Molded lip seal with polytetrafluoroethylene liner and method for making the same
Assignee: Garlock Inc
•
Filing: 1976-12-01
•
Granted: 1979-10-23
•
Expires: 1996-12-01
Abstract
Abstract A shaft seal (and method for making the same) of the type having an annular elastomeric body, a molded lip, and the molded lip having a liner of sintered polytetrafluoroethylene bonded thereto. The elastomer is molded simultaneously with the polytetrafluoroethylene liner being formed and bonded to the elastomer. The method for making the seal employs the same mold used to make common, molded lip elastomeric seals.
Inventors
- 👤 Dean R. Bainard
- 👤 Dennis N. Denton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:01
CPC Classifications
B; B29; B29D; B29D99/00; B29D99/0053; B29C; B29C43/00; B29C43/02; B29C43/027; B29C43/18; F; F16; F16J; F16J15/00; F16J15/16; F16J15/32; F16J15/328; F16J15/3284; B29K; B29K2021/00; B29L; B29L2031/00; B29L2031/26; Y; Y10; Y10S; Y10S277/00; Y10S277/924; Y10S425/00; Y10S425/047; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
83 words
A method for making a shaft seal of the type including an annular elastomeric body, a molded lip and the molded lip having a liner of sintered polytetrafluoroethylene, comprising: (a) molding, at a temperature in the range of from about 300° to 450° F., an annular elastomeric body; and (b) simultaneously with said molding step, forming a ring of sintered polytetrafluoroethylene into a liner on said elastomeric body in the shape of a molded lip and bonding said liner to said elastomeric body.
Claim 2
Independent Claim
83 words
A method for making a shaft seal of the type including an annular elastomeric body, a molded lip and the molded lip having a liner of sintered polytetrafluoroethylene, comprising: (a) molding, at a temperature in the range of from about 300° to 450° F., an annular elastomeric body; and (b) simultaneously with said molding step, forming a ring of sintered polytetrafluoroethylene into a liner on said elastomeric body in the shape of a molded lip and bonding said liner to said elastomeric body.
Claim 3
Dependent Claim
28 words
The method according to claim 1 wherein said simultaneously forming step comprises lining said body for at least 0.060 inch on each axial side of said molded lip.
Claim 4
Dependent Claim
23 words
The method according to claim 1 wherein said simultaneously forming step includes forming hydrodynamic pumping elements on a shaft-engaging surface of said liner.
Claim 5
Dependent Claim
73 words
The method according to claim 1 wherein said simultaneously forming step comprises placing said ring of sintered polytetrafluoroethylene in a standard mold cavity having a molded-lip groove of the type for use in making an elastomeric, molded lip seal, and forcing elastomeric material into said mold cavity from behind said ring to force said ring against and into said molded-lip groove to form said ring as a polytetrafluoroethylene liner with a molded lip.
Claim 6
Dependent Claim
39 words
The method according to claim 4 wherein said placing step comprises placing said ring in said mold cavity at a location spaced away from said molded-lip groove such that said ring is out of contact with said molded-lip groove.
Claim 7
Dependent Claim
26 words
The method according to claim 4 wherein said placing step comprises placing a polytetrafluoroethylene ring having a thickness of about 0.010-0.050 inch in said mold cavity.
Claim 8
Dependent Claim
47 words
The method according to claim 4 wherein said placing step includes placing said ring in said cavity such that at least a portion thereof extends radially out into the cavity a sufficient distance such that said portion will extend past said molded-lip groove during said forcing step.
Claim 9
Dependent Claim
28 words
The method according to claim 7 wherein said simultaneously forming step comprises lining said body for at least 0.060 inch on each axial side of said molded lip.
Claim 10
Dependent Claim
23 words
The method according to claim 8 wherein said simultaneously forming step includes forming hydrodynamic pumping elements on a shaft-engaging surface of said liner.
Claim 11
Dependent Claim
26 words
The method according to claim 9 wherein said placing step comprises placing a polytetrafluoroethylene ring having a thickness of about 0.010-0.050 inch in said mold cavity.
Claim 12
Dependent Claim
39 words
The method according to claim 10 wherein said placing step comprises placing said ring in said mold cavity at a location spaced away from said molded-lip groove such that said ring is out of contact with said molded-lip groove.
Claim 13
Dependent Claim
36 words
The method according to claim 1 wherein said molding step comprises compression molding said elastomeric body from a pre-form of elastomer, and said forming step comprises forming a flat ring of sintered polytetrafluoroethelene into said liner.
Claim 14
Independent Claim
157 words
A method for making a shaft seal of the type including an annular elastomeric body, a molded lip, and the molded lip having a liner of sintered polytetrafluoroethylene, comprising the steps of: (a) compression molding, at a temperature in the range of from about 300° to 450° F., said elastomeric body from an elastomer pre-form while simultaneously forming said liner and bonding said formed liner to said elastomeric body, and (b) said forming step comprising: (1) placing, beneath said pre-form, a ring of sintered polytetrafluoroethylene in a mold cavity having a molded-lip groove with at least a portion of said ring extending radially out into the seal cavity a sufficient distance such that it will extend past said groove when formed in the direction of said groove, and (2) closing the mold to cause said elastomer to flow and force said ring against and into said groove, forming said ring as a liner with a molded lip.
Claim 15
Independent Claim
157 words
A method for making a shaft seal of the type including an annular elastomeric body, a molded lip, and the molded lip having a liner of sintered polytetrafluoroethylene, comprising the steps of: (a) compression molding, at a temperature in the range of from about 300° to 450° F., said elastomeric body from an elastomer pre-form while simultaneously forming said liner and bonding said formed liner to said elastomeric body, and (b) said forming step comprising: (1) placing, beneath said pre-form, a ring of sintered polytetrafluoroethylene in a mold cavity having a molded-lip groove with at least a portion of said ring extending radially out into the seal cavity a sufficient distance such that it will extend past said groove when formed in the direction of said groove, and (2) closing the mold to cause said elastomer to flow and force said ring against and into said groove, forming said ring as a liner with a molded lip.
Claim 16
Dependent Claim
39 words
The method according to claim 13 wherein said placing step comprises placing said ring in said mold cavity at a location spaced away from said molded-lip groove such that said ring is out of contact with said molded-lip groove.
References Cited (Backward Citations)
US2804324A
Cited
US3276115A
Cited
US3462333A
Cited
US3493645A
Cited
US3972975A
Cited
US3806398A
Cited
US3973781A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-22 | 1983-04-23 | 1983-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-22 | 1987-04-23 | 1987-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-22 | 1991-04-23 | 1991-10-23 | $7700.00 | Window Closed / Lapsed |