Method of manufacture of a soft-X-ray mask
Assignee: Massachusetts Institute of Technology
•
Filing: 1977-05-26
•
Granted: 1979-10-09
•
Expires: 1997-05-26
Abstract
Abstract A process for fabricating polyimide membrane x-ray lithography masks is described. Thin membrane of polyimide is formed by spinning polyamic acid on a glass substrate and polymerizing in situ. The glass substrate acts as a holder and efficient heat sink during formation of gold absorber patterns on top of the polyimide. A support ring is then bonded to the polyimide, and the glass etched in dilute HF. Optically smooth polyimide membranes with thicknesses from 0.5 to 5 μm are readily achieved. The method and resulting product is not limited to the above materials or to masks.
Inventors
- 👤 Dale C. Flanders
- 👤 Henry I. Smith
- 👤 Muriel A. Dalomba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 04:14
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/22
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
158 words
A method of making a soft-x-ray mask of a composite sheet of x-ray transmissive plastic and another x-ray opaque patterned material comprising: applying said plastic in liquid form to a substrate, hardening said plastic to form an optically smooth polymer film of plastic whose thickness and composition is substantially transparent to soft-x-rays and which has a mechanical bond to said substrate, depositing photolithographically patternable soft x-ray opaque material on said hardened plastic to form a mechanical bond therewith and hence a composite material of said plastic and opaque material, patterning a region of said deposited material to form a mask of said x-ray opaque material on said plastic, adhesively attaching a mechanical support to said composite material to enclose said patterned region within said support, dissolving the entire said substrate to leave only the composite material as attached to said support, removing that portion of said composite material external to said mechanical support to provide a supported mask.
Claim 2
Independent Claim
158 words
A method of making a soft-x-ray mask of a composite sheet of x-ray transmissive plastic and another x-ray opaque patterned material comprising: applying said plastic in liquid form to a substrate, hardening said plastic to form an optically smooth polymer film of plastic whose thickness and composition is substantially transparent to soft-x-rays and which has a mechanical bond to said substrate, depositing photolithographically patternable soft x-ray opaque material on said hardened plastic to form a mechanical bond therewith and hence a composite material of said plastic and opaque material, patterning a region of said deposited material to form a mask of said x-ray opaque material on said plastic, adhesively attaching a mechanical support to said composite material to enclose said patterned region within said support, dissolving the entire said substrate to leave only the composite material as attached to said support, removing that portion of said composite material external to said mechanical support to provide a supported mask.
Claim 3
Dependent Claim
63 words
The method of claim 1 wherein: said liquid form of plastic is polyimide plastic precursor, said hardening comprises heating said precursor to form a polyimide film, said substrate is a glass, said depositing of material on said polyimide film comprises vaporizing a metal and depositing the vapor on the film, said dissolving of the substrate comprises etching away said glass in hydrofluoric acid.
Claim 4
Dependent Claim
34 words
The method of claim 2 wherein: said applying of the polyimide plastic precursor on the glass substrate comprises spinning said precursor and substrate to form a layer of liquid precursor of substantially uniform thickness.
Claim 5
Dependent Claim
25 words
The method of claim 2 comprising in addition: forming a pattern in said deposited metal by ion beam etching away selected portions of the metal.
Claim 6
Dependent Claim
49 words
The method of claim 2 wherein: said mechanical support forms a liquid barrier to prevent said hydrofluoric acid from entering the region within said support, filling said support with a liquid prior to the etching step to prevent said acid from passing through said composite material during the etching.
Claim 7
Dependent Claim
16 words
The method of claim 2 wherein said polyimide film has a thickness between 0.05μ and 3μ.
Claim 8
Dependent Claim
64 words
The method of claim 1 comprising in addition: adhesively attaching a mask holder to said composite material to contain said pattern within said mask holder, said attachment being made before said substrate is etched away, and removing said attached mechanical support after said substrate is totally etched away to leave said composite material within and attached only to and supported by said mask holder.
Claim 9
Dependent Claim
69 words
The method of claim 1 comprising in addition: adhesively attaching a mask holder to the plastic nonpatterned side of said composite material to contain said pattern within said mask holder, said attachment being made after said substrate is etched away, and thereafter removing said attached mechanical support after said substrate is totally etched away to leave said composite material within and attached only to and supported by mask holder.
