Nitrile preforms and containers and process improvements for forming same
Assignee: Hoover Universal Inc
•
Filing: 1977-11-10
•
Granted: 1979-11-13
•
Expires: 1997-11-10
Abstract
Abstract In forming containers by distending preforms of nitrile thermoplastic material at molding temperature, the improvement comprising exposing such preforms to low dosage radiation to reduce residual nitrile monomer in the thermoplastic material and then distending the irradiated preforms to cause HCN generated during irradiation to flash off in forming the container. The containers formed have unusually low concentrations of residual nitrile monomer as well as extractable HCN making them especially suitable for packaging foods, beverages, pharmaceuticals and the like. The irradiated preforms from which such containers are made have similarly low residual nitrile monomer levels.
Inventors
- 👤 Morris Salame
- 👤 Samuel Steingiser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:41
CPC Classifications
B; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B29; B29C; B29C49/00; B29C49/0005; B29C49/071; B29C71/00; B29C71/04; B29C2949/00; B29C2949/07; B29C2949/072; B29C2949/0722; B29C2949/073; B29C2949/0731; B29C2949/074; B29C2949/0744; B29C2949/076; B29C2949/0768; B29C2949/077; B29C2949/0772; B29C2949/0773; B29C2949/081; B29C2949/0811; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/26; B29C2949/28; B29C2949/30; B29C2949/3024; B29C2949/3032; B29C2949/3041; B29C2949/3048; B29C2949/3056; B29C2949/3086; B29C2949/3088; B29C2949/309; B29C48/00; B29C48/03; B29C48/09; B29K; B29K2105/00; B29K2105/25; B29K2105/253; B29K2633/00; B29K2633/18; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1397; Y10T428/31504; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 53
Claim 1
Independent Claim
78 words
In the process of forming containers from preforms of thermoplastic material comprising at least about 20 weight percent of polymerized nitrile-group-containing monomer which includes distending the preforms while at molding temperature into containers in a mold, the improvement which comprises: exposing the preforms to low dosage electron beam radiation prior to said distending; whereby said radiation causes polymerization of unpolymerized nitrile-group-containing monomer and said distending causes HCN generated during such irradiation to be reduced in the thermoplastic material.
Claim 2
Dependent Claim
78 words
In the process of forming containers from preforms of thermoplastic material comprising at least about 20 weight percent of polymerized nitrile-group-containing monomer which includes distending the preforms while at molding temperature into containers in a mold, the improvement which comprises: exposing the preforms to low dosage electron beam radiation prior to said distending; whereby said radiation causes polymerization of unpolymerized nitrile-group-containing monomer and said distending causes HCN generated during such irradiation to be reduced in the thermoplastic material.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the preforms have a thickness of beteen about 0.1 to 0.6 cms.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein the thermoplastic material during distension is at molecular orientation temperature.
Claim 5
Dependent Claim
20 words
The process of claim 3 wherein the dosage of electron beam radiation is between about 0.01 to about 1.0 megarads.
Claim 6
Dependent Claim
23 words
The process of claim 4 wherein a formaldehyde compound is present in the thermoplastic material at the time of exposure to said radiation.
Claim 7
Dependent Claim
23 words
The process of claim 5 wherein the nitrile-group-containing monomer is selected from the group of monomers consisting of acrylonitrile, methacrylonitrile and mixtures thereof.
Claim 8
Dependent Claim
11 words
The process of claim 6 wherein the nitrile-group-containing monomer is acrylonitrile.
Claim 9
Dependent Claim
98 words
In the process of forming containers for environmentally sensitive materials from preforms of thermoplastic material comprising at least 20 weight percent of polymerized nitrile-group-containing monomer which includes distending the preforms while at blow molding temperature into the containers in a mold, the improvement minimizing unpolymerized nitrile-group-containing monomer and extractable HCN in the walls of the containers which comprises: distending irradiated preforms containing no greater than about 1.5 ppm of unpolymerized nitrile-group-containing monomer based on the weight of total polymer in the cavity of a mold into container form whereby said HCN is reduced without increasing said unpolymerized monomer.
