Method and composition for reclaiming polyurethane
Assignee: Ross Air Systems Inc
•
Filing: 1976-07-01
•
Granted: 1979-07-31
•
Expires: 1996-07-01
Abstract
Abstract Decomposiing polyurethane foams by treating such polyurethane materials with ammonia or ammonium hydroxide, preferably in the presence of a suitable organic solvent such as a glycol or polyol, or the decomposition product of a polyurethane. Treatment of the polyurethane material with ammonia or ammonium hydroxide, particularly in combination with such solvent, is carried out preferably at elevated temperature, and results in decomposition of the polyurethane. The resulting reaction product containing polyol fragments from such decomposition or depolymerization, can be incorporated with fresh polyurethane reactants, including polyisocyanate, or polyol and polyisocyanate, to produce new urethane polymer, thus permitting recovery and re-use of otherwise useless scrap polyurethane materials.
Inventors
- 👤 Martin B. Sheratte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:50
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/10; C08J11/16; C08J2375/00; C08J2375/04; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
39 words
A process for decomposing polyurethane which comprises treating said polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, completely liquefying said polyurethane, and recovering the reaction mixture.
Claim 2
Dependent Claim
39 words
A process for decomposing polyurethane which comprises treating said polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, completely liquefying said polyurethane, and recovering the reaction mixture.
Claim 3
Dependent Claim
64 words
A process for decomposing polyurethane which comprises treating said polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, completely liquefying said polyurethane, and recovering the reaction mixture, said treating said polyurethane with said ammonia taking place in the presence of an organic solvent having a boiling point of at least 100° C.
Claim 4
Dependent Claim
64 words
A process for decomposing polyurethane which comprises treating said polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, completely liquefying said polyurethane, and recovering the reaction mixture, said treating said polyurethane with said ammonia taking place in the presence of an organic solvent having a boiling point of at least 100° C.
Claim 5
Dependent Claim
13 words
The process as defined in claim 2, wherein said ammonia is ammonia gas.
Claim 6
Dependent Claim
21 words
The process as defined in claim 2, comprising contacting said polyurethane with said solvent while treating the mixture with said ammonia.
Claim 7
Dependent Claim
16 words
The process as defined in claim 4, wherein ammonia gas is passed into said organic solvent.
Claim 8
Dependent Claim
15 words
The process as defined in claim 1, said treating being carried out in an autoclave.
Claim 9
Dependent Claim
22 words
The process as defined in claim 2, said solvent being a compound suitable for reaction with a polyisocyanate to produce a polyurethane.
Claim 10
Dependent Claim
29 words
The process as defined in claim 2, said organic solvent selected from the group consisting of glycols, polyethers, polyols, mono- and polyalcohols, phenols, alkoxy benzenes, hydrocarbons and chlorinated hydrocarbons.
Claim 11
Dependent Claim
23 words
The process as defined in claim 2, wherein said solvent is a compound selected from the group consisting off glycols, polyols and polyethers.
Claim 12
Dependent Claim
52 words
The process as defined in claim 9, wherein said solvent is a compound selected from the group consisting of ethylene glycol, propylene glycol, and polyethylene and polypropylene glycols of molecular weight ranging from about 100 to about 5,000, and the adducts of propylene oxide with sorbitol and propylene oxide with ethylene diamine.
Claim 13
Dependent Claim
26 words
The process as defined in claim 2, the concentration of ammonia in said solvent ranging from about 0.1 to about 40% by weight of the solution.
Claim 14
Dependent Claim
23 words
The process as defined in claim 1, the proportion of ammonia to polyurethane employed ranging from about 0.1 to about 30% by weight.
Claim 15
Dependent Claim
23 words
The process as defined in claim 11, the proportion of ammonia to polyurethane employed ranging from about 0.1 to about 30% by weight.
Claim 16
Dependent Claim
28 words
The process as defined in claim 1, wherein said treating is carried out at a temperature within the range of from about 100 to about 250 degrees Centigrade.
