Solventless silicone resins
Assignee: General Electric Co
•
Filing: 1978-01-31
•
Granted: 1979-07-10
•
Expires: 1998-01-31
Abstract
Abstract There is provided by the present invention a process for producing a solventless silicone resin having a viscosity at 100% varying from 200 to 5,000 centipoise at 25° C., comprising adding a mixture of water and alcohol to the desired organochlorosilanes taking the silicone alkoxylate and washing it repeatedly with alcohol until the acid content is at least below 1000 parts per million, adding an alkali metal hydroxide to reduce the acidity of the silicone alkoxylate such that it does not exceed 100 parts per million, and then adding sufficient water such that the amount of water that is added is between 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in such silicone hydrolyxate. The excess alcohol and water is stripped off to give the solventless silicone resin of the instant invention having an organo to Si ratio varying from 1.1 to 1.9, having a silanol content varying from 1 to 4% by weight and a hydrocarbonoxy content that varies from 7 to 14% by weight. A less preferred solventless system can be obtained by simply mixing in an organic solvent, a high alkoxy containing silicone resin produced by traditional procedures, and a high silanol silicone resin also produced by traditional procedure and stripping off the solvent.
Inventors
- 👤 George F. Roedel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:33
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/06; C08L; C08L83/00; C08L83/04; C08G77/14; C08G77/18; C08G77/20; C08G77/70
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
209 words
A process for producing a solventless silicone resin having a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosilanes of the formula, R.sub.a Si Cl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added is from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoxylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product.
Claim 2
Dependent Claim
209 words
A process for producing a solventless silicone resin having a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosilanes of the formula, R.sub.a Si Cl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added is from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoxylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein after step (a), the alkoxylate is heated to a temperature in the range of 60° to 80° C. to drive off HCl prior to step (c).
Claim 4
Dependent Claim
66 words
The process of claim 1 wherein in step (c) there is added from 0.1 to 2 parts of the aliphatic alcohol per part of said alkoxylate and wherein said alkoxylate and alcohol mixture is heated to a range of 80° C. to 100° C. to strip off the alcohol and HCl wherein the step is repeated until the acid content is below 1000 parts per million.
Claim 5
Dependent Claim
31 words
The process of claim 3 wherein the aliphatic alcohol has the formula, R' OH where R' is selected from the class consisting of alkyl radicals of 1 to 3 carbon atoms.
Claim 6
Dependent Claim
19 words
The process of claim 4 wherein the aliphatic alcohol is methanol and the alkali metal hydroxide is potassium hydroxide.
Claim 7
Dependent Claim
25 words
The process of claim 5 wherein after the potassium hydroxide is added, the acid content of the methoxylate does not exceed 100 parts per million.
Claim 8
Dependent Claim
27 words
The process of claim 1 wherein in the step (e) the water is added in increments over a period of time varying from 0.5 to 3 hours.
Claim 9
Dependent Claim
17 words
The process of claim 5 wherein the potassium hydroxide is added as a solution in said methanol.
Claim 10
Dependent Claim
44 words
The process of claim 7 wherein methanol is added along with the water in step (e) so as to solubilize the water into the alkoxylate and wherein in step (f) said methanol is stripped off to leave behind the silicone resin at 100% solids.
Claim 11
Dependent Claim
50 words
The silicone resin product by the process of claim 1 wherein said resin has an R to Si ratio that varies from 1.0 to 1.9 to 1, a silanol content that varies from 0 to 4% by weight and a hydrocarbonoxy content that varies from 7 to 14% by weight.
Claim 12
Dependent Claim
43 words
The silicone resin produced by the process of claim 1 wherein the said resin has a R to Si ratio that varies from 1.0 to 1.9 to 1, and a viscosity at 100% which varies from 500 to 2,000 centipoise at 25° C.
Claim 13
Dependent Claim
69 words
The process of claim 1 wherein said resin is cured by adding to it from 0.05 to 0.5% of metal by weight of the total composition of a catalyst which is a metal salt of a carboxylic acid selected from the class consisting of metals ranging from manganese to zinc in the Periodic Table with the exception of iron and heating the mixture at a temperature above 200° C.
Claim 14
Dependent Claim
43 words
The process of claim 12 wherein said resin is cured by adding to it in addition to the metal salt catalysts the iron salt of a carboxylic acid at a concentration of from 0.005% iron or less by weight of the total composition.
Claim 15
Dependent Claim
91 words
The process of claim 1 wherein said resin is cured by adding to it from 0.5 to 4.0% by weight of the total composition of a catalyst which is the combination of 25 to 75% by weight of the metal salt of a carboxylic acid the metal ion being selected from the class consisting of metals ranging from manganese to zinc in the Periodic Table with the exception of iron and 25 to 75% by weight of an amine functional silane, and heating the mixture at a temperature above 100° C.
Claim 16
Dependent Claim
14 words
The process of claim 14 wherein the amine functional silane is gamma aminopropyltriethoxy silane.
References Cited (Backward Citations)
US2521672A
Cited
US2718512A
Cited
US3098833A
Cited
US3428706A
Cited
US3642693A
Cited
US3668180A
Cited
US3719634A
Cited
US3847848A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-09 | 1983-01-08 | 1983-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-09 | 1987-01-08 | 1987-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-09 | 1991-01-08 | 1991-07-10 | $7700.00 | Window Closed / Lapsed |