Transfer sheet with toner-receiving layer of thermoplastic and thermosetting polymers
Assignee: Kyocera Mita Industrial Co Ltd
•
Filing: 1977-09-09
•
Granted: 1979-09-18
•
Expires: 1997-09-09
Abstract
Abstract A transfer sheet for electrostatically transferring thereon an electrically conductive or electrically semi-conductive toner in electrostatic photography or electrostatic printing, which comprises a substrate and a toner-receiving layer formed on at least one surface of the substrate, which toner-receiving layer contains a composition comprising (A) a thermoplastic acrylic polymer having a carboxyl group content of 2 to 30% by weight and (B) a thermosetting resin reactive with the acrylic polymer (A), and a process for preparing this transfer sheet by using an aqueous coating composition are disclosed. In this transfer sheet, the electric resistance can be maintained at a high level even under high humidity conditions, and a toner image can be transferred on this transfer sheet at a high transfer efficiency.
Inventors
- 👤 Mamoru Kato
- 👤 Susumu Yamaura
- 👤 Yasutoki Kamezawa
- 👤 Tatsuo Aizawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:14
CPC Classifications
G; G03; G03G; G03G7/00; G03G7/0006; G03G7/002; G03G7/0026; G03G7/0046; G03G13/00; G03G13/14; G03G13/16; G03G7/004; Y; Y10; Y10S; Y10S428/00; Y10S428/914; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522; Y10T428/31652; Y10T428/31667; Y10T428/31678; Y10T428/31692; Y10T428/31699; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31906; Y10T428/31909; Y10T428/31913; Y10T428/31928
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
116 words
A transfer sheet for electrostatically transferring thereon an electrically conductive or electrically semi-conductive toner in electrostatic photography or electrostatic printing, which comprises a substrate and a toner-receiving layer formed on at least one surface of said substrate, said toner-receiving layer containing a composition comprising (A) a thermoplastic acrylic polymer having a carboxyl group content of 2 to 30% by weight and (B) a thermosetting resin reactive with said acrylic polymer (A), said thermosetting resin (B) being a glycidyl ether of a polyalkylene polyol having an epoxy equivalent of 100 to 400, said thermoplastic acrylic resin (A) and said thermosetting resin (B) being present at an (A)/(B) weight ratio ranging from 100/5 to 100/100 based on solids.
Claim 2
Dependent Claim
116 words
A transfer sheet for electrostatically transferring thereon an electrically conductive or electrically semi-conductive toner in electrostatic photography or electrostatic printing, which comprises a substrate and a toner-receiving layer formed on at least one surface of said substrate, said toner-receiving layer containing a composition comprising (A) a thermoplastic acrylic polymer having a carboxyl group content of 2 to 30% by weight and (B) a thermosetting resin reactive with said acrylic polymer (A), said thermosetting resin (B) being a glycidyl ether of a polyalkylene polyol having an epoxy equivalent of 100 to 400, said thermoplastic acrylic resin (A) and said thermosetting resin (B) being present at an (A)/(B) weight ratio ranging from 100/5 to 100/100 based on solids.
Claim 3
Dependent Claim
49 words
A transfer sheet as set forth in claim 1 wherein said thermoplastic acrylic polymer (A) is a copolymer composed of 4 to 60% by weight of an ethylenically unsaturated carboxylic acid and 40 to 96% by weight of an ethylenically unsaturated monomer other than said ethylenically unsaturated carboxylic acid.
Claim 4
Dependent Claim
38 words
A transfer sheet as set forth in claim 1 wherein said ethylenically unsaturated monomer other than said ethylenically unsaturated carboxylic acid is a member selected from the group consisting of styrene, acrylic acid esters and methacrylic acid esters.
Claim 5
Dependent Claim
90 words
A transfer sheet as set forth in claim 1 wherein said thermoplastic acrylic polymer (A) is a copolymer composed of (a) 4 to 60% by weight of units represented by the following formula: ##STR7## wherein R 1 stands for a hydrogen atom or a lower alkyl group having up to 4 carbon atoms, and (b) 40 to 96% by weight of units represented by the following formula: ##STR8## wherein R 1 is as defined above and R 2 stand for a lower alkyl group having up to 4 carbon atoms.
Claim 6
Dependent Claim
37 words
A transfer sheet as set forth in claim 4 wherein said units (b) are composed of 1 part by weight of methacrylic acid ester units and 0.02 to 0.6 part by weight of acrylic acid ester units.
Claim 7
Dependent Claim
119 words
A transfer sheet as set forth in claim 1 wherein said thermoplastic acrylic polymer (A) is a copolymer composed of (a) 4 to 60% by weight of units represented by the following formula: ##STR9## wherein R 1 stands for a hydrogen atom or a lower alkyl group having up to 4 carbon atoms, (b) 10 to 75% by weight of units represented by the following formula: ##STR10## wherein R 1 is as defined above, R 2 stands for a lower alkyl group having up to 4 carbon atoms, and m is 0 or 1, and (c) 0 to 86% by weight of units represented by the following formula: ##STR11## wherein R 1 and R 2 are as defined above.
Claim 8
Dependent Claim
43 words
A transfer sheet as set forth in claim 1 wherein said composition comprises finely divided silica prepared according to the dry method in an amount of 10 to 100 parts by weight per 100 parts by weight of said thermoplastic acrylic polymer (A).
Claim 9
Dependent Claim
38 words
A transfer sheet as set forth in claim 1 wherein said composition comprises rutile type titanium dioxide in an amount of 10 to 500 parts by weight per 100 parts by weight of said thermoplastic acrylic polymer (A).
Claim 10
Dependent Claim
16 words
A transfer sheet as set forth in claim 1 wherein the substrate is a paper substrate.
Claim 11
Dependent Claim
29 words
A transfer sheet as set forth in claim 1 wherein the toner-receiving layer is formed on the substrate in a coat amount of 2 to 20 g/m 2 .
Claim 12
Dependent Claim
83 words
A transfer sheet as set forth in claim 1 wherein the saturation voltage retain ratio under high humidity conditions (Rγ), which is defined by the following formula: Rγ=V.sub.100 /V.sub.40 wherein V 40 indicates the saturation voltage of the transfer sheet as measured at a temperature of 20° C. and a relative humidity of 40% and V 100 represents the saturation voltage of the transfer sheet as measured at a temperature of 40° C. and a relative humidity of 100%, is at least 0.7.
References Cited (Backward Citations)
US3697171A
Cited
US3993825A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-17 | 1983-03-19 | 1983-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-17 | 1987-03-19 | 1987-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-17 | 1991-03-19 | 1991-09-18 | $7700.00 | Window Closed / Lapsed |