High speed steels with phosphorus for improved cutting performance
Assignee: Latrobe Steel Co
•
Filing: 1978-02-28
•
Granted: 1979-09-18
•
Expires: 1998-02-28
Abstract
Abstract A new high speed steel with improved cutting life is provided consisting essentially of about 0.7 to 1.6% carbon, about 0.2 to 1.0% silicon, about 0.2 to 0.8% manganese, up to about 0.2% sulphur, about 0.5 to about 20% tungsten, about 0.5 to about 10% molybdenum, about 0.5 to 5% chromium, about 0.5 to about 6% vanadium, up to about 10% cobalt, more than 0.03% to about 0.20% phosphorus, the balance iron with residual impurities in ordinary amounts.
Inventors
- 👤 Rene Schlatter
- 👤 David P. Hughes
- 👤 James Stepanic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:08
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/12; C22C38/18; C22C38/24
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
99 words
A high phosphorous high speed steel with improved cutting life consisting essentially of about 0.7 to 1.6% carbon, about 0.2 to 1.0% silicon, about 0.2 to 0.8% manganese, up to about 0.2% sulphur, about 0.5 to about 20% tungsten, about 0.5 to about 10% molybdenum, about 0.5% to 5% chromium, about 0.5 to about 6% vanadium, up to about 10% cobalt, sufficient phosphorous in the range more than 0.03% to about 0.20% phosphorous, to provide improved cutting tool life as compared with a like alloy having less than 0.03% phosphorous, the balance iron with residual impurities in ordinary amounts.
Claim 2
Dependent Claim
99 words
A high phosphorous high speed steel with improved cutting life consisting essentially of about 0.7 to 1.6% carbon, about 0.2 to 1.0% silicon, about 0.2 to 0.8% manganese, up to about 0.2% sulphur, about 0.5 to about 20% tungsten, about 0.5 to about 10% molybdenum, about 0.5% to 5% chromium, about 0.5 to about 6% vanadium, up to about 10% cobalt, sufficient phosphorous in the range more than 0.03% to about 0.20% phosphorous, to provide improved cutting tool life as compared with a like alloy having less than 0.03% phosphorous, the balance iron with residual impurities in ordinary amounts.
Claim 3
Dependent Claim
13 words
A high speed steel according to claim 1 having 0.04 to 0.09% phosphorus.
Claim 4
Dependent Claim
34 words
A high speed steel according to claim 1 consisting essentially of 0.83% carbon, 8.3% molybdenum, 3.5% chromium, 1.9% tungsten, 1.0% vanadium and 0.103% phosphorus and the balance iron with residual impurities in ordinary amounts.
Claim 5
Dependent Claim
38 words
A high speed steel as claimed in claim 1 consisting essentially of 0.80% carbon, 6.0% tungsten, 4.0% chomium, 4.8% molybdenum, 1.8% vanadium, phosphorus between about 0.066% and 0.104% and the balance iron with residual impurities in ordinary amounts.
Claim 6
Dependent Claim
38 words
A high speed steel according to claim 1 consisting essentially of 0.96% carbon, about 7.8% molybdenum, about 4.2% chromium, about 0.7% tungsten, about 1.9% vanadium, about 0.066% phosphorus and the balance iron with residual impurities in ordinary amounts.
Claim 7
Dependent Claim
116 words
A high speed cutting tool made of an alloy consisting essentially by weight of about 0.7 to 1.6% carbon, about 0.2 to about 1.0% silicon, about 0.2 to about 0.8% manganese, up to about 0.2% sulphur, about 0.5 to about 20% tungsten, about 0.5 to about 10% molybdenum, about 0.5 to about 5% chromium, about 0.5 to about 6% vanadium, up to about 10% cobalt, sufficient phosphorous in the range more than about 0.03% to about 0.20% phosphorous to provide improved cutting tool life as compared with a like tool having less than 0.03% phosphorous and the balance iron with residual impurities in ordinary amounts, said tool being characterized by improved tool life and cutting performance.
Claim 8
Dependent Claim
116 words
A high speed cutting tool made of an alloy consisting essentially by weight of about 0.7 to 1.6% carbon, about 0.2 to about 1.0% silicon, about 0.2 to about 0.8% manganese, up to about 0.2% sulphur, about 0.5 to about 20% tungsten, about 0.5 to about 10% molybdenum, about 0.5 to about 5% chromium, about 0.5 to about 6% vanadium, up to about 10% cobalt, sufficient phosphorous in the range more than about 0.03% to about 0.20% phosphorous to provide improved cutting tool life as compared with a like tool having less than 0.03% phosphorous and the balance iron with residual impurities in ordinary amounts, said tool being characterized by improved tool life and cutting performance.
References Cited (Backward Citations)
US2983601A
Cited
US3113862A
Cited
US3259489A
Cited
US3295401A
Cited
JPS487180U
Cited
US3859081A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-09-17 | 1983-03-19 | 1983-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-09-17 | 1987-03-19 | 1987-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-09-17 | 1991-03-19 | 1991-09-18 | $7700.00 | Window Closed / Lapsed |