Process and composition for imparting anti-soil redeposition and soil release properties to polyester textile materials
Assignee: Milliken Research Corp
•
Filing: 1978-04-11
•
Granted: 1979-10-09
•
Expires: 1998-04-11
Abstract
Abstract An aqueous fabric treating composition for improving the particulate redeposition properties, as well as the soil release properties, of a polyester textile material during a laundering process is provided in which the aqueous fabric treating composition contains, as essential ingredients, from about 0.0001 to about 10 weight percent of a cellulose ether soil release agent and an effective amount of an anti-redeposition agent selected from the group consisting of citric acid and acidic acrylic copolymers containing from about 10 weight percent to about 90 weight percent of the acid constituent, such being calculated as acrylic acid. The effective amount of the anti-redeposition agent is that amount sufficient to provide a ratio of the anti-redeposition agent to the cellulose ether soil release agent of from about 1.5:1 to about 10:1. A method for improving the particulate redeposition properties of polyester textile materials during the laundering process, while providing desirable soil release properties to such materials, as well as the products so produced, is also provided.
Inventors
- 👤 Francis W. Marco
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:58
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/263; D06M13/00; D06M13/10; D06M13/184; D06M13/207; D06M15/01; D06M15/03; D06M15/05; D06M15/09
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
191 words
A method for improving the particulate redeposition properties of a polyester textile material while imparting soil release properties to same which comprises: (a) forming an aqueous admixture consisting essentially of from about 0.0001 to about 10 weight percent of a cellulose ether soil release agent and an effective amount of an anti-redeposition agent selected from the group consisting of citric acid and acidic acrylic copolymers containing from about 10 weight percent to about 90 weight percent of the acid constituent, such being calculated as acrylic acid, said effective amount being that amount to provide a ratio of the anti-redeposition agent to the cellulose ether soil release agent of from about 1.5:1 to about 50:1; (b) applying said aqueous admixture to the polyester textile material in an amount sufficient to substantially wet the polyester textile material and provide at least about 0.0001 weight percent of said hydroxy ether cellulose soil release agent on the textile material and at least about 0.001 weight percent of said anti-redeposition agent on the textile material; (c) drying the wetted textile material to remove substantially all the water therefrom; and (d) recovering a resulting treated textile material.
Claim 2
Independent Claim
191 words
A method for improving the particulate redeposition properties of a polyester textile material while imparting soil release properties to same which comprises: (a) forming an aqueous admixture consisting essentially of from about 0.0001 to about 10 weight percent of a cellulose ether soil release agent and an effective amount of an anti-redeposition agent selected from the group consisting of citric acid and acidic acrylic copolymers containing from about 10 weight percent to about 90 weight percent of the acid constituent, such being calculated as acrylic acid, said effective amount being that amount to provide a ratio of the anti-redeposition agent to the cellulose ether soil release agent of from about 1.5:1 to about 50:1; (b) applying said aqueous admixture to the polyester textile material in an amount sufficient to substantially wet the polyester textile material and provide at least about 0.0001 weight percent of said hydroxy ether cellulose soil release agent on the textile material and at least about 0.001 weight percent of said anti-redeposition agent on the textile material; (c) drying the wetted textile material to remove substantially all the water therefrom; and (d) recovering a resulting treated textile material.
Claim 3
Dependent Claim
38 words
The method for improving the particulate redeposition properties of a polyester textile material according to claim 1 wherein the ratio of the anti-redeposition agent to the cellulose ether soil release agent is from about 2:1 to about 5:1.
Claim 4
Dependent Claim
53 words
The method for improving the particulate redeposition properties of a polyester textile material according to claim 1 wherein said acidic acrylic copolymer anti-redeposition agent is further defined as a copolymer of ethyl acrylate and methacrylic acid and the ethyl acrylate and methacrylic acid constituents are present in a ratio of 30:70 percent respectively.
Claim 5
Dependent Claim
23 words
The method for improving the particulate redeposition properties of polyester textile material according to claim 1 wherein said anti-redeposition agent is citric acid.
Claim 6
Dependent Claim
111 words
An aqueous fabric treating composition for improving the soil release properties of a polyester textile material while also improving the particulate anti-redeposition properties of polyester fabrics which consists essentially of water, from about 0.0001 to about 10 weight percent of a cellulose ether soil release agent and an effective amount of a particulate anti-redeposition agent selected from the group consisting of citric acid and acidic acrylic copolymers containing from about 10 weight percent to about 90 weight percent of the acidic constituent, said effective amount being that amount to provide a ratio of the particulate anti-redeposition agent to the cellulose ether soil release agent of from about 1.5:1 to about 50:1.
Claim 7
Dependent Claim
111 words
An aqueous fabric treating composition for improving the soil release properties of a polyester textile material while also improving the particulate anti-redeposition properties of polyester fabrics which consists essentially of water, from about 0.0001 to about 10 weight percent of a cellulose ether soil release agent and an effective amount of a particulate anti-redeposition agent selected from the group consisting of citric acid and acidic acrylic copolymers containing from about 10 weight percent to about 90 weight percent of the acidic constituent, said effective amount being that amount to provide a ratio of the particulate anti-redeposition agent to the cellulose ether soil release agent of from about 1.5:1 to about 50:1.
Claim 8
Dependent Claim
37 words
The aqueous fabric treating composition according to claim 5 wherein said cellulose ether soil release agent is selected from the group consisting of methyl cellulose, hydroxy butyl methyl cellulose, hydroxy propyl methyl cellulose and hydroxy propyl cellulose.
Claim 9
Dependent Claim
30 words
The aqueous fabric treating composition according to claim 6 wherein the ratio of the anti-redeposition agent to the cellulose ether soil release agent is from about 2:1 to about 5:1.
Claim 10
Dependent Claim
45 words
The aqueous fabric treating composition according to claim 7 wherein said acidic acrylic copolymer anti-redeposition agent is further defined as a copolymer of ethyl acrylate and methacrylic acid and the ethyl acrylate and methacrylic acid constituents are present in a ratio of 30:70 percent respectively.
Claim 11
Dependent Claim
16 words
The aqueous fabric treating composition according to claim 7 wherein said anti-redeposition agent is citric acid.
References Cited (Backward Citations)
US2979373A
Cited
US2876140A
Cited
US3523088A
Cited
US3782898A
Cited
US3912681A
Cited
US3904359A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-08 | 1983-04-09 | 1983-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-08 | 1987-04-09 | 1987-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-08 | 1991-04-09 | 1991-10-09 | $7700.00 | Window Closed / Lapsed |