Pressure- and heat-sensitive coatings
Assignee: National Research Council Canada
•
Filing: 1977-12-19
•
Granted: 1979-06-19
•
Expires: 1997-12-19
Abstract
Abstract A composition for forming pressure- and heat-sensitive coatings comprising finely divided organic material of particle size from about 0.05 to 10 micrometers in diameter having a melting point above about 150 DEG C., the particles being of substantially uniform color and subject to plastic flow by heat or pressure, and a liquid carrier normally including a binder dispersed in the carrier to give a thixotropic gel. The composition optionally includes water-soluble or dispersible dye or a pigment uniformly dispersed in said particles. A method of preparing the compositions comprises precipitating the solid organic material in water, normally incorporating a binder, and optionally incorporating coloring material into the organic material to form a gel-type paste.
Inventors
- 👤 Frederick W. Meadus
- 👤 Ira E. Puddington
- 👤 Bryan D. Sparks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:32
CPC Classifications
C; C09; C09D; C09D131/00; C09D131/02; C09D131/04; B; B41; B41M; B41M5/00; B41M5/26; B41M5/36; B41M5/363; C09D133/00; C09D133/04; C09D133/06; C09D133/08; C08; C08L; C08L2205/00; C08L2205/14; C08L2205/18
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
208 words
A thixotropic composition, which on drying on a substrate forms a pressure- and heat-sensitive coating having voids of about 0.05 to 10 micrometers in diameter, comprising meldable metal soap particles of about 0.05 to 10 micrometers in diameter and having a cation selected from the group consisting of calcium, nickel, iron, copper, manganese, and lithium obtained as contiguous fine precipitated particles by double decomposition in water and having a melting point above about 150° C., the particles being of substantially uniform colour, that will provide a visible change from an opaque colour to a contrasting colour or transparent form when subjected to plastic flow or definite deformation by heat or pressure, water, being a liquid carrier for the precipitated soap, and a binder, dispersed or dissolved in the water to provide adhesion for the metal soap particles to a substrate without decreasing the pressure or heat deformability of the metal soap particles, the fatty acid of the soap being present in a concentration of about 7% to about 20% by weight and the binder being present in the composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, the lower proportions being used with the higher soap concentrations.
Claim 2
Dependent Claim
208 words
A thixotropic composition, which on drying on a substrate forms a pressure- and heat-sensitive coating having voids of about 0.05 to 10 micrometers in diameter, comprising meldable metal soap particles of about 0.05 to 10 micrometers in diameter and having a cation selected from the group consisting of calcium, nickel, iron, copper, manganese, and lithium obtained as contiguous fine precipitated particles by double decomposition in water and having a melting point above about 150° C., the particles being of substantially uniform colour, that will provide a visible change from an opaque colour to a contrasting colour or transparent form when subjected to plastic flow or definite deformation by heat or pressure, water, being a liquid carrier for the precipitated soap, and a binder, dispersed or dissolved in the water to provide adhesion for the metal soap particles to a substrate without decreasing the pressure or heat deformability of the metal soap particles, the fatty acid of the soap being present in a concentration of about 7% to about 20% by weight and the binder being present in the composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, the lower proportions being used with the higher soap concentrations.
Claim 3
Dependent Claim
20 words
The composition of claim 1 wherein the fatty acid of the metal soap has from 16 to 18 carbon atoms.
Claim 4
Dependent Claim
29 words
The aqueous coating composition of claim 2 wherein the fatty acid is chosen from stearic acid, palmitic acid and mixtures thereof, with at most, minor amounts of oleic acid.
Claim 5
Dependent Claim
19 words
The aqueous coating composition of claim 2 wherein the soap-forming cation is at least one of Ca and Ni.
Claim 6
Dependent Claim
24 words
The aqueous coating composition of claim 1, 2 or 3 wherein said precipitated particles are from about 1 to about 10 micrometers in diameter.
Claim 7
Dependent Claim
21 words
The aqueous coating composition of claim 1, wherein said precipitated particles are from about 0.5 to about 5 micrometers in diameter.
Claim 8
Dependent Claim
40 words
The aqueous coating composition of claim 1 wherein the binder is a mixture of (i) polyvinyl alcohol or alkaline salt of carboxymethylcellulose, as dispersant-binder (ii) as non-dispersant binder at least one of polyvinyl acetates, acrylic polymers and aminoplast condensation products.
Claim 9
Dependent Claim
57 words
The aqueous coating composition of claim 2 wherein the fatty acid concentration of the metal soap is from about 7.5 to about 12% by weight of the total dispersion and the binder is present in from about 100 to about 120% by weight of the fatty acid of the soap, the composition having an easily-spreadable paste consistency.
Claim 10
Dependent Claim
20 words
The aqueous coating composition of claim 1 having a total solids content of about 14 to about 40% by weight.
Claim 11
Dependent Claim
22 words
The aqueous coating composition of claim 1 wherein calcium stearate is the metal soap present in a major proportion of total soap.
Claim 12
Dependent Claim
22 words
The aqueous coating composition of claim 1 wherein nickel stearate is the metal soap present in a major proportion of total soap.
