Method of producing antireflective coatings on polydiethyleneglycoldiallylcarbonate, an optical product made by the method, and the use of the optical product
Assignee: Balzers und Leybold Deutschland Holding AG
•
Filing: 1977-12-21
•
Granted: 1979-07-17
•
Expires: 1997-12-21
Abstract
Abstract An optical body and a method of producing oxidic, antireflective coatings on transparent plastic substrates of polydiethyleneglycoldiallylcarbonate comprising depositing a first coating having a high refractive index by vaporizing an oxide mixture of essentially zirconium dioxide with a content of 4 to 15 weight percent of aluminum trioxide and depositing a second layer having a low refractive index by vaporizing in a vacuum a borosilicate glass containing less than 5 weight-percent of alkali metal oxides. The depositing of at least the first coating is performed in an oxidizing residual gas atmosphere.
Inventors
- 👤 Gerhard Kienel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:58
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/113; G02B1/115; B; B29; B29D; B29D11/00; B29D11/00009; B29D11/00865; C; C08; C08J; C08J7/00; C08J7/04; C08J7/046; C08J7/06; G02B1/04; C08J2369/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/31504; Y10T428/31507
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
117 words
A method of producing a three layer antireflective transparent article, comprising: providing a transparent plastic substrate of polydiethyleneglycoldiallylcarbonate to define the first layer; depositing a first coating on the substrate having a high refractive index by vaporizing an oxide mixture of substantially ZrO 2 with a content of 4 to 15 weight-percent of Al 2 O 3 to define the second layer; and depositing a second coating on the first coating having a low refractive index by the vaporization in a vacuum of a borosilicate glass containing less than 5 weight-percent of alkali metal oxides, to define the third layer wherein the depositing of at least the first coating is performed in an oxidizing residual gas atmosphere.
Claim 2
Independent Claim
117 words
A method of producing a three layer antireflective transparent article, comprising: providing a transparent plastic substrate of polydiethyleneglycoldiallylcarbonate to define the first layer; depositing a first coating on the substrate having a high refractive index by vaporizing an oxide mixture of substantially ZrO 2 with a content of 4 to 15 weight-percent of Al 2 O 3 to define the second layer; and depositing a second coating on the first coating having a low refractive index by the vaporization in a vacuum of a borosilicate glass containing less than 5 weight-percent of alkali metal oxides, to define the third layer wherein the depositing of at least the first coating is performed in an oxidizing residual gas atmosphere.
Claim 3
Dependent Claim
38 words
The method according to claim 1, wherein the first and second coats are deposited in a thickness of a quarter wavelength with respect to the wavelength of visible light for which the human eye has the maximum sensitivity.
Claim 4
Dependent Claim
56 words
The method according to claim 1, wherein the first coat is applied in a thickness of about one twelfth of a wavelength with respect to the wavelength of visible light for which the human eye has the maximum sensitivity, and that the material of the second coat is deposited until the reflection has a minimum value.
Claim 5
Dependent Claim
91 words
A three layer antireflective transparent optical body, consisting of a substrate of polydiethyleneglycoldiallylcarbonate to define the first layer; a first coat on the substrate of ZrO 2 having a content of 4 to 15 weight-percent of Al 2 O 3 and having a first refractive index to define the second layer; and a second coat of a borosilicate glass superposed on the first coating and containing less than 5 weight-percent of alkali metal oxides and having a second refractive index less than said first refractive index to define the third layer.
Claim 6
Dependent Claim
91 words
A three layer antireflective transparent optical body, consisting of a substrate of polydiethyleneglycoldiallylcarbonate to define the first layer; a first coat on the substrate of ZrO 2 having a content of 4 to 15 weight-percent of Al 2 O 3 and having a first refractive index to define the second layer; and a second coat of a borosilicate glass superposed on the first coating and containing less than 5 weight-percent of alkali metal oxides and having a second refractive index less than said first refractive index to define the third layer.
Claim 7
Dependent Claim
44 words
The optical body according to claim 4, wherein the first coating is applied by vaporizing the oxide mixture and the second coating is applied by vaporization in a vacuum and wherein at least the first coating is applied in an oxidizing residual gas atmosphere.
Claim 8
Dependent Claim
10 words
An optical lens comprising the optical body of claim 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-16 | 1983-01-15 | 1983-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-16 | 1987-01-15 | 1987-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-16 | 1991-01-15 | 1991-07-17 | $7700.00 | Window Closed / Lapsed |