US4173672A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Decorated safety glass
Assignee: Individual
•
Filing: 1977-09-06
•
Granted: 1979-11-06
•
Expires: 1997-09-06
Abstract
Abstract A method to decorated laminate glass comprised of two glass sheets joined by a decorated film of a thermoplastic polymer. A sheet of glass, the film and a lamina of cellulosic material, decorated on the surface that contacts the film, are subjected to pressure and heat so as to transfer, by sublimation, said decoration to the film at the moment that it adheres itself to the surface of the glass. A second sheet of glass is over-placed on the decorated film and pressed to it, with heat, so as to form a safety glass decorated and/or colored in the interior.
Inventors
- 👤 Jose R. Mannheim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:06
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10009; B32B17/10036; B32B27/00; B32B27/30; B32B27/306; B32B17/10165; B32B17/10174; B32B17/10247; B32B17/10256; B32B17/10275; B32B17/1055; B32B17/10761; B32B17/10807; B41; B41M; B41M1/00; B41M1/26; B41M1/34; B44; B44C; B44C1/00; B44C1/16; B44C1/165; B44C1/17; B44C1/1712; B44C3/00; B44C3/02; B44F; B44F1/00; B44F1/06; B44F1/066; B32B2329/00; B32B2329/06; Y; Y10; Y10S; Y10S428/00; Y10S428/914; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24851; Y10T428/24868; Y10T428/24926; Y10T428/31504; Y10T428/31551; Y10T428/31627; Y10T428/3163
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
141 words
A method of manufacturing decorated colored glass comprising the following steps: (a) transferring, with heat and pressure, a color impression from a printed cellulosic support into an adhesive plastic polyvinyl butyral film spread on a lamina of glass for a time period sufficient for the film to become semi-fluid and for the colorants to permeate the entire thickness thereof; (b) removing the cellulosic support when the color impression has been transferred from the cellulosic layer into the polyvinyl butyral film and when said film has been permanently adhered to said lamina of glass; (c) placing a second lamina over the decorated polyvinyl butyral film, in direct contact with it; and (d) laminating these two lamina and said interposed decorated film at a pressure ranging from 25 psi to 850 psi and at a temperature ranging from 70° C. to 350° C.
Claim 2
Independent Claim
141 words
A method of manufacturing decorated colored glass comprising the following steps: (a) transferring, with heat and pressure, a color impression from a printed cellulosic support into an adhesive plastic polyvinyl butyral film spread on a lamina of glass for a time period sufficient for the film to become semi-fluid and for the colorants to permeate the entire thickness thereof; (b) removing the cellulosic support when the color impression has been transferred from the cellulosic layer into the polyvinyl butyral film and when said film has been permanently adhered to said lamina of glass; (c) placing a second lamina over the decorated polyvinyl butyral film, in direct contact with it; and (d) laminating these two lamina and said interposed decorated film at a pressure ranging from 25 psi to 850 psi and at a temperature ranging from 70° C. to 350° C.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein the plastic film bearing the color-impression remains strongly adhered to the sheet of glass when the cellulosic support is removed from the three-layer composite.
Claim 4
Dependent Claim
31 words
The method of claim 1 wherein the plastic film, bearing the color impression, is covered with another film of polyvinyl butyral before said second lamina is over-placed on said decorated film.
Claim 5
Dependent Claim
32 words
The method of claim 1, further including between steps (b) and (c), the steps of cleaning the affixed film, and drying the same to a humidity content of from 0.1 to 2.5%.
Claim 6
Dependent Claim
62 words
The method of claim 1 wherein the plastic sheet, bearing the color impression, is covered with a second and permanent lamina to form a composite of three elements comprising two outer sheets and a core adhesive element of decorative polyvinyl butyral, this composite being subjected to a lamination at temperatures in the range of 60° to 220° C. to eliminate the air.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein the plastic sheet bearing the color impression is covered with a permanent lamina of transparent synthetic material.
Claim 8
Dependent Claim
26 words
The method of claim 5, wherein the laminate composite is autoclaved at a temperature ranging from 75° C. to 150° C. and pressure of 100 psi.
Claim 9
Dependent Claim
22 words
The method of claim 7, wherein step (d) is carried out for a time period of from 30 minutes to 24 hours.
Claim 10
Dependent Claim
52 words
The method of claim 1 wherein said printed cellulose support, said adhesive film and said sheet of glass forming a sandwich, at the center of which is the polyvinyl butyral film, is subjected to temperatures between 60° to 220° C. and pressure between 100 to 1,000 gr/cm 2 in the thermo-impression process.
Claim 11
Dependent Claim
25 words
The method of claim 9 wherein the printed cellulosic support is covered with a temporary rigid sheet, of metal or glass, during the thermo-impression process.
Claim 12
Dependent Claim
20 words
The method of claim 9 wherein the film and lamina of glass are dried to a humidity content of 0.3%.
Claim 13
Dependent Claim
13 words
The product of the method of claim 1, wherein said product is transparent.
Claim 14
Dependent Claim
13 words
The product of the method of claim 1 wherein said product is translucent.
Claim 15
Dependent Claim
13 words
The product of the method of claim 1 wherein said product is opaque.
References Cited (Backward Citations)
GB717387A
Cited
US3537944A
Cited
US3922546A
Cited
US3922445A
Cited
US3860388A
Cited
US4059471A
Cited
US3868286A
Cited
JPS5038152A
Cited
US3952131A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-05 | 1983-05-07 | 1983-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-05 | 1987-05-07 | 1987-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-05 | 1991-05-07 | 1991-11-06 | $7700.00 | Window Closed / Lapsed |