Bonded, differentially creped, fibrous webs and method and apparatus for making same
Assignee: Kimberly Clark Tissue Co
•
Filing: 1971-06-24
•
Granted: 1979-06-19
•
Expires: 1991-06-24
Abstract
Abstract A method is disclosed for forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, by formimg a web of cellulosic fibers having a basis weight of from about 5 to about 55 pounds per ream of 2,880 square feet, adhering one surface of the web to a creping surface in a fine pattern arrangement by a bonding material adhered to one surface of the web and to the creping surface in the fine pattern arrangement, and creping the web from the creping surface to form the sheet material. Sheet materials formed by the above method are also disclosed.
Inventors
- 👤 Henry E. Becker
- 👤 Albert L. McConnell
- 👤 Richard W. Schutte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:21
CPC Classifications
B; B31; B31F; B31F1/00; B31F1/12; B31F1/126; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24446; Y10T428/24455; Y10T428/24802
Claims Analysis
Total Claims: 60
Claim 1
Independent Claim
168 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web from said creping surface to form said sheet material.
Claim 2
Independent Claim
168 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web from said creping surface to form said sheet material.
Claim 3
Dependent Claim
21 words
A method of forming sheet material according to claim 1, wherein said bonding material is applied to said web by printing.
Claim 4
Dependent Claim
24 words
A method of forming sheet material according to claim 1, wherein only said bonded portions of said web are adhered to said creping surface.
Claim 5
Dependent Claim
18 words
A method of forming sheet material according to claim 1, wherein said bonding material is an elastomeric material.
Claim 6
Dependent Claim
21 words
A method of forming sheet material according to claim 1, wherein said bonding material imparts structural integrity to said sheet material.
Claim 7
Dependent Claim
32 words
A method of forming sheet material according to claim 1, wherein said bonding material is applied to said web in a continuous predetermined reticular pattern which forms a net-like web of strength.
Claim 8
Dependent Claim
36 words
A method of forming sheet material according to claim 1, wherein said bonding material forms bonded web portions in said sheet material which have greater strength than the portions of the web not having bonding material.
Claim 9
Dependent Claim
31 words
A method of forming sheet material according to claim 1, wherein said creping shortens said web from about 10% to about 20% of its machine direction length before said creping step.
Claim 10
Dependent Claim
25 words
The method as defined in claim 1, further comprising the step of processing the sheet material into a sanitary paper tissue adapted for wiping purposes.
Claim 11
Dependent Claim
21 words
The method as defined by claim 9, wherein said sanitary paper tissue adapted for wiping purposes essentially consists of bathroom tissue.
Claim 12
Dependent Claim
21 words
The method as defined by claim 9, wherein said sanitary paper tissue adapted for wiping purposes essentially consists of paper towels.
Claim 13
Dependent Claim
13 words
The method as defined by claim 10, wherein said bathroom tissue is single-ply.
Claim 14
Dependent Claim
13 words
The method as defined by claim 10, wherein said bathroom tissue is two-ply.
Claim 15
Dependent Claim
13 words
The method as defined by claim 11, wherein said paper towels are single-ply.
Claim 16
Dependent Claim
13 words
The method as defined by claim 11, wherein said paper towels are two-ply.
Claim 17
Dependent Claim
32 words
The method as defined by claim 1, said strong, soft, fibrous sheet material having an average calculated density throughout its thickness under no load of less than 0.300 grams per cubic centimeter.
Claim 18
Dependent Claim
23 words
The method as defined by claim 16, said strong, soft, fibrous sheet material having a TEA-to-stiffness ratio of greater than 1.50×10 -4 .
Claim 19
Dependent Claim
27 words
The method as defined by claim 1, said web having a basis weight of from about 10 to about 30 lbs. per ream of 2880 square feet.
Claim 20
Dependent Claim
23 words
The method as defined by claim 1, said web comprising up to about 50% by weight of natural or synthetic textile length fibers.
Claim 21
Dependent Claim
48 words
The method as defined by claim 19, wherein said natural or synthetic textile length fibers have a length of up to about 21/2 inches, and are selected from the group consisting of cotton, wool, rayon, regenerated cellulose, cellulose ester, polyamide, acrylic, polyester, vinyl, protein, fluorocarbon, dinitrile and nitrile.
Claim 22
Dependent Claim
40 words
The method as defined by claim 1, said strong, soft, fibrous sheet material displaying stretch in the machine direction of from about 14 to about 30% and stretch in the cross machine direction of from about 5 to about 17%.
Claim 23
Dependent Claim
42 words
The method as defined by claim 1, wherein said bonding material comprises a mixture of ingredients, certain ingredients having the ability to effect the interfiber bonding and certain ingredients having the ability to effect adherence of the web to the creping surface.