Claim 10
Dependent Claim
98 words
In the process of forming containers for environmentally sensitive materials from preforms of thermoplastic material comprising at least 20 weight percent of polymerized nitrile-group-containing monomer which includes distending the preforms while at blow molding temperature into the containers in a mold, the improvement minimizing unpolymerized nitrile-group-containing monomer and extractable HCN in the walls of the containers which comprises: distending irradiated preforms containing no greater than about 1.5 ppm of unpolymerized nitrile-group-containing monomer based on the weight of total polymer in the cavity of a mold into container form whereby said HCN is reduced without increasing said unpolymerized monomer.
Claim 11
Dependent Claim
23 words
The process of claim 8 wherein extractable HCN based on extracting liquid, during distension, is reduced to no greater than about 50 ppb.
Claim 12
Dependent Claim
18 words
The process of claim 8 wherein the thickness of the preforms is between about 0.1 to 0.6 cms.
Claim 13
Dependent Claim
19 words
The process of claim 8 wherein at least portions of the preforms are at molecular orientation temperature during distension.
Claim 14
Dependent Claim
23 words
The process of claim 11 wherein extractable HCN based on extracting liquid, during distension, is reduced to no greater than about 50 ppb.
Claim 15
Dependent Claim
20 words
The process of claim 12 wherein the dosage of electron beam radiation is between about 0.05 to about 0.8 megarads.
Claim 16
Dependent Claim
25 words
The process of claim 13 wherein an effective amount of an HCN scavenging compound is present in the thermoplastic material during exposure to said irradiation.
Claim 17
Dependent Claim
23 words
The process of claim 13 wherein the nitrile-group-containing monomer is selected from the group of monomers consisting of acrylonitrile, methacrylonitrile and mixtures thereof.
Claim 18
Dependent Claim
11 words
The process of claim 15 wherein the nitrile-group-containing monomer is acrylonitrile.
Claim 19
Dependent Claim
19 words
The process of claim 16 wherein the thermoplastic material comprises from about 55 to about 85 weight percent acrylonitrile.
Claim 20
Dependent Claim
107 words
In the process of forming containers for foods, beverages, pharmaceuticals and the like from tubular preforms comprising a major proportion of polymerized nitrile-group-containing monomer which includes distending the preforms while at molding temperature into the containers in a mold, the improvement wherein unpolymerized nitrile-group-containing monomer and extractable HCN in the walls of the containers are reduced which comprises: distending irradiated preforms containing (a) no greater than about 1.5 ppm unpolymerized nitrile-group-containing monomer based on the total weight of the polymer and (b) a detectable extractable HCN content, in the cavity of a mold into container form whereby said HCN content is reduced without increasing said unpolymerized monomer.
Claim 21
Dependent Claim
107 words
In the process of forming containers for foods, beverages, pharmaceuticals and the like from tubular preforms comprising a major proportion of polymerized nitrile-group-containing monomer which includes distending the preforms while at molding temperature into the containers in a mold, the improvement wherein unpolymerized nitrile-group-containing monomer and extractable HCN in the walls of the containers are reduced which comprises: distending irradiated preforms containing (a) no greater than about 1.5 ppm unpolymerized nitrile-group-containing monomer based on the total weight of the polymer and (b) a detectable extractable HCN content, in the cavity of a mold into container form whereby said HCN content is reduced without increasing said unpolymerized monomer.
Claim 22
Dependent Claim
20 words
The process of claim 18 wherein the preforms before distending have a thickness of between about 0.1 to 0.6 cms.
Claim 23
Dependent Claim
18 words
The process of claim 18 including rotating the preforms about their longitudinal axes during exposure to the radiation.
Claim 24
Dependent Claim
63 words
An irradiated preform for conversion into a container for environmentally sensitive materials, said preform being formed of a thermoplastic material comprising at least 20 weight percent of a polymerized nitrile-group-containing monomer and an effective amount of an HCN scavenger, the level of unpolymerized nitrile monomer in such preform being no greater than about 1.5 ppm based on the total weight of the polymer.
Claim 25
Dependent Claim
63 words
An irradiated preform for conversion into a container for environmentally sensitive materials, said preform being formed of a thermoplastic material comprising at least 20 weight percent of a polymerized nitrile-group-containing monomer and an effective amount of an HCN scavenger, the level of unpolymerized nitrile monomer in such preform being no greater than about 1.5 ppm based on the total weight of the polymer.
Claim 26
Dependent Claim
23 words
The preform of claim 21 wherein the nitrile-group-containing monomer is selected from the group of monomers consisting of acrylonitrile, methacrylonitrile and mixtures thereof.
