Molten salt leach for removal of inorganic cores from directionally solidified eutectic alloy structures
Assignee: General Electric Co
•
Filing: 1977-09-19
•
Granted: 1979-07-24
•
Expires: 1997-09-19
Abstract
Abstract Cores made of either Y 2 O 3 , Y 3 Al 5 O 12 , LaAlO 3 , MgAl 2 O 4 or Al 2 O 3 are removed from castings of advanced superalloy materials by immersion in a molten salt bath of either Li 3 AlF 6 or a mixture of CaF 2 -NaF.
Inventors
- 👤 Ronald H. Arendt
- 👤 Marcus P. Borom
- 👤 Irvin C. Huseby
- 👤 Frederic J. Klug
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:12
CPC Classifications
B; B22; B22D; B22D29/00; B22D29/001; B22D29/002
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
128 words
A method for removing ceramic cores from castings of superalloy materials including the process steps of (a) preparing a molten leachant salt bath of a mixture of 67 mole percent sodium fluoride and 33 mole percent calcium fluoride leachant salts; (b) covering the molten leachant salt bath with a controlled atmosphere which has an oxygen content of less than 50 ppm; (c) immersing the casting and the ceramic core in the molten leachant salt bath; (d) leaching the core material from the casting in the molten leachant salt bath, and (e) rinsing the casting to remove leachant products from the casting by immersing the casting in a molten salt rinse both having a composition of 9 mole percent NaCl, 36 mole percent KCl, and 55 mole percent LiCl.
Claim 2
Independent Claim
128 words
A method for removing ceramic cores from castings of superalloy materials including the process steps of (a) preparing a molten leachant salt bath of a mixture of 67 mole percent sodium fluoride and 33 mole percent calcium fluoride leachant salts; (b) covering the molten leachant salt bath with a controlled atmosphere which has an oxygen content of less than 50 ppm; (c) immersing the casting and the ceramic core in the molten leachant salt bath; (d) leaching the core material from the casting in the molten leachant salt bath, and (e) rinsing the casting to remove leachant products from the casting by immersing the casting in a molten salt rinse both having a composition of 9 mole percent NaCl, 36 mole percent KCl, and 55 mole percent LiCl.
Claim 3
Dependent Claim
29 words
The method of claim 1 and including the additional process step of agitating the molten leachant salt bath during the time the casting and the core are immersed therein.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein the molten leachant salt bath is agitated by bubbling a gas through the leachant salt bath.
Claim 5
Dependent Claim
27 words
The method of claim 3 wherein the controlled atmosphere is a gas which is one selected from the group consisting of argon, neon, hydrogen, nitrogen and helium.
Claim 6
Dependent Claim
11 words
The method of claim 4 wherein the controlled atmosphere is nitrogen.
Claim 7
Dependent Claim
35 words
The method of claim 4 wherein the gas bubbled through the molten salt bath is one selected from the group consisting of nitrogen gas, hydrogen gas, forming gas, helium gas, argon gas and neon gas.
Claim 8
Dependent Claim
12 words
The method of claim 6 wherein the bubbler gas is forming gas.
Claim 9
Dependent Claim
24 words
The method of claim 6 wherein the bubbler gas is forming gas of a composition of from about 90% by volume nitrogen, remainder hydrogen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-23 | 1983-01-22 | 1983-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-23 | 1987-01-22 | 1987-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-23 | 1991-01-22 | 1991-07-24 | $7700.00 | Window Closed / Lapsed |