Low gloss finishes by gradient intensity cure
Assignee: Lord Corp
•
Filing: 1978-06-26
•
Granted: 1979-09-25
•
Expires: 1998-06-26
Abstract
Abstract The gloss of energy-curable coating and ink compositions is reduced by exposing such compositions to actinic radiation in an oxygen-rich atmosphere at differential intensity levels. The intensities are selected to effect at a first intensity range substantially complete cure of the composition except for the surface, with final cure of the surface being effected subsequently at a different and higher intensity range. Gradient Intensity Cure can be employed with substantially any composition which is curable by free radical-induced addition polymerization using a photosensitizer-photoinitiator photocatalyst system.
Inventors
- 👤 John R. McDowell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:14
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/06; B41; B41M; B41M7/00; B41M7/0045; B41M7/0081
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
210 words
A method for providing a surface having a reduced gloss finish comprising subjecting a substantially inert solvent-free, essentially 100% reactive composition comprising at least one reactive oligomer; at least one reactive monomer diluent; silica and an effective amount of a photo catalyst composition comprising (1) an effective amount of at least one photosensitizer compound which promotes free radical polymerization through bimolecular photochemical reactions of the energy donor type or hydrogen abstraction type or by formation of a donor-acceptor complex with monomers or additives leading to ionic or radical species and (2) an effective amount of at least one photoinitiator compound which promotes free radical polymerization by generating reactive specie by way of unimolecular scission resulting from photoexcitation to ultraviolet irradiation in an oxygen-containing atmosphere at a first intensity level and a first exposure time until such composition is substantially fully cured except for its surface and subsequently subjecting such composition to ultraviolet irradiation in an oxygen-containing atmosphere at at least one other intensity level and at at least one other exposure time until the surface of such composition is substantially fully cured, said other intensity level being higher than said first intensity level, and said other exposure time being less than, equal to or more than said first exposure time.
Claim 2
Independent Claim
210 words
A method for providing a surface having a reduced gloss finish comprising subjecting a substantially inert solvent-free, essentially 100% reactive composition comprising at least one reactive oligomer; at least one reactive monomer diluent; silica and an effective amount of a photo catalyst composition comprising (1) an effective amount of at least one photosensitizer compound which promotes free radical polymerization through bimolecular photochemical reactions of the energy donor type or hydrogen abstraction type or by formation of a donor-acceptor complex with monomers or additives leading to ionic or radical species and (2) an effective amount of at least one photoinitiator compound which promotes free radical polymerization by generating reactive specie by way of unimolecular scission resulting from photoexcitation to ultraviolet irradiation in an oxygen-containing atmosphere at a first intensity level and a first exposure time until such composition is substantially fully cured except for its surface and subsequently subjecting such composition to ultraviolet irradiation in an oxygen-containing atmosphere at at least one other intensity level and at at least one other exposure time until the surface of such composition is substantially fully cured, said other intensity level being higher than said first intensity level, and said other exposure time being less than, equal to or more than said first exposure time.
Claim 3
Dependent Claim
29 words
A method according to claim 1 wherein said higher intensity level has an average value at least 50 percent higher than the average value of said first intensity level.
Claim 4
Dependent Claim
18 words
A method according to claim 1 wherein said atmosphere contains at least 5,000 parts per million of oxygen.
Claim 5
Dependent Claim
11 words
A method according to claim 1 wherein said atmosphere is air.
Claim 6
Dependent Claim
103 words
A method according to claim 1 wherein the amount of said photoinitiator compound is in the range from 0.01 to 10 parts by weight, per 100 parts by weight of said reactive oligomer and said reactive monomer diluent, and the amount of said photosensitizer is in a range which is ineffective to generate sufficient free radicals from excitation at said first intensity level to overcome oxygen inhibition at the surface of said composition but is effective to generate sufficient free radicals from excitation at said higher intensity level to overcome oxygen inhibition at the surface and fully polymerize the surface of such composition.
Claim 7
Dependent Claim
18 words
A method according to claim 5 wherein said photosensitizer is benzophenone and said photoinitiator is benzoin isobutyl ether.
Claim 8
Dependent Claim
16 words
A method according to claim 5 wherein said photosensitizer is benzophenone and said photoinitiator is diethoxyacetophenone.
Claim 9
Dependent Claim
122 words
A coating composition comprising (a) at least one unsaturated oligomer, (b) a reactive diluent which is copolymerizable with said oligomer; (c) from 1 to 12 parts by weight, per 100 parts by combined weight of said oligomer and said diluent, silica; and (d) an effective amount of a photocatalyst system comprising (1) an effective amount of at least one photosensitizer which promotes free radical photopolymerization through bimolecular photochemical reactions of the energy donor type or hydrogen abstraction type, or through formation of a donor-acceptor complex with monomers or additives leading to ionic or radical specie; and (2), an effective amount of at least one photoinitiator which promotes free radical photopolymerization by generating radical specie by way of linimolecular homolysis resulting from photoexcitation.
Claim 10
Dependent Claim
122 words
A coating composition comprising (a) at least one unsaturated oligomer, (b) a reactive diluent which is copolymerizable with said oligomer; (c) from 1 to 12 parts by weight, per 100 parts by combined weight of said oligomer and said diluent, silica; and (d) an effective amount of a photocatalyst system comprising (1) an effective amount of at least one photosensitizer which promotes free radical photopolymerization through bimolecular photochemical reactions of the energy donor type or hydrogen abstraction type, or through formation of a donor-acceptor complex with monomers or additives leading to ionic or radical specie; and (2), an effective amount of at least one photoinitiator which promotes free radical photopolymerization by generating radical specie by way of linimolecular homolysis resulting from photoexcitation.
Claim 11
Dependent Claim
121 words
A coating composition according to claim 8 wherein the amount of said photocatalyst system is effective, when exposed to ultraviolet irradiation having a wavelength of 200 to 400 nanometers in an oxygen-containing atmosphere at a first intensity level I 1 , to generate an amount of free radicals from excitation of such photosensitizer and such photoinitiator sufficient to cure all but the surface of such composition at said first intensity level, and, when exposed to such irradiation in an oxygen-containing environment at a second intensity level I 2 , said level I 2 being higher than said level I 1 , is effective to generate sufficient free radicals from excitation of said photosensitizer to substantially cure the surface of such composition.
Claim 12
Dependent Claim
38 words
A coating composition according to claim 9 wherein the amount of said photosensitizer is in the range from 0.01 to 10 parts by weight, per 100 parts by weight of said reactive oligomer and said reactive monomer diluent.
Claim 13
Dependent Claim
19 words
A coating composition according to claim 10 wherein said photosensitizer is benzophenone and said photoinitiator is benzoin isobutyl ether.
Claim 14
Dependent Claim
17 words
A coating composition according to claim 10 wherein said photosensitizer is benzophenone and said photoinitiator is diethoxyacetophenone.
References Cited (Backward Citations)
US3759807A
Cited
US3850675A
Cited
US3953622A
Cited
US3759808A
Cited
US4020193A
Cited
US3918393A
Cited
US3783004A
Cited
US3943046A
Cited
US4017652A
Cited
US4017652B1
Cited
US4048036A
Cited
US3992275A
Cited
US3966572A
Cited
US4075366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-24 | 1983-03-26 | 1983-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-24 | 1987-03-26 | 1987-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-24 | 1991-03-26 | 1991-09-25 | $7700.00 | Window Closed / Lapsed |