Method of preparing an electrochemical cell in uncharged state
Assignee: Energy Research and Development Administration ERDA
•
Filing: 1976-03-11
•
Granted: 1977-02-01
•
Expires: 1996-03-11
Abstract
Abstract A secondary electrochemical cell is assembled in an uncharged state for the preparation of a lithium alloy-transition metal sulfide cell. The negative electrode includes a material such as aluminum or silicon for alloying with lithium as the cell is charged. The positive electrode is prepared by blending particulate lithium sulfide, transition metal powder and electrolytic salt in solid phase. The mixture is simultaneously heated to a temperature in excess of the melting point of the electrolyte and pressed onto an electrically conductive substrate to form a plaque. The plaque is assembled as a positive electrode within the cell. During the first charge cycle lithium alloy is formed within the negative electrode and transition metal sulfide such as iron sulfide is produced within the positive electrode.
Inventors
- 👤 Hiroshi Shimotake
- 👤 Louis G. Bartholme
- 👤 John D. Arntzen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 04:36
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/13; H01M10/00; H01M10/36; H01M10/39; H01M10/399; H01M4/04; H01M4/0438; H01M4/044; H01M4/0459; H01M4/0461; H01M4/36; H01M4/58; H01M4/581; H01M4/5815; H01M2004/026; H01M2004/027; H01M2004/028; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M4/043; H01M4/38; H01M4/40; H01M4/405; H01M4/64; H01M4/66; H01M4/661; H01M4/70; H01M4/80; H01M4/808; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
132 words
A method of preparing a positive electrode for use in a secondary electrochemical cell opposite to a negative electrode containing an element for alloying with lithium comprising blending particulate lithium sulfide, transition metal and electrolytic salt of alkali metal halides or alkaline earth metal halides at a temperature below the melting point of the electrolytic salt to form a solid mixture; heating said solid mixture to a temperature in excess of the melting point of said electrolytic salt while simultaneously pressing said mixture onto an electrically conductive substrate to form a plaque; and assembling said plaque as a positive electrode within said electrochemical cell opposite to said negative electrode and electrically charging said cell to produce a transition metal sulfide in said positive electrode and a lithium alloy within said negative electrode.
Claim 2
Independent Claim
132 words
A method of preparing a positive electrode for use in a secondary electrochemical cell opposite to a negative electrode containing an element for alloying with lithium comprising blending particulate lithium sulfide, transition metal and electrolytic salt of alkali metal halides or alkaline earth metal halides at a temperature below the melting point of the electrolytic salt to form a solid mixture; heating said solid mixture to a temperature in excess of the melting point of said electrolytic salt while simultaneously pressing said mixture onto an electrically conductive substrate to form a plaque; and assembling said plaque as a positive electrode within said electrochemical cell opposite to said negative electrode and electrically charging said cell to produce a transition metal sulfide in said positive electrode and a lithium alloy within said negative electrode.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said lithium sulfide transition metal and electrolytic salt are comminuted to about 350 micrometers particle size.
Claim 4
Dependent Claim
32 words
The method of claim 1 wherein iron and copper powder is included within said solid mixture and FeS with sulfides of copper are produced within said positive electrode during said electrical charging.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein iron and cobalt powder is included within said solid mixture and FeS 2 with sulfides of cobalt are produced during the electrical charging of said cell.
Claim 6
Dependent Claim
34 words
The method of claim 1 wherein said solid mixture includes a eutectic composition of LiCl-KCl as electrolytic salt and is heated to 350° to 400° C. and maintained for about 10 minutes while pressing.
Claim 7
Dependent Claim
36 words
The method of claim 1 wherein said mixture is pressed within a die onto an electrically conductive substrate at about 2 to 3 MPa while heating in excess of the melting point of said electrolytic salt.
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein two plaques are formed and bonded together for assembly as said positive electrode.
Claim 9
Dependent Claim
55 words
The method of claim 1 wherein said electrically conductive substrate on which said mixture is pressed comprises an iron grid and sufficient iron powder being included within said mixture to combine with all of the included sulfur and said electrochemical cell being operated at cutoff voltages sufficiently low to prevent production of FeS 2 .
Claim 10
Dependent Claim
33 words
The method of claim 1 wherein lithium sulfide is provided in sufficient amount to be in stoichiometric excess to that required to combine with all of said transition metal powder as a monosulfide.
Claim 11
Dependent Claim
15 words
The method of claim 1 wherein Li 2 C 2 is included within said mixture.
Claim 12
Dependent Claim
30 words
The method of claim 10 wherein said Li 2 C 2 is included in an amount of about 5 to 25 mole percent in combination with said Li 2 S.
Claim 13
Dependent Claim
27 words
The method of claim 10 wherein said electrochemical cell is operated at discharge cutoff voltages sufficiently high to prevent formation of Li 2 C 2 on discharge.
Claim 14
Dependent Claim
31 words
The method of claim 10 wherein said electrochemical cell is initially charged to convert substantially all of said lithium carbide and lithium sulfide to lithium alloy, iron sulfides and carbon powder.
References Cited (Backward Citations)
US3881951A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-01 | 1980-08-02 | 1981-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-01 | 1984-08-02 | 1985-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-01 | 1988-08-02 | 1989-02-01 | $7700.00 | Window Closed / Lapsed |