Process for the manufacture of optical fibers with a radial refractive index
Assignee: Thales SA
•
Filing: 1977-10-14
•
Granted: 1979-08-21
•
Expires: 1997-10-14
Abstract
Abstract A process yielding a glass blank in the form of a rod intended for drawing an optical fiber of the kind of self-focussing fiber i.e. having a radial refractive index gradient, having features (substantially transparency or transmission efficiency) lower than those of the fibers intended for long distance communication but sufficient for middle distance transmission, and which exhibits a lower cost than known processes. In a first stage a phase separation yields a "hard" phase (rich in silicon) and a "soft" phase (poor in silicon and rich in impurities) due to the drawing of a rod from a bath of molten glass through a cooling system having a strong temperature gradient and creating a radial refractive index gradient. In a second stage the soft phase is leached, eliminating the impurities contained in the soft phase but keeping safe the radial gradient. In a third stage a consolidation treatment is a pure annealing treatment rendering the hard phase more homogeneous.
Inventors
- 👤 Arnaud DE Panafieu
- 👤 Michel Villard
- 👤 Christiane Baylac
- 👤 Michel Favre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:50
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C23/00; C03C23/008; C03C3/076; C03C3/089; C03C3/091
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
237 words
A process for the manufacture of a glass blank used in the preparation of self-focusing optical fibers having a radial refractive index gradient, wherein said glass blank has a larger diameter than said fibers, from starting oxides which are capable of entering into a glass composition showing the phenomenon of separation into two interconnected and continuous solid phases of different composition, said starting oxides comprising oxides of boron, silicon, sodium and at least one oxide selected from the group consisting of germanium, titanium, phosphorous and aluminum oxides, and said oxides having an impurity level of under 10 -5 calculated with molar proportions of oxides of transition metals taken into account, and which comprises the stages of I. mixing said oxides; followed by melting said oxides into a molten bath; Ii. drawing said glass blank at a rate from said molten bath through a cooling system having a decreasing temperature gradient wherein said rate and temperature gradient are sufficient to cause an incipient phase separation in said glass blank and a radial variation in the chemical composition of each phase as a result of the variation in the rate of cooling between the periphery and the core of the blank due to the passage of said glass blank through said cooling system; followed by thermally annealing said glass blank; and Iii. leaching said glass blank to eliminate most of the impurities; followed by heat consolidating said glass blank.
Claim 2
Dependent Claim
237 words
A process for the manufacture of a glass blank used in the preparation of self-focusing optical fibers having a radial refractive index gradient, wherein said glass blank has a larger diameter than said fibers, from starting oxides which are capable of entering into a glass composition showing the phenomenon of separation into two interconnected and continuous solid phases of different composition, said starting oxides comprising oxides of boron, silicon, sodium and at least one oxide selected from the group consisting of germanium, titanium, phosphorous and aluminum oxides, and said oxides having an impurity level of under 10 -5 calculated with molar proportions of oxides of transition metals taken into account, and which comprises the stages of I. mixing said oxides; followed by melting said oxides into a molten bath; Ii. drawing said glass blank at a rate from said molten bath through a cooling system having a decreasing temperature gradient wherein said rate and temperature gradient are sufficient to cause an incipient phase separation in said glass blank and a radial variation in the chemical composition of each phase as a result of the variation in the rate of cooling between the periphery and the core of the blank due to the passage of said glass blank through said cooling system; followed by thermally annealing said glass blank; and Iii. leaching said glass blank to eliminate most of the impurities; followed by heat consolidating said glass blank.
Claim 3
Dependent Claim
96 words
A process as claimed in claim 1, wherein said starting oxides are mixed in the following molar proportions: from 35 to 70% of SiO 2 from 17 to 42% of B 2 O 3 from 4 to 15% of Na 2 O and at least one of the following oxides, mixed in the following molar proportions with respect to the entirety of materials: from 0 to 5% of Al 2 O 3 from 0 to 10% of TiO 2 from 0 to 10% of P 2 O 5 from 0 to 15% of GeO 2 .
Claim 4
Dependent Claim
36 words
A process as claimed in claim 1, wherein said starting oxides have the following molar proportions: 57% of SiO 2 25% of B 2 O 3 8% of Na 2 O 10% of GeO 2 .
Claim 5
Dependent Claim
52 words
A process as claimed in claim 1, wherein prior to the heat consolidation treatment, the process additionally comprises rinsing with deionised water, first drying at 100° C. in a gas stream and subsequently drying in vacuo over a period of about 20 hours at a temperature of from 500° to 600° C.
Claim 6
Dependent Claim
36 words
A process as claimed in claim 1, wherein said heat consolidation treatment is carried out over a period of from one to several hours at a temperature in the range from 700° C. to 900° C.
Claim 7
Dependent Claim
26 words
A process as claimed in claim 1, wherein prior to the heat consolidation treatment the process additionally comprises heating said glass blank in a controlled atmosphere.
Claim 8
Dependent Claim
37 words
A process as claimed in claim 1, wherein said blank is drawn in a tubular shape and said blank is heated in the flame after the consolidation step to convert said tubular blank into a solid blank.
Claim 9
Dependent Claim
21 words
A process as claimed in claim 1, wherein after said heat consolidation step said blank is converted into a glass fiber.
Claim 10
Dependent Claim
57 words
A process as claimed in claim 1 wherein, after heat consolidation, said blank is placed in a tube of glass rich in silica wherein said silica content is about 90% and wherein the internal diameter of said tube is adjusted to fit the diameter of said blank; and said blank is thereafter drawn to a glass fiber.
References Cited (Backward Citations)
US3758284A
Cited
US3881945A
Cited
US3929497A
Cited
US3938974A
Cited
US3870399A
Cited
US4097258A
Cited
US4061486A
Cited
US4060401A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-20 | 1983-02-19 | 1983-08-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-20 | 1987-02-19 | 1987-08-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-20 | 1991-02-19 | 1991-08-21 | $7700.00 | Window Closed / Lapsed |