Elastoplastic compositions of rubber and polyamide
Assignee: Advanced Elastomer Systems LP
•
Filing: 1977-07-15
•
Granted: 1979-11-06
•
Expires: 1997-07-15
Abstract
Abstract Elastoplastic compositions are described comprising blends of cross-linked rubber and thermoplastic polyamide.
Inventors
- 👤 Aubert Y. Coran
- 👤 Raman P. Patel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:57
CPC Classifications
C; C08; C08L; C08L77/00; C08L77/02; C08L77/06; C08L9/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
154 words
An elastoplastic composition comprising a blend essentially free of low molecular weight phenol plasticizer of (a) thermoplastic crystalline polyamide in an amount sufficient to impart thermoplasticity up to 50 weight percent of the composition, wherein the polyamide in said blend retains at least 50% of its original crystallinity, (b) rubber cross-linked to the extent that the gel content of the rubber is at least about 80 percent, wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is a homopolymer of 1,3-butadiene, copolymer of 1,3-butadiene or isoprene or mixtures thereof, in an amount sufficient to impart rubberlike elasticity up to 80 weight percent of the composition provided that, when the amount of polyamide exceeds the amount of rubber, sufficient inert plasticizer is present to impart rubberlike elasticity to the composition which composition is processable as a thermoplastic and is elastomeric.
Claim 2
Dependent Claim
154 words
An elastoplastic composition comprising a blend essentially free of low molecular weight phenol plasticizer of (a) thermoplastic crystalline polyamide in an amount sufficient to impart thermoplasticity up to 50 weight percent of the composition, wherein the polyamide in said blend retains at least 50% of its original crystallinity, (b) rubber cross-linked to the extent that the gel content of the rubber is at least about 80 percent, wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is a homopolymer of 1,3-butadiene, copolymer of 1,3-butadiene or isoprene or mixtures thereof, in an amount sufficient to impart rubberlike elasticity up to 80 weight percent of the composition provided that, when the amount of polyamide exceeds the amount of rubber, sufficient inert plasticizer is present to impart rubberlike elasticity to the composition which composition is processable as a thermoplastic and is elastomeric.
Claim 3
Dependent Claim
37 words
The composition of claim 1 containing inert plasticizer in an amount not exceeding the weight of polyamide in which the total weight of the rubber and inert plasticizer does not exceed 80 weight percent of the composition.
Claim 4
Dependent Claim
34 words
The composition of claim 2 in which the inert plasticizer is selected from the group consisting of phthalate plasticizers, adipate plasticizers, phosphate plasticizers, glycolate plasticizers, sulfonamide plasticizers, trimellitate plasticizers and polymeric type permanent plasticizers.
Claim 5
Dependent Claim
13 words
The composition of claim 3 in which the plasticizer is a sulfonamide plasticizer.
Claim 6
Dependent Claim
133 words
An elastoplastic composition comprising a blend essentially free of low molecular weight phenol plasticizer, of (a) about 20-50 parts by weight of thermoplastic crystalline polyamide, wherein the polyamide in said blend retains at least 50% of its original crystallinity and (b) about 80-50 parts by weight of rubber per 100 parts total weight of polyamide and rubber, wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is cross-linked to the extent that the gel content of the rubber is at least about 80 percent, the rubber being a homopolymer of 1,3-butadiene, a copolymer of 1,3-butadiene or isoprene copolymerized with vinylarene monomer or vinyl nitrile monomer or mixtures thereof, which composition is processable as a thermoplastic and is elastomeric.
Claim 7
Dependent Claim
133 words
An elastoplastic composition comprising a blend essentially free of low molecular weight phenol plasticizer, of (a) about 20-50 parts by weight of thermoplastic crystalline polyamide, wherein the polyamide in said blend retains at least 50% of its original crystallinity and (b) about 80-50 parts by weight of rubber per 100 parts total weight of polyamide and rubber, wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is cross-linked to the extent that the gel content of the rubber is at least about 80 percent, the rubber being a homopolymer of 1,3-butadiene, a copolymer of 1,3-butadiene or isoprene copolymerized with vinylarene monomer or vinyl nitrile monomer or mixtures thereof, which composition is processable as a thermoplastic and is elastomeric.
Claim 8
Dependent Claim
36 words
The composition of claim 5 containing inert plasticizer in an amount not exceeding the weight of polyamide in which the total weight of the rubber and plasticizer does not exceed 80 weight percent of the composition.
Claim 9
Dependent Claim
33 words
The composition of claim 6 in which the plasticizer is selected from the group consisting of phthalate plasticizers, adipate plasticizers, phosphate plasticizers, glycolate plasticizers, sulfonamide plasticizers, trimellitate plasticizers and polymeric type permanent plasticizers.
Claim 10
Dependent Claim
13 words
The composition of claim 7 in which the plasticizer is a sulfonamide plasticizer.
Claim 11
Dependent Claim
15 words
The composition of claim 6 wherein the polyamide has a melting point between 160°-230° C.
Claim 12
Dependent Claim
56 words
The composition of claim 5 in which the rubber is cross-linked to the extent that the composition contains no more than about four percent by weight of rubber extractable at room temperature or that the cross-link density determined on the same rubber as the composition is greater than about 3×10 -5 moles per ml of rubber.
Claim 13
Dependent Claim
30 words
The composition of claim 10 in which the rubber is cross-linked to the extent that the cross-link density of the rubber is at least about 5×10 -5 moles per ml.