Claim 10
Dependent Claim
93 words
The method of claim 1 wherein: said mechanical support comprises a first and second mechanical support each adhesively attached to said composite material, said second mechanical support forming a liquid tight enclosure around said first mechanical support, said first mechanical support being of a material which would be dissolved at the time that said substrate is being dissolved in the absence of being enclosed by said second mechanical support, and wherein said removing of the composite material comprises removing said second mechanical support and said composite material external to said first mechanical support.
Claim 11
Dependent Claim
40 words
The method of claim 1 wherein said patterning of said x-ray opaque material includes removing said opaque material from the region of attachment of said mechanical support to result in said attachment of said mechanical support being to said plastic.
Claim 12
Independent Claim
193 words
The method of making a soft x-ray mask of composite sheet of x-ray transmissive plastic and an x-ray opaque material comprising: applying said plastic in liquid form to a substrate, hardening said plastic to form an optically smooth polymer film of plastic of thickness and composition substantially transparent to soft-x-rays, said plastic having a mechanical bond to said substrate, depositing a photolithographically patternable soft-x-ray opaque material on said hardened plastic to form a mechanical bond therewith and hence a composite material of said plastic and opaque material, patterning a region of said deposited material to form a mask of said x-ray opaque material on said plastic, adhesively attaching a mechanical support to said composite material to enclose said patterned region within said support, selectively dissolving said substrate to leave only a portion of said substrate in the form of a ring attached to said plastic to support said composite material, said supporting substrate enclosing said patterned region within the region supported by said mechanical support, removing said composite material and mechanical support external to said substrate support ring to leave said substrate support ring attached to said film to provide a supported mask.
Claim 13
Independent Claim
193 words
The method of making a soft x-ray mask of composite sheet of x-ray transmissive plastic and an x-ray opaque material comprising: applying said plastic in liquid form to a substrate, hardening said plastic to form an optically smooth polymer film of plastic of thickness and composition substantially transparent to soft-x-rays, said plastic having a mechanical bond to said substrate, depositing a photolithographically patternable soft-x-ray opaque material on said hardened plastic to form a mechanical bond therewith and hence a composite material of said plastic and opaque material, patterning a region of said deposited material to form a mask of said x-ray opaque material on said plastic, adhesively attaching a mechanical support to said composite material to enclose said patterned region within said support, selectively dissolving said substrate to leave only a portion of said substrate in the form of a ring attached to said plastic to support said composite material, said supporting substrate enclosing said patterned region within the region supported by said mechanical support, removing said composite material and mechanical support external to said substrate support ring to leave said substrate support ring attached to said film to provide a supported mask.
Claim 14
Dependent Claim
63 words
The method of claim 11 wherein: said liquid form of plastic is polyimide plastic precursor, said hardening comprises heating said precursor to form a polyimide film, said substrate is a glass, said depositing of material on said polyimide film comprises vaporizing a metal and depositing the vapor on the film, said dissolving of the substrate comprises etching away said glass in hydrofluoric acid.
Claim 15
Dependent Claim
16 words
The method of claim 12 wherein said polyimide film has a thickness between 0.05μ and 3μ.
Claim 16
Dependent Claim
34 words
The method of claim 11 wherein: said applying of the polyimide plastic precursor on the glass substrate comprises spinning said precursor and substrate to form a layer of liquid precursor of substantially uniform thickness.
Claim 17
Dependent Claim
25 words
The method of claim 11 comprising in addition: forming a pattern in said deposited metal by ion beam etching away selected portions of the metal.
Claim 18
Dependent Claim
49 words
The method of claim 11 wherein: said mechanical support forms a liquid barrier to prevent said hydrofluoric acid from entering the region within said support, filling said support with a liquid prior to the etching step to prevent said acid from passing through said composite material during the etching.
Claim 19
Dependent Claim
40 words
The method of claim 11 wherein said patterning of said x-ray opaque material includes removing said opaque material from the region of attachment of said mechanical support to result in said attachment of said mechanical support being to said plastic.
References Cited (Backward Citations)
US3179634A
Cited
US3607997A
Cited
US3767494A
Cited
US3742230A
Cited
US3930914A
Cited
US3873824A
Cited
US3892973A
Cited
US4037111A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-08 | 1983-04-09 | 1983-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-08 | 1987-04-09 | 1987-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-08 | 1991-04-09 | 1991-10-09 | $7700.00 | Window Closed / Lapsed |