Claim 13
Dependent Claim
183 words
A pressure- and heat-sensitive coating or layer having an opaque highly compactible open porous continuous matrix structure of contiguous fine light-scattering meldable metal soap particles and fine light-scattering open voids; the particles and voids each being about 0.05 to 10 micrometers in diameter, the particles being obtained as a precipitate by double decomposition in water and having a melting point above about 150° C., the particles being of substantially uniform opaque colour that will provide a visible change to a contrasting colour or transparent form when subjected to plastic flow or deformation by heat or pressure and a binder providing adhesion for the metal soap particles to a substrate while allowing satisfactory pressure- or heat-deformability of the metal soap particles, the fatty acid of the soap having been present in a concentration of about 7% to about 20% by weight in the coating composition before deposition and the binder being present in the composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, the lower proportions being used with the higher soap concentrations.
Claim 14
Dependent Claim
183 words
A pressure- and heat-sensitive coating or layer having an opaque highly compactible open porous continuous matrix structure of contiguous fine light-scattering meldable metal soap particles and fine light-scattering open voids; the particles and voids each being about 0.05 to 10 micrometers in diameter, the particles being obtained as a precipitate by double decomposition in water and having a melting point above about 150° C., the particles being of substantially uniform opaque colour that will provide a visible change to a contrasting colour or transparent form when subjected to plastic flow or deformation by heat or pressure and a binder providing adhesion for the metal soap particles to a substrate while allowing satisfactory pressure- or heat-deformability of the metal soap particles, the fatty acid of the soap having been present in a concentration of about 7% to about 20% by weight in the coating composition before deposition and the binder being present in the composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, the lower proportions being used with the higher soap concentrations.
Claim 15
Dependent Claim
39 words
The coating of claim 12 wherein the metal soap particles have a cation selected from the group consisting of calcium, nickel, iron, copper, and lithium and fatty acid of the metal soap has from 16 to 18 carbon atoms.
Claim 16
Dependent Claim
34 words
The coating of claim 12 wherein the binder is a non-waxy, water soluble or water-dispersible binder selected from the group consisting of polyvinyl alcohols, polyvinyl acetates, acrylic polymers, aminoplast condensation products and mixtures thereof.
Claim 17
Dependent Claim
14 words
The coating of claim 12 wherein the metal soap comprises a stearate or hydroxystearate.
Claim 18
Dependent Claim
12 words
The coating of claim 12 wherein the metal soap comprises an oleate.
Claim 19
Dependent Claim
12 words
The coating of claim 12 wherein the metal soap comprises a palmitate.
Claim 20
Dependent Claim
25 words
The coating of claim 12 wherein the weight ratio of fatty acid of the soap to binder is in the range of 1:0.7 to 1:1.2.
Claim 21
Dependent Claim
26 words
The coating of claim 12 wherein the coating has a light colour adapted to yield a dark version of the same colour on application of pressure.
Claim 22
Dependent Claim
39 words
The coating of claim 12 wherein the binder is a mixture of (i) polyvinyl alcohol or alkaline salt of carboxy:methylcellulose, as dispersant-binder and (ii) as non-dispersant binder at least one of polyvinyl acetates, acrylic polymers and aminoplast condensation products.
Claim 23
Dependent Claim
10 words
The coating of claim 12 further comprising dye or pigment.
Claim 24
Dependent Claim
11 words
The coating of claim 12 further comprising titanium dioxide as pigment.
Claim 25
Independent Claim
113 words
A method of preparing an aqueous coating composition of high solids content suitable for deposition of pressure- and heat-sensitive coatings which comprises: forming an aqueous solution of a sodium, potassium or ammonium soap, adding metal cations selected from the group consisting of calcium, nickel, iron, copper, and lithium to the aqueous solution so that a precipitate of the soap of said cation is formed, providing a water-soluble or -dispersible binder in the aqueous composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, and providing that the total solids content is within 14 to 40% by weight for spreading application onto a substrate.
Claim 26
Independent Claim
113 words
A method of preparing an aqueous coating composition of high solids content suitable for deposition of pressure- and heat-sensitive coatings which comprises: forming an aqueous solution of a sodium, potassium or ammonium soap, adding metal cations selected from the group consisting of calcium, nickel, iron, copper, and lithium to the aqueous solution so that a precipitate of the soap of said cation is formed, providing a water-soluble or -dispersible binder in the aqueous composition in a proportion of from about 40 to about 120% by weight of the fatty acid of the soap, and providing that the total solids content is within 14 to 40% by weight for spreading application onto a substrate.
Claim 27
Dependent Claim
22 words
The method of claim 23 wherein the cation is added to the aqueous solution as an aqueous solution of the metal halide.
Claim 28
Dependent Claim
19 words
The method of claim 23 wherein the metal cation is added in an amount two times the stoichiometric amount.
Claim 29
Dependent Claim
28 words
The method of claim 23 wherein the formation of said initial aqueous solution of soap is by the addition of ammonium hydroxide to a fatty acid water mixture.
Claim 30
Dependent Claim
33 words
The method of claim 26 wherein ammonium hydroxide is added to stearic acid in water followed by the addition of the chloride of said metal to give the precipitate of said metal stearate.
References Cited (Backward Citations)
US1293983A
Cited
US1819078A
Cited
US1830980A
Cited
US2313808A
Cited
US2313810A
Cited
US3619157A
Cited
US3967034A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-18 | 1982-12-18 | 1983-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-18 | 1986-12-18 | 1987-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-18 | 1990-12-18 | 1991-06-19 | $7700.00 | Window Closed / Lapsed |