Claim 24
Dependent Claim
52 words
The method as defined by claim 1, wherein said web is formed by deposition from an aqueous slurry of predominantly cellulosic or lignocellulosic fibers and including the step of treating such fibers with a chemical debonding agent prior to formation of said web therefrom, so as to reduce their interfiber bonding capacity.
Claim 25
Dependent Claim
17 words
The method as defined by claim 23, wherein said chemical debonding agent is a cationic debonding agent.
Claim 26
Dependent Claim
45 words
The method as defined by claim 24, wherein said cationic debonding agent is selected from the group consisting of a fatty dialkyl quaternary amine salt, amino fatty alkyl tertiary amine salt, primary amine salt, unsaturated fatty alkylamine salt, tertiary amine oxide and a cation-active amine.
Claim 27
Dependent Claim
45 words
The method as defined by claim 1, wherein said web is formed by deposition from an aqueous slurry of predominantly lignocellulosic fibers under conditions of reduced pressing until it is substantially dried, whereby the amount of interfiber contact and its interfiber bonding strength is reduced.
Claim 28
Dependent Claim
66 words
The method as defined by claim 1, wherein said creping step effects shrinking of said bonded web portions, thereby creating compression in the plane of the web and in the direction of shrinkage in portions of said web intermediate said bonded web portions, whereby web portions intermediate said bonded web portions form raised arched areas to give the web a puffed appearance and an increased bulk.
Claim 29
Dependent Claim
25 words
The method as defined by claim 1, wherein said sheet material, following said creping step, is split internally, in the general plane of the web.
Claim 30
Dependent Claim
22 words
The method as defined by claim 1, wherein said web is formed by deposition from a gaseous suspension of predominantly cellulosic fibers.
Claim 31
Independent Claim
147 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominated of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 pounds per ream of 2880 square feet, applying a bonding material which includes a curable component to one surface of said web in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded web portions in said sheet material in which fibers are bonded together by said bonding material, adhering with said bonding material said bonded web portions to a creping surface, creping said web from said creping surface to form said sheet material, and curing said curable component in said bonding material after creping said web.
Claim 32
Independent Claim
147 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominated of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 pounds per ream of 2880 square feet, applying a bonding material which includes a curable component to one surface of said web in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded web portions in said sheet material in which fibers are bonded together by said bonding material, adhering with said bonding material said bonded web portions to a creping surface, creping said web from said creping surface to form said sheet material, and curing said curable component in said bonding material after creping said web.
Claim 33
Independent Claim
180 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight from about 5 to 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, bringing said one surface of said web into engagement with a creping surface to adhere said bonded portions to said creping surface by said bonding material, and differentially creping said web from said creping surface to form said sheet material.
Claim 34
Independent Claim
180 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight from about 5 to 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, bringing said one surface of said web into engagement with a creping surface to adhere said bonded portions to said creping surface by said bonding material, and differentially creping said web from said creping surface to form said sheet material.
Claim 35
Dependent Claim
42 words
The method as defined by claim 1, further including the step of creping said web of cellulosic fibers over its entire surface so as to disrupt and break interfiber bonds by creping action before the bonding material is applied to the web.
Claim 36
Independent Claim
181 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, said bonding material penetrating said web generally only part way through the thickness of said web, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web creping surface to form said sheet material.
Claim 37
Independent Claim
181 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web predominantly of cellulosic fibers having a length of less than 1/4 inch to have a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, said bonding material penetrating said web generally only part way through the thickness of said web, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web creping surface to form said sheet material.
Claim 38
Independent Claim
260 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions interfiber its own plane, comprising: (i) providing a web which comprises a matrix of cellulosic fibers, said web being characterized by such reduced inter-fiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily cellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material penetrating said web at least part way through the thickness of said web, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, and (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type.
Claim 39
Independent Claim
260 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions interfiber its own plane, comprising: (i) providing a web which comprises a matrix of cellulosic fibers, said web being characterized by such reduced inter-fiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily cellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material penetrating said web at least part way through the thickness of said web, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, and (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type.
Claim 40
Dependent Claim
24 words
The method as defined by claim 34, wherein said bonding material is an elastomeric bonding material capable of at least 75% elongation without rupture.
Claim 41
Dependent Claim
35 words
The method as defined in claim 34, wherein said elastomeric materials are selected from the group consisting of butadiene/acrylonitrile, natural or synthetic rubber latices or dispersions thereof, butadiene-styrene, neoprene, polyvinyl chloride, vinyl copolymers and nylon.
