Method for determining sulfur content of cast iron
Assignee: Individual
•
Filing: 1978-05-01
•
Granted: 1979-08-14
•
Expires: 1998-05-01
Abstract
Abstract A test for determining the sulfur content of the base cast iron used for the production of nodular iron or iron containing compacted graphite. A sample of the molten base cast iron is removed from the melt, then a known amount of a nodular iron inoculant or a compacted iron inoculant is added to the molten metal. The molten metal sample is then cast into test bar or test wedge, solidified and tested to determine whether the bar or wedge is nodular iron or iron containing compacted graphite. The test may be fractured and inspected to visually determine whether the fracture is gray or white. Alternatively, the wedge or bar may be ultrasonically tested to determine whether the wedge or bar contains flake graphite or nodular graphite or compacted graphite. As a further alternative, the cooling or solidification curve of the molten metal sample, after inoculation, can be determined and compared with the cooling curve from a molten base cast iron sample. The comparison will show the shifting of the phase change points between the two curves, and this shifting can be correlated with the sulfur content of the base cast iron to form the basis for determining the amount of nodularizing inoculant to be added to the base metal, thus insuring adequate, yet not wasteful, inoculant addition during production. The inoculant can be added by various procedures and, by performing certain initial, qualifying tests, the sulfur content of any base metal composition can be determined with accuracy and without the need for either chemical or spectroscopic analysis.
Inventors
- 👤 Henry A. Laforet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:07
CPC Classifications
G; G01; G01N; G01N33/00; G01N33/20; G01N33/202; G01N33/2022
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
91 words
The method of determining the sulfur content of cast iron by the steps of (1) adding to a sample of molten cast iron iron an amount of cerium ranging from 0.25% to about 1.0% by weight of the sample, (2) casting the sample into a test bar having a cross section in the form of a 60°, 30°, right triangle, (3) fracturing the test bar, (4) observing the location and amount of any white areas in the test bar to determine the sulfur content of the metal constituting the test bar.
Claim 2
Independent Claim
91 words
The method of determining the sulfur content of cast iron by the steps of (1) adding to a sample of molten cast iron iron an amount of cerium ranging from 0.25% to about 1.0% by weight of the sample, (2) casting the sample into a test bar having a cross section in the form of a 60°, 30°, right triangle, (3) fracturing the test bar, (4) observing the location and amount of any white areas in the test bar to determine the sulfur content of the metal constituting the test bar.
Claim 3
Independent Claim
86 words
The method of determining the sulfur content of a base cast iron, comprising the steps of (1) pouring a molten sample of the base cast iron into a test bar; (2) during the performance of Step (1) incorporating into the molten metal an amount of a nodular iron innoculant sufficient to convert the cast iron to nodular iron if the sulfur content of the test bar is less than about 0.03% by weight; and (3) visually or ultrasonically determining whether the test bar is nodular iron.
Claim 4
Independent Claim
86 words
The method of determining the sulfur content of a base cast iron, comprising the steps of (1) pouring a molten sample of the base cast iron into a test bar; (2) during the performance of Step (1) incorporating into the molten metal an amount of a nodular iron innoculant sufficient to convert the cast iron to nodular iron if the sulfur content of the test bar is less than about 0.03% by weight; and (3) visually or ultrasonically determining whether the test bar is nodular iron.
Claim 5
Independent Claim
88 words
The method of determining the sulfur content of a base cast iron, comprising the steps of (1) pouring a sample of the molten base metal through a flow path into a test bar mold; (2) interposing in said flow path a source of nodular iron inoculant; (3) during the performance of Steps (1) and (2), incorporating the inoculant into the molten base metal; and (4) determining whether the innoculant has reacted with the sulfur content of the base metal and the test bar is free of flake graphite.
Claim 6
Independent Claim
88 words
The method of determining the sulfur content of a base cast iron, comprising the steps of (1) pouring a sample of the molten base metal through a flow path into a test bar mold; (2) interposing in said flow path a source of nodular iron inoculant; (3) during the performance of Steps (1) and (2), incorporating the inoculant into the molten base metal; and (4) determining whether the innoculant has reacted with the sulfur content of the base metal and the test bar is free of flake graphite.
Claim 7
Independent Claim
103 words
The method of determining the sulfur content of molten cast iron, comprising the steps of (1) removing a sample of the molten cast iron; (2) forming the molten cast iron sample into a test wedge; (3) during the performance of Steps (1) and (2) incorporating into the molten sample a known amount of a nodularizing inoculant; (4) fracturing the sample test wedge; and (5) observing the coloration of the test wedge at the point of fracture to determine whether the inoculant has reacted with all the sulfur in the samples and has converted the test metal into nodular iron or compacted graphic iron.
Claim 8
Independent Claim
103 words
The method of determining the sulfur content of molten cast iron, comprising the steps of (1) removing a sample of the molten cast iron; (2) forming the molten cast iron sample into a test wedge; (3) during the performance of Steps (1) and (2) incorporating into the molten sample a known amount of a nodularizing inoculant; (4) fracturing the sample test wedge; and (5) observing the coloration of the test wedge at the point of fracture to determine whether the inoculant has reacted with all the sulfur in the samples and has converted the test metal into nodular iron or compacted graphic iron.
