US4158719A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low expansion low resistivity composite powder metallurgy member and method of making the same
Assignee: CRS Holdings LLC
•
Filing: 1977-06-09
•
Granted: 1979-06-19
•
Expires: 1997-06-09
Abstract
Abstract A compacted article having low thermal expansivity and high thermal conductivity is made by compacting a mixture of two metal powders, one of which has low thermal expansivity and the other of which has high thermal conductivity, and strip material made therefrom which is suitable for use in forming the supportive lead frames in integrated circuit components. The powders are mixed together, formed into a green preform, sintered, and rolled to size to produce compacted or densified strip which has a unique combination of low thermal expansivity and high thermal conductivity. A low-expansivity metal disclosed in an alloy containing about 45-70% iron, 20-55% nickel, up to 25% cobalt, and up to 5% chromium which in powder form is mixed with a high-conductivity metal powder disclosed as substantially elemental iron, copper or nickel.
Inventors
- 👤 Earl L. Frantz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:02
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/40; H10W70/456; B; B22; B22F; B22F1/00; B22F1/09; C; C22; C22C; C22C33/00; C22C33/02; C22C33/0207; H10W70/01; H10W70/04; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/1216
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
165 words
A low thermal expansion, low electrical resistivity sintered, shaped electronic device member including a lead, comprising 15-85 volume percent of compacted particles of a first metal powder having an average thermal expansion coefficient over the range of 25° C. to 400° C. of less than about 12×10 -6 /°C., and the balance compacted particles of a second metal powder having an electrical resistivity of less than 200 ohm/cmf, said compacted particles of both powders being substantially intermixed throughout said member, with said second metal powder having a corresponding 400° C. thermal expansion coefficient greater than that of said first metal powder, said first metal powder having an electrical resistivity greater than that of said second metal powder, and the extent of alloying between the particles of said first and second metal powders being so small that said member has a 400° C. thermal expansion coefficient less than that of said second metal powder and an electrical resistivity less than that of said first metal powder.
Claim 2
Dependent Claim
165 words
A low thermal expansion, low electrical resistivity sintered, shaped electronic device member including a lead, comprising 15-85 volume percent of compacted particles of a first metal powder having an average thermal expansion coefficient over the range of 25° C. to 400° C. of less than about 12×10 -6 /°C., and the balance compacted particles of a second metal powder having an electrical resistivity of less than 200 ohm/cmf, said compacted particles of both powders being substantially intermixed throughout said member, with said second metal powder having a corresponding 400° C. thermal expansion coefficient greater than that of said first metal powder, said first metal powder having an electrical resistivity greater than that of said second metal powder, and the extent of alloying between the particles of said first and second metal powders being so small that said member has a 400° C. thermal expansion coefficient less than that of said second metal powder and an electrical resistivity less than that of said first metal powder.
Claim 3
Dependent Claim
19 words
The member of claim 1 comprising about 40-60 volume percent of the compacted particles of said first metal powder.
Claim 4
Dependent Claim
143 words
The member of claim 1 in which said first metal powder comprises by weight about 20 to 55% nickel, up to about 25% cobalt, up to about 5% chromium, and the balance iron, the iron content being about 45 to 70%; and in which said second metal powder is selected from the group consisting in weight percent of (a) elemental iron comprising up to about 10% chromium, up to about 10% nickel, up to about 5% copper, and the balance at least about 90% iron, (b) elemental copper comprising up to about 20% nickel, up to about 20% zinc, up to about 10% aluminum, up to about 3% of iron or beryllium, and the balance at least about 80% copper, and (c) elemental nickel comprising up to about 20% copper, up to about 20% iron, and the balance at least about 80% nickel.
Claim 5
Dependent Claim
38 words
The member of claim 3 wherein said first metal powder has a 400° C. thermal expansion coefficient of less than about 10×10 -6 /°C. and said second metal powder has an electrical resistivity of less than 100 ohm/cmf.
Claim 6
Dependent Claim
16 words
The member of claim 4 wherein said first metal powder contains about 35 to 52% nickel.
Claim 7
Dependent Claim
18 words
The member of claim 4 wherein said second metal powder is elemental iron containing at least 99% iron.
Claim 8
Dependent Claim
18 words
The member of claim 4 wherein said second metal powder is elemental copper containing at least 99% copper.
Claim 9
Dependent Claim
18 words
The member of claim 4 wherein said second metal powder is elemental nickel containing at least 99% nickel.
Claim 10
Dependent Claim
38 words
The member of claim 4 wherein the composition is balanced to provide a member with a 400° C. thermal expansion coefficient of less than about 12×10 -6 /°C. and an electrical resistivity of less than about 200 ohm/cmf.
Claim 11
Dependent Claim
28 words
The member of claim 9 wherein the composition is balanced to provide a member with a 400° C. thermal expansion coefficient of less than about 10×10 -6 /°C.
