percent of which is accounted for by oxyethylene units, said surfactant being present in said aqueous solution in an amount between 0.001 and 1%, said amount being effective to cause said washing to remove contaminating grafted polyvinyl pyrrolidone from the surface of said beads and cause said beads to become expandable into impervious product containers.
Claim 2
Dependent Claim
116 words
In making beads of expandable-polystyrene destined for container use from a recipe including styrene, free-radical initiator, and polyvinyl pyrrolidone, the improvement comprising washing the beads for about 3 to 10 hours at a temperature of about 40-55 degrees Centigrade in an aqueous solution of a hydrophilic alkoxylated nonionic surfactant which is solid at room temperature and has a molecular weight, 70-90 percent of which is accounted for by oxyethylene units, said surfactant being present in said aqueous solution in an amount between 0.001 and 1%, said amount being effective to cause said washing to remove contaminating grafted polyvinyl pyrrolidone from the surface of said beads and cause said beads to become expandable into impervious product containers.
Claim 3
Dependent Claim
54 words
An improvement as defined in claim 1, wherein said surfactant is a block copolymer based upon ethylene glycol, which is first oxyethylated to an extent such that the oxyethylene units account for approximately 80 percent of the total molecular weight, and then capped with oxypropylene units, the total average molecular weight being about 9000.
References Cited (Backward Citations)
US3001954A
Cited
US3468820A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-12 | 1983-05-14 | 1983-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-12 | 1987-05-14 | 1987-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-12 | 1991-05-14 | 1991-11-13 | $7700.00 | Window Closed / Lapsed |