US4165877A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Molded golf balls exhibiting isometric compression
Assignee: Kidde Inc
•
Filing: 1977-08-25
•
Granted: 1979-08-28
•
Expires: 1997-08-25
Abstract
Abstract A golf ball comprising a substantially spherical homogeneous molded mass of elastomer highly cross-linked into a three dimensional network with long, flexible cross-links formed from a metal-containing cross-linkable monomer, said comonomer simultaneously functioning at least in part as a filler, said mass exhibiting substantially isometric compression across any diameter. Advantageously the elastomer comprises polybutadiene and said metal-containing cross-linkable monomer comprises zinc dimethacrylate present in about 15 to 60 parts per 100 parts by weight of the polybutadiene. The composition may additionally contain a small amount of zinc oxide. By proper selection of the shape and make up of the slugs from which the balls are molded or by particular techniques, e.g. laboratory sheeting mills, balls can be produced which have a maximum difference in compression across different diameters of about 5 units.
Inventors
- 👤 Richard Miller
- 👤 Murray H. Reich
- 👤 Emma Kuntz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:48
CPC Classifications
B; B29; B29D; B29D99/00; B29D99/0042; A; A63; A63B; A63B37/00; A63B37/0003; A63B37/0023; A63B37/0024; A63B37/005; A63B37/007; A63B37/0072; A63B37/0074; B29K; B29K2009/00; B29K2033/00; B29L; B29L2031/00; B29L2031/54
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
147 words
A golf ball comprising a substantially spherical homogeneous molded mass of cis-polybutadiene highly cross-linked into a three dimensional network with long, flexible cross-links formed from a metal-containing cross-linkable monomer comprising a polyvalent metal salt of an unsaturated acid present in about 0.046 to 0.41 equivalents per mole of cis-polybutadiene, whereby said comonomer simultaneously functions at least in part as a filler, said ball in addition to said filler-functioning cross-linking monomer containing up to about 30 parts of a further filler per 100 parts by weight of said cis-polybutadiene, said mass exhibiting substantially isometric compression across any diameter and having been produced by continuously extruding a cross-linkable elastomer through a die to form an extrudate, cutting said extrudate so as to produce approximately cylindrical slugs about 2.5 to 3.3 inches long and having substantially flat or convex top and bottom surfaces, and molding said slugs into golf balls.
Claim 2
Dependent Claim
147 words
A golf ball comprising a substantially spherical homogeneous molded mass of cis-polybutadiene highly cross-linked into a three dimensional network with long, flexible cross-links formed from a metal-containing cross-linkable monomer comprising a polyvalent metal salt of an unsaturated acid present in about 0.046 to 0.41 equivalents per mole of cis-polybutadiene, whereby said comonomer simultaneously functions at least in part as a filler, said ball in addition to said filler-functioning cross-linking monomer containing up to about 30 parts of a further filler per 100 parts by weight of said cis-polybutadiene, said mass exhibiting substantially isometric compression across any diameter and having been produced by continuously extruding a cross-linkable elastomer through a die to form an extrudate, cutting said extrudate so as to produce approximately cylindrical slugs about 2.5 to 3.3 inches long and having substantially flat or convex top and bottom surfaces, and molding said slugs into golf balls.
Claim 3
Dependent Claim
26 words
A golf ball according to claim 1, wherein said filler is present in about 10 to 20 parts per 100 parts by weight of said elastomer.
Claim 4
Dependent Claim
44 words
A golf ball according to claim 1, wherein said golf ball is a two piece ball including a molded cover over said molded mass, said molded mass containing about 20 to 30 parts of said filler per 100 parts by weight of said elastomer.
Claim 5
Dependent Claim
165 words
A golf ball according to claim 1, wherein said metal-containing cross-linkable monomer comprises a salt selected from the group consisting of (RCO 2 ) m .M, R(SO 3 ) m .M, R(SO 2 ) m .M, (RCO 2 ) p .MO, (rso 3 ) p .MO, R(SO 2 ) p .MO, (R 2 PO 2 ) m .M, (r 2 po 2 ) p .MO, (RPO 3 ) q .M, (RPO 3 ).M'0; ##STR3## wherein each R independently is a group having at least one polymerizable olefinic unsaturation. R' is a divalent group having a polymerizable olefinic usaturation, each R" independently is an alkyl, aryl, or aralkyl group, M is a metal ion having a valence, m, of from 1 to 5, M' is a metal ion having a valence of 4, M" is a metal ion having a valence of 1 or 2, p is m-2 when m is greater than 2, and q has the value m/2 when m is 2 or 4.
Claim 6
Dependent Claim
52 words
A golf ball according to claim 1, wherein said metal-containing cross-linkable monomer comprises a salt of at least one metal selected from the group consisting of zinc, magnesium and calcium, and at least one acid selected from the group consisting of methacrylic, acrylic, cinnamic, acotinic, crotonic, vinylacetic, itaconic, styrenesulfonic and benzoylacrylic acids.
Claim 7
Dependent Claim
30 words
A golf ball according to claim 1, wherein said metal-containing cross-linkable monomer comprises zinc dimethacrylate present in about 15 to 60 parts per 100 parts by weight of the polybutadiene.
Claim 8
Dependent Claim
38 words
A golf ball according to claim 6, wherein said golf ball is a unitary golf ball and said mass additionally contains up to about 20 parts by weight of zinc oxide per 100 parts by weight of polybutadiene.
Claim 9
Dependent Claim
58 words
A golf ball according to claim 6, wherein said golf ball is a two piece ball including a molded cover over said molded mass, said molded mass containing about 20 to 30 parts by weight of zinc oxide per 100 parts by weight of polybutadiene, and said cover comprising an ionic co-polymer about 0.1 to 0.2 inch thick.
Claim 10
Dependent Claim
20 words
A golf ball according to claim 6, having a maximum difference in compression across different diameters of about 5 units.
References Cited (Backward Citations)
US3454280A
Cited
US3940146A
Cited
US3974238A
Cited
US3819768A
Cited
US4056269A
Cited
US4068849A
Cited
US4065537A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-27 | 1983-02-26 | 1983-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-27 | 1987-02-26 | 1987-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-27 | 1991-02-26 | 1991-08-28 | $7700.00 | Window Closed / Lapsed |