Method for preparing active cathodes for electrochemical processes
Assignee: Norsk Hydro ASA
•
Filing: 1978-02-24
•
Granted: 1979-10-16
•
Expires: 1998-02-24
Abstract
Abstract Improved active cathodes, prepared by cleaning and etching with nitric acid and activated by a galvanic coating in a bath containing a nickel salt and sulphur liberating component, are provided. The improvement resides in controlled etching and activation conditions.
Inventors
- 👤 Hakon Harang
- 👤 Karl Widding
- 👤 Knut A. Andreassen
- 👤 Johan B. Holte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:34
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/12; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
128 words
In a method for the preparation of active cathodes suitable for electrolysis for water wherein the cathode substrate is cleaned and etched in nitric acid and is then activated by galvanic coating in a bath containing a nickel salt and a sulphur liberating component, the improvement wherein: (a) the etching of the cathode is performed within 5-10 minutes in a nitric acid solution with a concentration of 10-25%; (b) the temperature is kept at 35°-45° C. during the etching; (c) the cathode is activated in a bath with 50-350 g/l nickel sulphate-hydrate, 10-200 g/l thiourea; and (d) the temperature is kept at 30°-60° C. and the pH is kept at 3-6, while the activation is performed during application of a cathodic current density of 0.3-6 A/dm 2 .
Claim 2
Dependent Claim
128 words
In a method for the preparation of active cathodes suitable for electrolysis for water wherein the cathode substrate is cleaned and etched in nitric acid and is then activated by galvanic coating in a bath containing a nickel salt and a sulphur liberating component, the improvement wherein: (a) the etching of the cathode is performed within 5-10 minutes in a nitric acid solution with a concentration of 10-25%; (b) the temperature is kept at 35°-45° C. during the etching; (c) the cathode is activated in a bath with 50-350 g/l nickel sulphate-hydrate, 10-200 g/l thiourea; and (d) the temperature is kept at 30°-60° C. and the pH is kept at 3-6, while the activation is performed during application of a cathodic current density of 0.3-6 A/dm 2 .
Claim 3
Dependent Claim
53 words
The method according to claim 1, wherein said improvement further comprises performing the activation of the cathode in a bath with 200-250 g/l nickel sulphate-hydrate, 50-150 g/l thiourea, pH of 4, temperature of 45°-50° C., and applying a cathodic current density of 2-3 A/dm 2 while the activation is performed for 1-2 hours.
Claim 4
Dependent Claim
53 words
The method according to claim 1, wherein said improvement further comprises performing the activation of the cathode in a bath having 60-100 g/l nickel sulphate-hydrate, 80-120 g/l thiourea, pH of 3.5-4, temperature of 40°-45° C., and applying a cathodic current density of 0.5-1.5 A/dm 2 while the activation is performed for 4-8 hours.
Claim 5
Independent Claim
35 words
The method according to claims 1, 2 or 3 wherein said improvement further comprises performing the etching of the cathode in a 15% nitric acid solution at 36°-39° C. for a period of 6-8 minutes.
Claim 6
Dependent Claim
19 words
The method according to claim 1 wherein the substrate is nickel or steel with or without a nickel coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-15 | 1983-04-16 | 1983-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-15 | 1987-04-16 | 1987-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-15 | 1991-04-16 | 1991-10-16 | $7700.00 | Window Closed / Lapsed |