Abstract A method of preparing an electrochemical cell including a metal sulfide as the positive electrode reactant and lithium alloy as the negative electrochemical reactant with an alkali metal, molten salt electrolyte is disclosed which permits the assembly to be accomplished in air. The electrode reactants are introduced in the most part as a sulfide of lithium and the positive electrode metal in a single-phase compound. For instance, Li 2 FeS 2 is a single-phase compound that is produced by the reaction of Li 2 S and FeS. This compound is an intermediate in the positive electrode cycle from FeS 2 to Fe and Li 2 S. Its use minimizes volumetric changes from the assembled to the charged and discharged conditions of the electrode and minimizes electrode material interaction with air and moisture during assembly.
A method of preparing a positive electrode for use in a secondary electrochemical cell also including a negative electrode having lithium or lithium-metalloid alloy as the neagative electrode reactant and a molten salt including a lithium halide as electrolyte, said method comprising combining FeS with Li 2 S to form the compound Li 2 FeS 2 ; incorporating said compound into an integral structure for use as a positive electrode; and assembling said positive electrode into said electrochemical cell.
Claim 2
Independent Claim
79 words
A method of preparing a positive electrode for use in a secondary electrochemical cell also including a negative electrode having lithium or lithium-metalloid alloy as the neagative electrode reactant and a molten salt including a lithium halide as electrolyte, said method comprising combining FeS with Li 2 S to form the compound Li 2 FeS 2 ; incorporating said compound into an integral structure for use as a positive electrode; and assembling said positive electrode into said electrochemical cell.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein said Li 2 FeS 2 is formed by melting approximately equal molar amounts of FeS with Li 2 S together at about 1300 K and resolidifying to form single-phase, solid Li 2 FeS 2 .
Claim 4
Dependent Claim
47 words
The method of claim 1 wherein FeS and Li 2 S are combined in about equal molar portions and Cu 2 S is added to the combination in an amount less than 10 mole percent based on total metal sulfides to form a single-phased, positive electrode material.
Claim 5
Dependent Claim
33 words
The method of claim 3 wherein FeS, Li 2 S and Cu 2 S are reacted together in the molar proportion of 5, 5 to 1 respectively to form the positive electrode material.
Claim 6
Dependent Claim
28 words
The method of claim 1 wherein Li 2 FeS 2 in particulate form is blended with solid particulate LiCl-KCl salt and pressed to form a positive electrode compact.
Claim 7
Dependent Claim
36 words
The method of claim 1 wherein a uniform mixture of Li 2 FeS 2 and a second transition metal sulfide selected from the sulfides of cobalt and nickel is formed for use in said positive electrode.
Claim 8
Dependent Claim
18 words
The method of claim 1 wherein said cell is assembled in air with less than 30% relative humidity.