Composite metal as a contact material for vacuum switches
Assignee: Siemens AG
•
Filing: 1976-05-06
•
Granted: 1977-06-28
•
Expires: 1996-05-06
Abstract
Abstract A contact material for vacuum switches comprising a composite inclusion metal of at least two metal components in which a first component has an electric conductivity of at least 10 m/ohm mm 2 , the share of this component being between 35 and 60% by volume. At least one component has a melting point of at least 1400° C and at least one component is effective as a getter. These components are embedded in the first component, with only isolated bridges existing between the finely distributed inclusions. The porosity of the composite inclusion metal is less than 2% by volume.
Inventors
- 👤 Heinrich Hassler
- 👤 Horst Kippenberg
- 👤 Horst Schreiner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:57
CPC Classifications
H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/023; B; B22; B22F; B22F3/00; B22F3/12; B22F3/16; H01H1/0203; H01H33/00; H01H33/60; H01H33/66; H01H33/668; H01H33/6683; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/929; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/1216
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
173 words
A composite inclusion metal for vacuum switches comprising a mixture of copper as a first metal component in an amount from about 35% to 60% by volume of said composite inclusion metal, a second metal component selected from the group consisting of iron and nickel and a getter component selected from the group consisting of chromium, titanium and zirconium; wherein at least one of said second or getter components is embedded in said copper to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being formed by cold-pressing a mixture of said copper, said second metal component and said getter component to form a molding with a porosity of less than 30% by volume, sintering the molding at a temperature below the melting point of the lowest melting component of said mixture in a protective gas or vacuum, and hot-densifying the molding at a temperature below the melting point of the lowest melting component down to a residual porosity of less than 2% by volume.
Claim 2
Dependent Claim
173 words
A composite inclusion metal for vacuum switches comprising a mixture of copper as a first metal component in an amount from about 35% to 60% by volume of said composite inclusion metal, a second metal component selected from the group consisting of iron and nickel and a getter component selected from the group consisting of chromium, titanium and zirconium; wherein at least one of said second or getter components is embedded in said copper to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being formed by cold-pressing a mixture of said copper, said second metal component and said getter component to form a molding with a porosity of less than 30% by volume, sintering the molding at a temperature below the melting point of the lowest melting component of said mixture in a protective gas or vacuum, and hot-densifying the molding at a temperature below the melting point of the lowest melting component down to a residual porosity of less than 2% by volume.
Claim 3
Dependent Claim
24 words
The composite metal of claim 1, wherein the linear extent of the phase areas of the heterogeneous microstructure is between 10 and 250 um.
Claim 4
Dependent Claim
17 words
The composite metal of claim 1, wherein the share of the first component is 50% by volume.
Claim 5
Dependent Claim
138 words
A composite inclusion metal for vacuum switches comprising a mixture of copper or nickel as a first component in an amount of from 35 to 60% by volume of said composite, a second metal component consisting of aluminum wherein said second component is embedded in said first component to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being formed by cold-pressing a mixture of said components to form a molding with a porosity of less than 30% by volume, sintering the molding at a temperature below the melting point of the lowest-melting component of said mixture in a protective gas or vacuum and hot densifying the molding at a temperature below the melting point of the lowest-melting component down to a residual porosity of less than 2% by volume.
Claim 6
Dependent Claim
138 words
A composite inclusion metal for vacuum switches comprising a mixture of copper or nickel as a first component in an amount of from 35 to 60% by volume of said composite, a second metal component consisting of aluminum wherein said second component is embedded in said first component to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being formed by cold-pressing a mixture of said components to form a molding with a porosity of less than 30% by volume, sintering the molding at a temperature below the melting point of the lowest-melting component of said mixture in a protective gas or vacuum and hot densifying the molding at a temperature below the melting point of the lowest-melting component down to a residual porosity of less than 2% by volume.
Claim 7
Dependent Claim
20 words
The composite metal of claim 4, wherein the first component is copper or nickel and the second component is aluminum.
Claim 8
Dependent Claim
18 words
The composite metal of claim 4, wherein the first component is copper and the second component is nickel.
Claim 9
Dependent Claim
17 words
The composite inclusion metal of claim 4 which further comprises annealing the molding after the hot-densification step.
Claim 10
Dependent Claim
25 words
The composite inclusion metal of claim 4 wherein the linear extent of the phase areas of the heterogeneous microstructure is between 10 and 250 um.
Claim 11
Dependent Claim
24 words
The composite inclusion metal of claim 4, wherein the first component is present in an amount of about 50% by volume of the composite.
Claim 12
Dependent Claim
140 words
A composite inclusion metal of a mixture of copper and chromium wherein said copper is present in an amount of from 35 to 60% by volume, said chromium being embedded in said copper to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being prepared by mixing the copper and chromium in powder form, cold-pressing the mixture to form a molding with a porosity of less than 30% by volume, sintering the molding in a protective gas or vacuum, the sintering temperature being in the range of from above the melting temperature of said copper to a temperature not exceeding 100° C. above said melting temperature, and hot densifying the molding at a temperature below the melting point of the copper down to a residual porosity of less than 2% by volume.
Claim 13
Dependent Claim
140 words
A composite inclusion metal of a mixture of copper and chromium wherein said copper is present in an amount of from 35 to 60% by volume, said chromium being embedded in said copper to form a heterogeneous microstructure with only isolated bridge formations existing between finely-distributed inclusions, said composite inclusion metal being prepared by mixing the copper and chromium in powder form, cold-pressing the mixture to form a molding with a porosity of less than 30% by volume, sintering the molding in a protective gas or vacuum, the sintering temperature being in the range of from above the melting temperature of said copper to a temperature not exceeding 100° C. above said melting temperature, and hot densifying the molding at a temperature below the melting point of the copper down to a residual porosity of less than 2% by volume.
Claim 14
Dependent Claim
18 words
The composite inclusion metal method of claim 10 which further comprises annealing the molding after the hot-densification step.
References Cited (Backward Citations)
US2656595A
Cited
US2179960A
Cited
US2401221A
Cited
US3366463A
Cited
US3489530A
Cited
US3721550A
Cited
US3859087A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-27 | 1980-12-27 | 1981-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-27 | 1984-12-27 | 1985-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-27 | 1988-12-27 | 1989-06-28 | $7700.00 | Window Closed / Lapsed |