Claim 14
Dependent Claim
18 words
The composition of claim 10 which contains no more than about four percent by weight of rubber extractable.
Claim 15
Dependent Claim
16 words
The composition of claim 11 in which the rubber is a copolymer of 1,3-butadiene and acrylonitrile.
Claim 16
Dependent Claim
14 words
The composition of claim 13 in which the polyamide is a crystalline linear polyamide.
Claim 17
Dependent Claim
18 words
The composition of claim 5 prepared by masticating the blend at cross-linking temperature until the rubber is cross-linked.
Claim 18
Dependent Claim
29 words
The composition of claim 14 in which the blend comprises about 20 to about 45 parts by weight polyamide and about 80 to about 55 parts by weight rubber.
Claim 19
Dependent Claim
21 words
The composition of claim 16 having a tensile strength at least 50% higher than that of the composition containing noncross-linked rubber.
Claim 20
Dependent Claim
14 words
The composition of claim 13 in which the polyamide is a crystalline linear polylactam.
Claim 21
Dependent Claim
11 words
The composition of claim 18 in which the polyamide is polycaprolactam.
Claim 22
Dependent Claim
14 words
The composition of claim 12 in which the rubber is a homopolymer of 1,3-butadiene.
Claim 23
Dependent Claim
29 words
The composition of claim 20 in which the blend comprises about 20 to about 45 parts by weight polyamide and about 80 to about 55 parts by weight rubber.
Claim 24
Dependent Claim
22 words
The composition of claim 21 having a tensile stength at least 50% higher than that of the same composition containing noncross-linked rubber.
Claim 25
Dependent Claim
13 words
The composition of claim 5 in which the rubber is self-curing nitrile rubber.
Claim 26
Dependent Claim
14 words
The composition of claim 14 in which the particle size is below 20 microns.
Claim 27
Dependent Claim
11 words
The composition of claim 1 containing 10-30 weight percent inert plasticizer.
Claim 28
Dependent Claim
11 words
The composition of claim 5 containing 10-30 weight percent inert plasticizer.
Claim 29
Dependent Claim
113 words
The An elastoplastic composition consisting essentially of a blend of about 20-50 parts by weight of thermoplastic crystalline polyamide wherein the polyamide in said blend retains at least 50% of its original crystallinity and about 80-50 parts by weight of rubber per 100 parts total weight of polyamide and rubber wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is a homopolymer of 1,3-butadiene or copolymer of 1,3-butadiene or isoprene or mixtures thereof and is cross-linked to the extent that the gel content is at least about 80 percent, which composition is processable as thermoplastic and is elastomeric.
Claim 30
Dependent Claim
113 words
The An elastoplastic composition consisting essentially of a blend of about 20-50 parts by weight of thermoplastic crystalline polyamide wherein the polyamide in said blend retains at least 50% of its original crystallinity and about 80-50 parts by weight of rubber per 100 parts total weight of polyamide and rubber wherein the rubber in said blend is in the form of small dispersed particles essentially of the size of 50 microns or below and is a homopolymer of 1,3-butadiene or copolymer of 1,3-butadiene or isoprene or mixtures thereof and is cross-linked to the extent that the gel content is at least about 80 percent, which composition is processable as thermoplastic and is elastomeric.
Claim 31
Dependent Claim
48 words
The composition of claim 27 in which the blend contains about 20-45 parts by weight of thermoplastic crystalline polyamide and about 80-55 parts by weight of rubber per 100 parts total weight of polyamide and rubber, the rubber being a copolymer of 1,3-butadiene copolymerized with vinyl nitrile monomer.
Claim 32
Dependent Claim
13 words
The composition of claim 28 in which the vinyl nitrile monomer is acrylonitrile.
Claim 33
Dependent Claim
18 words
The composition of claim 29 which contains a phenolic compound having a molecular weight of at least 200.
Claim 34
Dependent Claim
44 words
A modified thermoplastic crystalline polyamide prepared by blending said polyamide and elastoplastic composition of claim 27 in an amount such that the modified polyamide contains about 5 to 50 parts by weight of rubber per about 95 to 50 parts total weight of polyamide.
Claim 35
Dependent Claim
40 words
The polyamide of claim 31 in which the elastoplastic composition contains about 20 to 50 parts by weight of thermoplastic crystalline polyamide and 80 to 50 parts by weight of rubber per 100 parts total weight of polyamide and rubber.
Claim 36
Dependent Claim
20 words
The polyamide of claim 32 in which the rubber of the elastoplastic composition is a copolymer of 1,3-butadiene and acrylonitrile.
Claim 37
Dependent Claim
21 words
The polyamide of claim 33 in which the polyamide is linear polyamide having a melting point between 160° to 230° C.
Claim 38
Dependent Claim
11 words
The polyamide of claim 34 in which the polyamide is polycaprolactam.
References Cited (Backward Citations)
CA533879A
Cited
US2249686A
Cited
US2683697A
Cited
US2809944A
Cited
GB866479A
Cited
US3388083A
Cited
US3468974A
Cited
GB1190049A
Cited
FR1592857A
Cited
US3701702A
Cited
US3853796A
Cited
US3965055A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-05 | 1983-05-07 | 1983-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-05 | 1987-05-07 | 1987-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-05 | 1991-05-07 | 1991-11-06 | $7700.00 | Window Closed / Lapsed |