Claim 17
Dependent Claim
23 words
The process as defined in claim 2, wherein said treating is carried out at temperature ranging from about 100° to about 250° C.
Claim 18
Dependent Claim
23 words
The process as defined in claim 2, wherein said treating is carried out at temperature ranging from about 150° to about 230° C.
Claim 19
Dependent Claim
35 words
The process as defined in claim 9, wherein said treating is carried out at temperature ranging from about 100° to about 250° C., for a period ranging from about 10 seconds to about 3 hours.
Claim 20
Dependent Claim
34 words
The process as defined in claim 9, wherein said treating is carried out at temperature ranging from about 150° to about 230° C. for a period ranging from about 1 to about 15 minutes.
Claim 21
Dependent Claim
23 words
The process as defined in claim 13, wherein said treating is carried out at temperature ranging from about 100° to about 250° C.
Claim 22
Dependent Claim
39 words
The process as defined in claim 13, wherein said solvent is a compound selected from the group consisting of glycols, polyols and polyethers, and said treating is carried out at temperature ranging from about 100° to about 250° C.
Claim 23
Dependent Claim
78 words
A process for decomposing and dissolving polyurethane which comprises passing a stream of ammonia gas through a solvent selected from the group consisting of glycols, polyols and polyethers, heated to a temperature ranging from about 100° to about 250° C., in the absence of water, adding polyurethane to said heated solvent and decomposing said polyurethane with said ammonia and completely liquefying said polyurethane, and recovering the resulting solution containing the decomposition products of said polyurethane and containing polyol.
Claim 24
Dependent Claim
78 words
A process for decomposing and dissolving polyurethane which comprises passing a stream of ammonia gas through a solvent selected from the group consisting of glycols, polyols and polyethers, heated to a temperature ranging from about 100° to about 250° C., in the absence of water, adding polyurethane to said heated solvent and decomposing said polyurethane with said ammonia and completely liquefying said polyurethane, and recovering the resulting solution containing the decomposition products of said polyurethane and containing polyol.
Claim 25
Dependent Claim
23 words
The process as defined in claim 21, wherein said treating is carried out at temperature ranging from about 150° to about 230° C.
Claim 26
Dependent Claim
52 words
The process as defined in claim 22, wherein said solvent is a polyol selected from the group consisting of ethylene glycol, propylene glycol, and polyethylene and polypropylene glycols of molecular weight ranging from about 100 to about 5,000, and the adducts of propylene oxide with sorbitol and propylene oxide with etheylene diamine.
Claim 27
Dependent Claim
26 words
The process as defined in claim 23, the concentration of ammonia in said solvent ranging from about 0.1 to about 40% by weight of the solution.
Claim 28
Dependent Claim
23 words
The process as defined in claim 24, the proportion of ammonia to polyurethane employed ranging from about 0.1 to about 30% by weight.
Claim 29
Dependent Claim
23 words
The process as defined in claim 25, said decomposition reaction taking place for a period ranging from about 1 to about 15 minutes.
Claim 30
Dependent Claim
23 words
The process as defined in claim 2, including reacting the resulting reaction mixture following treatment of said polyurethane, with polyisocyanate to produce polyurethane.
Claim 31
Dependent Claim
37 words
The process as defined in claim 1, including adding the resulting reaction mixture following treatment of said polyurethane, to a polyol reactant for producing polyurethane resin, and reacting the resulting polyol mixture with polyisocyanate to produce polyurethane.
Claim 32
Dependent Claim
37 words
The process as defined in claim 8, including adding the resulting reaction mixture following treatment of said polyurethane, to a polyol reactant for producing polyurethane resin, and reacting the resulting polyol mixture with polyisocyanate to produce polyurethane.
