Foamable heat insulating compositions containing alkali silicate and alumina cement
Assignee: SK Kaken Co Ltd
•
Filing: 1977-12-14
•
Granted: 1979-10-23
•
Expires: 1997-12-14
Abstract
Abstract A process for manufacturing inorganic heat insulating material by mixing up water-soluble alkali silicate, alumina cement, metal base foaming agent and foam stabilizing agent into pasty state under presence of water. The heat insulating material manufactured by this process is of the class useful for heat insulating walls of buildings and for heat insulating plates incorporated in machinery.
Inventors
- 👤 Hideo Motoki
- 👤 Shigehiro Nagaretani
- 👤 Eiichi Tomita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:08
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
162 words
A composition capable of being foamed upon mixing with water and capable of being cured into a heat insulating material at normal temperatures comprising A, B, C and D, wherein A is a water-soluble alkali silicate having a mol ratio SiO 2 /R I 2 O, with R I representing alkali metal, of 1.5-4.0; B is alumina cement; C is a metallic or semi-metallic elemental foaming agent belonging to periods IB, IIA, IIB, IIIA, IIIB, IVA, IVB, VA, VB, VIB, VIIB and VIII in the periodic table, an alloy or an intermetallic compound of the said metals; and D is foam stabilizing agent selected from the consisting of silica gel, zeolite, artificial zeolite, carbon black, active carbon, alumina gel, talc, mica, animal protein and dimethyl silicone derivatives; and the solid portion of the ingredient B comprises 100-700 weight parts; the ingredient C comprises 0.5-35 weight parts and the ingredient D comprises 0.1-50 weight parts all based on 100 weight parts of A.
Claim 2
Dependent Claim
162 words
A composition capable of being foamed upon mixing with water and capable of being cured into a heat insulating material at normal temperatures comprising A, B, C and D, wherein A is a water-soluble alkali silicate having a mol ratio SiO 2 /R I 2 O, with R I representing alkali metal, of 1.5-4.0; B is alumina cement; C is a metallic or semi-metallic elemental foaming agent belonging to periods IB, IIA, IIB, IIIA, IIIB, IVA, IVB, VA, VB, VIB, VIIB and VIII in the periodic table, an alloy or an intermetallic compound of the said metals; and D is foam stabilizing agent selected from the consisting of silica gel, zeolite, artificial zeolite, carbon black, active carbon, alumina gel, talc, mica, animal protein and dimethyl silicone derivatives; and the solid portion of the ingredient B comprises 100-700 weight parts; the ingredient C comprises 0.5-35 weight parts and the ingredient D comprises 0.1-50 weight parts all based on 100 weight parts of A.
Claim 3
Dependent Claim
29 words
The composition of claim 1, wherein the ingredient B includes portland cement in a ratio of under 20 to 100 weight parts by weight based on the alumina cement.
Claim 4
Dependent Claim
24 words
The composition of claim 1, wherein the ingredient A is in the form of an aqueous solution having a concentration of 20 to 60%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-22 | 1983-04-23 | 1983-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-22 | 1987-04-23 | 1987-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-22 | 1991-04-23 | 1991-10-23 | $7700.00 | Window Closed / Lapsed |