US4160703A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Nonplating cathode and method for producing same
Assignee: National Steel Corp
•
Filing: 1978-07-03
•
Granted: 1979-07-10
•
Expires: 1998-07-03
Abstract
Abstract A cathode, particularly a lead cathode, which is immune to plating zinc on its surface when used in an electrolytic galvanizing solution. The method of producing such a cathode which comprises placing the lead cathode in an electrolytic solution containing zinc ions, electrolytically forming a light zinc coating on the surface of the cathode, and removing the zinc coating from the surface of the cathode, preferably by interrupting the applied current for a sufficient period to permit the zinc coating to dissolve in the electrolytic solution.
Inventors
- 👤 Richard A. Bird
- 👤 Lowell W. Austin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:15
CPC Classifications
C; C25; C25D; C25D17/00; C25D17/10; C25D7/00; C25D7/06; C25D7/0614; C25D7/0657; C25F; C25F5/00; Y; Y10; Y10T; Y10T428/00; Y10T428/12
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
145 words
A method for producing metal strip material having a zinc coating only on one side comprising, (a) conditioning a lead cathode means so as to immunize it against plating zinc on its surface during an electrolytic operation, said conditioning including immersing the lead cathode means in a zinc ion-containing electrolytic bath, electrolytically causing a light zinc coating to form on the surface of the cathode means, and electrolytically or chemically removing said zinc coating from the cathode means, (b) immersing a zinc coated metal strip in said electrolytic bath and passing it through the electrolyte solution between anode means and the conditioned lead cathode means, and (c) electrolytically treating the strip so as to remove the zinc coating from the side of the strip facing the conditioned cathode means while simultaneously depositing a substantially equivalent amount of zinc on the opposite side of the strip.
Claim 2
Independent Claim
145 words
A method for producing metal strip material having a zinc coating only on one side comprising, (a) conditioning a lead cathode means so as to immunize it against plating zinc on its surface during an electrolytic operation, said conditioning including immersing the lead cathode means in a zinc ion-containing electrolytic bath, electrolytically causing a light zinc coating to form on the surface of the cathode means, and electrolytically or chemically removing said zinc coating from the cathode means, (b) immersing a zinc coated metal strip in said electrolytic bath and passing it through the electrolyte solution between anode means and the conditioned lead cathode means, and (c) electrolytically treating the strip so as to remove the zinc coating from the side of the strip facing the conditioned cathode means while simultaneously depositing a substantially equivalent amount of zinc on the opposite side of the strip.
Claim 3
Dependent Claim
32 words
A method according to claim 1 wherein said electrolytic bath includes between about 0.5 lbs./gal. to about 2.5 lbs./gal. of zinc sulfate and about 2 to about 10% by weight sulfuric acid.
Claim 4
Dependent Claim
44 words
A method as defined in claim 2 where in conditioning the lead cathode means, the light zinc coating is formed on the cathode means by applying about 6000 amps to the lead cathode means for a period between about 10 to about 15 minutes.
Claim 5
Dependent Claim
41 words
A method according to claim 1 where in conditioning the lead cathode means, the light zinc coating is removed from the cathode means by interrupting the current flow for a sufficient period to permit the zinc coating to dissolve in solution.
Claim 6
Dependent Claim
20 words
A method according to claim 4 wherein the current flow is interrupted for a period of at least 1 hour.
Claim 7
Dependent Claim
34 words
A method according to claim 5 wherein the current flow is re-applied at the end of said period and increased gradually to the current level required for effective electrolytic galvanizing of metal strip material.
Claim 8
Dependent Claim
39 words
A method according to claim 6 wherein said current is re-applied at 4000 amps, maintained at that level for 1 hour, and thereafter increased hourly at 2000 amp increments for 8 additional hours to a maximum of 20,000 amps.
References Cited (Backward Citations)
US3178305A
Cited
US3901771A
Cited
US3970537A
Cited
US3959099A
Cited
US3988216A
Cited
US3989604A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-09 | 1983-01-08 | 1983-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-09 | 1987-01-08 | 1987-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-09 | 1991-01-08 | 1991-07-10 | $7700.00 | Window Closed / Lapsed |