Strengthening of thin-walled, light glass containers
Assignee: Yamamura Glass KK
•
Filing: 1978-02-27
•
Granted: 1979-08-14
•
Expires: 1998-02-27
Abstract
Abstract Thin-walled, light glass containers formed by the press and blow process may be strengthened by (1) exposing the internal surface of said containers to the action of an agent capable of decreasing the amount of extractable alkali from said surface at an elevated temperature immediately after the blowing process but before the annealing process; (2) passing the containers through the annealing station; and (3) subjecting the external and internal surfaces of said glass containers to a treatment of exchanging sodium ions in the surface portion with potassium ions to form a compressive stress layer in said surface portion.
Inventors
- 👤 Muneo Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:21
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C15/00; C03C21/00; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/211; C03C2217/212; C03C2217/218; C03C2217/22; C03C2218/00; C03C2218/30; C03C2218/32
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
148 words
In a process for strengthening thin-walled, light containers made of soda-lime glass comprising the steps of molding said containers by the press-and-blow process, annealing the glass containers and thereafter exchanging sodium ions present in the surface portion of the external surface and the internal surface of said containers with potassium ions to form a compressive stress layer in said surface portion, the improvement which comprises the pretreatment step of placing a compound selected from the group consisting of elemental sulfur, sulfur dioxide, ammonium chloride, ammonium sulfate, aluminum chloride, water, a fluorine-containing substance and a mixture thereof into the interior of said containers immediately after the molding step but before the annealing step at an elevated temperature so that only said internal surface of said containers reacts with the gas generated from said compound at said elevated temperature to decrease the amount of extractable alkali on said internal surface.
Claim 2
Dependent Claim
148 words
In a process for strengthening thin-walled, light containers made of soda-lime glass comprising the steps of molding said containers by the press-and-blow process, annealing the glass containers and thereafter exchanging sodium ions present in the surface portion of the external surface and the internal surface of said containers with potassium ions to form a compressive stress layer in said surface portion, the improvement which comprises the pretreatment step of placing a compound selected from the group consisting of elemental sulfur, sulfur dioxide, ammonium chloride, ammonium sulfate, aluminum chloride, water, a fluorine-containing substance and a mixture thereof into the interior of said containers immediately after the molding step but before the annealing step at an elevated temperature so that only said internal surface of said containers reacts with the gas generated from said compound at said elevated temperature to decrease the amount of extractable alkali on said internal surface.
Claim 3
Dependent Claim
142 words
The process of claim 1, wherein said sodium ion-exchanging step comprises applying a relatively concentrated aqueous solution of a mixture of potassium nitrate and a potassium salt selected from the group consisting of potassium chloride and potassium sulfate onto the external and internal surfaces of the glass containers while the temperature of the solution is higher than that of the containers so that said potassium salt precipitates out on said surfaces due to the temperature differential between the solution and the containers to form a solid layer of said mixture, maintaining the glass containers at an elevated temperature below but near the strain point of said glass to cause said ion-exchanging reaction for a length of time sufficient to form a compressive stress layer on said surfaces, cooling the glass containers to room temperature and removing said solid layer of said mixture.
Claim 4
Dependent Claim
36 words
The process of claim 2, wherein said mixture has such proportion that about 10% to 80% of the mixture occurs as a solid phase at said temperature below but near the strain point of said glass.
Claim 5
Dependent Claim
14 words
The process of claim 2, wherein said temperature differential is less than 75° C.
Claim 6
Dependent Claim
41 words
The process of claim 1, which further includes the step of applying an abrasion-resistant coating of a metal oxide on the external surface of said glass container at an elevated temperature immediately after the blowing process but before the pretreatment process.
Claim 7
Dependent Claim
25 words
The process of claim 5, wherein said metal oxide is selected from the group consisting of tin oxide, titanium oxide, zirconium oxide and vanadium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-13 | 1983-02-12 | 1983-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-13 | 1987-02-12 | 1987-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-13 | 1991-02-12 | 1991-08-14 | $7700.00 | Window Closed / Lapsed |