Claim 9
Independent Claim
96 words
The method of determining the sulfur content of a molten base cast iron preparatory to the inoculation of the cast iron to form either nodular iron or compacted graphite iron, comprising the steps of (1) withdrawing a molten sample of the base cast iron; (2) solidifying the molten sample into a test wedge; (3) intermediate Steps (1) and (2) incorporating a known amount of an inoculant selected from the group consisting of cerium and magnesium into the molten base cast iron; and (4) determining whether the test bar is free of residual sulfur and flake carbon.
Claim 10
Independent Claim
96 words
The method of determining the sulfur content of a molten base cast iron preparatory to the inoculation of the cast iron to form either nodular iron or compacted graphite iron, comprising the steps of (1) withdrawing a molten sample of the base cast iron; (2) solidifying the molten sample into a test wedge; (3) intermediate Steps (1) and (2) incorporating a known amount of an inoculant selected from the group consisting of cerium and magnesium into the molten base cast iron; and (4) determining whether the test bar is free of residual sulfur and flake carbon.
Claim 11
Independent Claim
104 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) inoculating a series of molten samples of the molten cast iron with varying amounts of an innoculant selected from the group consisting of cerium and magnesium, (2) testing each sample to determine the amount of inoculant necessary to eliminate flake carbon from the sample, (3) comparing the necessary amount determined in Step (2) with a chemical analysis of the cast iron sulfur content, and (4) thereafter inoculating periodic samples with said inoculant in the necessary amount to determine any variation of the sulfur content of such periodic samples.
Claim 12
Independent Claim
104 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) inoculating a series of molten samples of the molten cast iron with varying amounts of an innoculant selected from the group consisting of cerium and magnesium, (2) testing each sample to determine the amount of inoculant necessary to eliminate flake carbon from the sample, (3) comparing the necessary amount determined in Step (2) with a chemical analysis of the cast iron sulfur content, and (4) thereafter inoculating periodic samples with said inoculant in the necessary amount to determine any variation of the sulfur content of such periodic samples.
Claim 13
Independent Claim
84 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) withdrawing two molten samples of the base cast iron; (2) inoculating one sample with a known amount of a nodularizing ingredient; (3) solidifying each sample; (4) during the performance of step (3) measuring the solidification curve of each sample; and (5) comparing the shift change points of the two curves determine whether the known amount of nodularizing ingredient has eliminated sulfur and flake graphite from the inoculated sample.
Claim 14
Independent Claim
84 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) withdrawing two molten samples of the base cast iron; (2) inoculating one sample with a known amount of a nodularizing ingredient; (3) solidifying each sample; (4) during the performance of step (3) measuring the solidification curve of each sample; and (5) comparing the shift change points of the two curves determine whether the known amount of nodularizing ingredient has eliminated sulfur and flake graphite from the inoculated sample.
Claim 15
Independent Claim
85 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) withdrawing two molten samples of the base cast iron; (2) inoculating one sample with a known amount of a nodularizing ingredient; (3) solidifying each sample; (4) transmitting ultrasonic vibrations through each sample; (5) during the performance of step (4) measuring the time of transmission; and (6) comparing the transmission times to determine whether the known amount of nodularizing ingredient has eliminated sulfur and flake graphite from the inoculated sample.
Claim 16
Independent Claim
85 words
The method of determining the sulfur content of molten cast iron comprising the steps of (1) withdrawing two molten samples of the base cast iron; (2) inoculating one sample with a known amount of a nodularizing ingredient; (3) solidifying each sample; (4) transmitting ultrasonic vibrations through each sample; (5) during the performance of step (4) measuring the time of transmission; and (6) comparing the transmission times to determine whether the known amount of nodularizing ingredient has eliminated sulfur and flake graphite from the inoculated sample.
Claim 17
Independent Claim
100 words
The method of determining the sulfur content of a molten base cast iron preparatory to the inoculation of the cast iron to form either nodular iron or compacted graphite iron, comprising the steps of (1) withdrawing a molten sample of the base cast iron; (2) solidifying the molten sample into a test wedge; (3) intermediate Steps (1) and (2), blowing into the molten iron an inert gas having suspended therein a known amount of an inoculant selected from the group consisting of cerium and magnesium; and (4) determining whether the test bar is free of residual sulfur and flake carbon.
Claim 18
Independent Claim
100 words
The method of determining the sulfur content of a molten base cast iron preparatory to the inoculation of the cast iron to form either nodular iron or compacted graphite iron, comprising the steps of (1) withdrawing a molten sample of the base cast iron; (2) solidifying the molten sample into a test wedge; (3) intermediate Steps (1) and (2), blowing into the molten iron an inert gas having suspended therein a known amount of an inoculant selected from the group consisting of cerium and magnesium; and (4) determining whether the test bar is free of residual sulfur and flake carbon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-08-13 | 1983-02-12 | 1983-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-08-13 | 1987-02-12 | 1987-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-08-13 | 1991-02-12 | 1991-08-14 | $7700.00 | Window Closed / Lapsed |