Claim 12
Dependent Claim
24 words
The member of claim 9 wherein the composition is balanced to provide a member with an electrical resistivity of less than about 150 ohm/cmf.
Claim 13
Dependent Claim
24 words
The member of claim 11 wherein the composition is balanced to provide a member with an electrical resistivity of less than about 150 ohm/cmf.
Claim 14
Dependent Claim
172 words
In a method for making a low thermal expansion, low electrical resistivity sintered, shaped electronic device member including a lead, the steps of making a mixture of about 15-85 volume percent of a first metal powder having an average thermal expansion coefficient over the range of 25° C. to 400° C. of less than about 12×10 -6 /°C. with the balance a second metal powder having an electrical resistivity of less than 200 ohm/cmf, said second metal powder having a corresponding 400° C. thermal expansion coefficient greater than that of said first metal powder, and said first metal powder having an electrical resistivity greater than that of said second metal powder; and sintering and forming said mixture to a sintered and shaped member while controlling the amount of alloying between the particles of said first and second metal powders so that said sintered shaped member has a 400° C. thermal expansion coefficient less than that of said second metal powder and an electrical resistivity less than that of said first metal powder.
Claim 15
Dependent Claim
172 words
In a method for making a low thermal expansion, low electrical resistivity sintered, shaped electronic device member including a lead, the steps of making a mixture of about 15-85 volume percent of a first metal powder having an average thermal expansion coefficient over the range of 25° C. to 400° C. of less than about 12×10 -6 /°C. with the balance a second metal powder having an electrical resistivity of less than 200 ohm/cmf, said second metal powder having a corresponding 400° C. thermal expansion coefficient greater than that of said first metal powder, and said first metal powder having an electrical resistivity greater than that of said second metal powder; and sintering and forming said mixture to a sintered and shaped member while controlling the amount of alloying between the particles of said first and second metal powders so that said sintered shaped member has a 400° C. thermal expansion coefficient less than that of said second metal powder and an electrical resistivity less than that of said first metal powder.
Claim 16
Dependent Claim
20 words
The method of claim 13 wherein said mixture is made of about 40-60 volume percent of said first metal powder.
Claim 17
Dependent Claim
143 words
The method of claim 13 in which said first metal powder comprises by weight about 20 to 55% nickel, up to about 25% cobalt, up to about 5% chromium, and the balance iron, the iron content being about 45 to 70%; and in which said second metal powder is selected from the group consisting in weight percent of (a) elemental iron comprising up to about 10% chromium, up to about 10% nickel, up to about 5% copper, and the balance at least about 90% iron, (b) elemental copper comprising up to about 20% nickel, up to about 20% zinc, up to about 10% aluminum, up to about 3% of iron or beryllium, and the balance at least about 80% copper, and (c) elemental nickel comprising up to about 20% copper, up to about 20% iron, and the balance at least about 80% nickel.
Claim 18
Dependent Claim
48 words
The method of claim 15 wherein forming said mixture includes applying pressure thereto to form a green preform, and densifying said preform by sintering at a temperature at least about 100° F. below the lower of the melting points of the two metal powders to form said member.
Claim 19
Dependent Claim
28 words
The method of claim 16 wherein said preform after being densified is cold rolled into strip, and then annealed at a temperature below that of said sintering temperature.
Claim 20
Dependent Claim
75 words
The method of claim 15 wherein said first metal powder has a 400° C. thermal expansion coefficient of less than about 10×10 -6 /°C. and said second metal powder has an electrical resistivity of less than 100 ohm/cmf, and wherein the composition of said member is balanced to provide said member with a 400° C. thermal expansion coefficient of less than about 12×10 -6 /°C. and an electrical resistivity of less than about 200 ohm/cmf.
Claim 21
Dependent Claim
16 words
The method of claim 18 wherein said first metal powder contains about 35 to 52% nickel.
Claim 22
Dependent Claim
18 words
The method of claim 18 wherein said second metal powder is elemental iron containing at least 99% iron.
Claim 23
Dependent Claim
18 words
The method of claim 18 wherein said second metal powder is elemental copper containing at least 99% copper.
Claim 24
Dependent Claim
18 words
The method of claim 18 wherein said second metal powder is elemental nickel containing at least 99% nickel.
Claim 25
Dependent Claim
28 words
The method of claim 18 wherein the composition is balanced to provide said member with a 400° C. thermal expansion coefficient of less than about 10×10 -6 /°C.
Claim 26
Dependent Claim
24 words
The method of claim 18 wherein the composition is balanced to provide said member with an electrical resistivity of less than about 150 ohm/cmf.
Claim 27
Dependent Claim
24 words
The method of claim 23 wherein the composition is balanced to provide said member with an electrical resistivity of less than about 150 ohm/cmf.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-18 | 1982-12-18 | 1983-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-18 | 1986-12-18 | 1987-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-18 | 1990-12-18 | 1991-06-19 | $7700.00 | Window Closed / Lapsed |