Claim 27
Dependent Claim
13 words
The preform of claim 21 wherein the HCN scavenger is a formaldehyde compound.
Claim 28
Dependent Claim
11 words
The preform of claim 22 wherein the nitrile-group-containing monomer is acrylonitrile.
Claim 29
Dependent Claim
22 words
The preform of claim 22 wherein the nitrile-group-containing monomer comprises from about 55 to about 85 weight percent of the polymerized monomer.
Claim 30
Dependent Claim
10 words
The preform of claim 25 wherein the monomer is acrylonitirle.
Claim 31
Dependent Claim
9 words
The preform of claim 26 having a tubular shape.
Claim 32
Dependent Claim
58 words
A container for environmentally sensitive materials formed of an irradiated thermoplastic material comprising at least 20 weight percent of a polymerized nitrile-group-containing monomer, said container having levels of unpolymerized nitrile monomer and extractable HCN of no greater than about 0.8 ppm based on the total weight of the polymer and about 50 ppb based on extracting liquid respectively.
Claim 33
Dependent Claim
58 words
A container for environmentally sensitive materials formed of an irradiated thermoplastic material comprising at least 20 weight percent of a polymerized nitrile-group-containing monomer, said container having levels of unpolymerized nitrile monomer and extractable HCN of no greater than about 0.8 ppm based on the total weight of the polymer and about 50 ppb based on extracting liquid respectively.
Claim 34
Dependent Claim
23 words
The container of claim 28 wherein the nitrile-group-containing monomer is selected from the group of monomers consisting of acrylonitrile, methacrylonitrile and mixtures thereof.
Claim 35
Dependent Claim
20 words
The container of claim 28 wherein the extractable HCN based on extracting liquid is no greater than about 20 ppb.
Claim 36
Dependent Claim
19 words
The container of claim 28 wherein the level of unpolymerized nitrile monomer is no greater than about 0.5 ppm.
Claim 37
Dependent Claim
11 words
The container of claim 29 wherein the nitrile-group-containing monomer is acrylonitrile.
Claim 38
Dependent Claim
22 words
The container of claim 29 wherein the nitrile-group-containing monomer comprises from about 55 to about 85 weight percent of the polymerized monomer.
Claim 39
Dependent Claim
10 words
The container of claim 33 wherein the monomer is acrylonitrile.
Claim 40
Dependent Claim
16 words
The container of claim 33 wherein at least portions of the walls thereof are molecularly oriented.
Claim 41
Dependent Claim
15 words
The container of claim 28 including a food, beverage, pharmaceutical or the like packaged therein.
Claim 42
Dependent Claim
15 words
The container of claim 29 including a food, beverage, pharmaceutical or the like packaged therein.
Claim 43
Dependent Claim
15 words
The container of claim 33 including a food, beverage, pharmaceutical or the like packaged therein.
Claim 44
Dependent Claim
15 words
The container of claim 34 including a food, beverage, pharmaceutical or the like packaged therein.
Claim 45
Dependent Claim
29 words
The container of claim 39 wherein the level of acrylonitrile monomer in the contents is less than 10 ppb based on extracting liquid after 30 days at 49° C.
Claim 46
Dependent Claim
8 words
Containers formed by the process of claim 1.
Claim 47
Dependent Claim
8 words
Containers formed by the process of claim 8.
Claim 48
Dependent Claim
8 words
Containers formed by the process of claim 18.
Claim 49
Dependent Claim
18 words
Environmentally sensitive substances such as foods, beverages, pharmaceuticals or the like packaged in the containers of claim 41.
Claim 50
Dependent Claim
18 words
Environmentally sensitive substances such as foods, beverages, pharmaceuticals or the like packaged in the containers of claim 32.
Claim 51
Dependent Claim
18 words
Environmentally sensitive substances such as foods, beverages, pharmaceuticals or the like packaged in the containers of claim 43.
Claim 52
Dependent Claim
17 words
The container of claim 28 wherein the environmentally sensitive materials comprise foods, pharmaceuticals, beverages, and the like.
Claim 53
Dependent Claim
15 words
The container of claim 28 having a capacity of about 120 to 3780 cubic centimeters.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-12 | 1983-05-14 | 1983-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-12 | 1987-05-14 | 1987-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-12 | 1991-05-14 | 1991-11-13 | $7700.00 | Window Closed / Lapsed |