US4170575A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Compound for patching voids in a semi-conductive component of insulated electric cable
Assignee: Vulkor Inc
•
Filing: 1977-08-24
•
Granted: 1979-10-09
•
Expires: 1997-08-24
Abstract
Abstract The mending of defective semiconductive components of insulated electrical cable, comprising filling and sealing voids or breaks within a body of semiconductive material with a curable semiconductive patching compound comprising the combination of chlorosulfonated polyethylene, conductive filler and lauroyl peroxide, and heating the patching compound to cure the same.
Inventors
- 👤 Sidney Rothenberg
- 👤 Joseph E. Vostovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:39
CPC Classifications
H; H01; H01B; H01B13/00; H01B13/30; H01B1/00; H01B1/20; H01B1/24
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
74 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electrical cable, consisting essentially of the combination of polymeric material, conductive filler material and lauroyl peroxide in amount of about 2 to about 8 parts by weight of the polymeric material, said polymeric material being composed of at least about 65% by weight of chlorosulfonated polyethylene and 0 to about 35% by weight of ethylene-propylene rubber.
Claim 2
Dependent Claim
74 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electrical cable, consisting essentially of the combination of polymeric material, conductive filler material and lauroyl peroxide in amount of about 2 to about 8 parts by weight of the polymeric material, said polymeric material being composed of at least about 65% by weight of chlorosulfonated polyethylene and 0 to about 35% by weight of ethylene-propylene rubber.
Claim 3
Dependent Claim
11 words
The cured product of the semiconductive polymeric compound of claim 1.
Claim 4
Dependent Claim
80 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electrical cable, comprising the combination of 100 parts by weight of polymeric material, about 15 to about 100 parts by weight of conductive carbon black filler, and about 2 to about 8 parts by weight of lauroyl peroxide, said polymeric material comprising at least about 75% by weight of chlorosulfonated polyethylene and about 0 to about 25% by weight of ethylene-propylene rubber.
Claim 5
Dependent Claim
80 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electrical cable, comprising the combination of 100 parts by weight of polymeric material, about 15 to about 100 parts by weight of conductive carbon black filler, and about 2 to about 8 parts by weight of lauroyl peroxide, said polymeric material comprising at least about 75% by weight of chlorosulfonated polyethylene and about 0 to about 25% by weight of ethylene-propylene rubber.
Claim 6
Dependent Claim
26 words
The curable semiconductive polymeric compound of claim 3, comprising up to about 5 parts by weight per 100 parts of curable polymeric material of a coagent.
Claim 7
Dependent Claim
11 words
The cured product of the semiconductive polymeric compound of claim 3.
Claim 8
Dependent Claim
68 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electric cable, comprising the combination of about 75 to about 90 parts by weight of chlorosulfonated polyethylene with about 10 to about 25 parts by weight of ethylene-propylene rubber, about 50 to 100 parts by weight of conductive carbon black filler, and about 5 parts by weight of lauroyl peroxide.
Claim 9
Dependent Claim
68 words
A curable semiconductive polymeric compound for patching voids in a body of a semiconductive component of an insulated electric cable, comprising the combination of about 75 to about 90 parts by weight of chlorosulfonated polyethylene with about 10 to about 25 parts by weight of ethylene-propylene rubber, about 50 to 100 parts by weight of conductive carbon black filler, and about 5 parts by weight of lauroyl peroxide.
Claim 10
Dependent Claim
33 words
The curable semiconductive polymeric compound of claim 6, comprising up to about 5 parts by weight per 100 parts by weight of curable polymeric material of a free radical crosslink cure enhancing coagent.
Claim 11
Dependent Claim
11 words
The cured product of the semiconductive polymeric compound of claim 6.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-08 | 1983-04-09 | 1983-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-08 | 1987-04-09 | 1987-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-08 | 1991-04-09 | 1991-10-09 | $7700.00 | Window Closed / Lapsed |