Claim 33
Dependent Claim
35 words
The process as defined in claim 29, wherein said polyol reactant is a polyalkylene ether polyol and said polyisocyanate is selected from the group consisting of the 2,4- and 2,6-toluene diisocyanates, and polyphenyl polymethylene polyisocyanate.
Claim 34
Dependent Claim
84 words
The process for decomposing and dissolving scrap polyurethane and employing the resulting solution for production of fresh polyurethane, which comprises contacting said scrap polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, in an organic solvent having a boiling point of at least 100° C., at a temperature ranging from about 100° to about 250° C., completely liquefying said polyurethane, and reacting the resulting reaction mixture with polyisocyanate to produce fresh polyurethane.
Claim 35
Dependent Claim
84 words
The process for decomposing and dissolving scrap polyurethane and employing the resulting solution for production of fresh polyurethane, which comprises contacting said scrap polyurethane with ammonia in the absence of water, said ammonia selected from the group consisting of ammonia gas and anhydrous ammonia, in an organic solvent having a boiling point of at least 100° C., at a temperature ranging from about 100° to about 250° C., completely liquefying said polyurethane, and reacting the resulting reaction mixture with polyisocyanate to produce fresh polyurethane.
Claim 36
Dependent Claim
36 words
The process as defined in claim 31, including adding the reaction mixture containing the dissolved depolymerized products of said scrap polyurethane to a polyol reactant, and reacting the resulting mixture with polyisocyanate to produce fresh polyurethane.
Claim 37
Dependent Claim
23 words
The process as defined in claim 32, wherein said solvent is a compound selected from the group consisting of glycols, polyols and polyethers.
Claim 38
Dependent Claim
42 words
The process as defined in claim 33, the concentration of ammonia in said solvent ranging from about 0.1 to about 40% by weight of the solution, the proportion of ammonia to polyurethane employed ranging from about 0.1 to about 30% by weight.
Claim 39
Dependent Claim
17 words
The process as defined in claim 34, said temperature ranging from about 150° to about 230° C.
Claim 40
Dependent Claim
35 words
The process as defined in claim 35, wherein said polyol reactants is a polyalkylene ether polyol and said polyisocyanate is selected from the group consisting of the 2,4- and 2,6-toluene diisocyanates, and polyphenyl polymethylene polyisocyanate.
Claim 41
Dependent Claim
40 words
A composition for decomposing polyurethane, comprising a mixture of ammonia, and a high boiling organic solvent selected from the group consisting of glycols, polyethers, polyols, mono- and polyalcohols, phenols, alkoxy benzenes, hydrocarbons and chlorinated hydrocarbons in the absence of water.
Claim 42
Dependent Claim
40 words
A composition for decomposing polyurethane, comprising a mixture of ammonia, and a high boiling organic solvent selected from the group consisting of glycols, polyethers, polyols, mono- and polyalcohols, phenols, alkoxy benzenes, hydrocarbons and chlorinated hydrocarbons in the absence of water.
Claim 43
Dependent Claim
23 words
A composition as defined in claim 37, wherein said solvent is a compound selected from the group consisting of glycols, polyols and polyethers.
Claim 44
Dependent Claim
53 words
A composition as defined in claim 38, wherein said solvent is a polyol selected from the group consisting of ethylene glycol, propylene glycol, and polyethylene glycol and polypropylene glycols of molecular weight ranging from about 100 to about 5,000, and the adducts of propylene oxide with sorbitol and propylene oxide with ethylene diamine.
Claim 45
Dependent Claim
29 words
A composition as defined in claim 37, said ammonia being present in said solvent in a concentration ranging from about 0.1 to about 40% by weight of the solution.
Claim 46
Dependent Claim
30 words
A solvent composition as defined in claim 39, said ammonia being present in said solvent in a concentration ranging from about 0.1 to about 40% by weight of the solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-30 | 1983-01-29 | 1983-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-30 | 1987-01-29 | 1987-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-30 | 1991-01-29 | 1991-07-31 | $7700.00 | Window Closed / Lapsed |