Claim 42
Dependent Claim
36 words
The method as defined in claim 34, wherein said bonding material is selected from the group consisting of acrylic latex rubber emulsion, acrylate emulsion, vinyl acetate emulsion, vinyl chloride emulsion, methacrylate emulsion, carboxymethylcellulose, polyvinylalcohol and polyacrylamide.
Claim 43
Dependent Claim
18 words
The method as defined by claim 34, wherein said bonding material is applied to said web by printing.
Claim 44
Dependent Claim
29 words
The method as defined by claim 34 wherein said bonding material is applied to said web in a continuous predetermined reticular pattern which forms a net-like web of strength.
Claim 45
Dependent Claim
27 words
The method as defined by claim 34, wherein said creping shortens said web from about 10 to 20% of its machine direction length before said creping step.
Claim 46
Dependent Claim
46 words
The method as defined by claim 34, wherein said step (i) web has inadequate structural integrity by reason of having been creped over its entire surface so as to disrupt and break interfiber bonds by such creping action, prior to the bonding material application step (ii).
Claim 47
Dependent Claim
42 words
The method as defined by claim 34, wherein said web is formed by deposition from an aqueous slurry of cellulosic or lignocellulosic fibers to have a basis weight of from about 10 to about 30 lbs. per ream of 2880 square feet.
Claim 48
Dependent Claim
21 words
The method as defined by claim 34, wherein said fine pattern of applied bonding material is a pattern of parallel lines.
Claim 49
Dependent Claim
20 words
The method as defined by claim 34, wherein said fine pattern of applied bonding material is a pattern of bars.
Claim 50
Dependent Claim
21 words
The method as defined by claim 34, wherein said fine pattern of applied bonding material is a pattern of discrete areas.
Claim 51
Dependent Claim
24 words
The method as defined by claim 33, wherein step (ii) said bonding material penetrates said web generally only part way through the thickness thereof.
Claim 52
Dependent Claim
24 words
The method as defined by claim 33, wherein said web is formed by deposition from a gaseous suspension of predominantly cellulosic or lignocellulosic fibers.
Claim 53
Independent Claim
309 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: (i) providing a web which comprises a matrix of lignocellulosic fibers, said web being characterized by very little interfiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily lignocellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material penetrating said web at least part way through the thickness of said web and said interfiber bonding amount thereof being in excess of that amount required for the below step (iii) of adhering to a creping surface, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, and (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type, and whereby the very little interfiber bonding strength of the web is maintained, except for that created by the bonding material in the bonded areas.
Claim 54
Independent Claim
309 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: (i) providing a web which comprises a matrix of lignocellulosic fibers, said web being characterized by very little interfiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily lignocellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material penetrating said web at least part way through the thickness of said web and said interfiber bonding amount thereof being in excess of that amount required for the below step (iii) of adhering to a creping surface, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, and (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type, and whereby the very little interfiber bonding strength of the web is maintained, except for that created by the bonding material in the bonded areas.
Claim 55
Independent Claim
167 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: providing a web predominantly of cellulosic fibers having a length of less than 1/4 inch and a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web from said creping surface to form said sheet material.
Claim 56
Independent Claim
167 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: providing a web predominantly of cellulosic fibers having a length of less than 1/4 inch and a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material, adhering with said bonding material said bonded portions to a creping surface, and differentially creping said web from said creping surface to form said sheet material.
Claim 57
Independent Claim
209 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web by deposition from an aqueous slurry of lignocellulosic fibers to have a basis weight of from about 10 to about 30 lbs./ream of 2,880 square feet, said web formed under conditions of reduced pressing until substantially dried to reduce the amount of interfiber contact and interfiber bonding strength in the web, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a continuous reticular, fine pattern which leaves at least 65% of said surface of said web free from said bonding material, said bonding material penetrating only partly into the thickness of said web to form bonded web portions in said sheet material in which fibers are bonded together by said bonding material, bringing said one surfface of said web into engagement with a creping surface to adhere only said bonded web portions to said creping surface with said bonding material, and creping said web from said creping surface to form said sheet material.
Claim 58
Independent Claim
209 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: forming a web by deposition from an aqueous slurry of lignocellulosic fibers to have a basis weight of from about 10 to about 30 lbs./ream of 2,880 square feet, said web formed under conditions of reduced pressing until substantially dried to reduce the amount of interfiber contact and interfiber bonding strength in the web, applying a bonding material to one surface of said web in a quantity to result in said sheet material having at least about 1.4% non-volatile constituents of bonding material based on the dry web weight of said sheet material, and in a continuous reticular, fine pattern which leaves at least 65% of said surface of said web free from said bonding material, said bonding material penetrating only partly into the thickness of said web to form bonded web portions in said sheet material in which fibers are bonded together by said bonding material, bringing said one surfface of said web into engagement with a creping surface to adhere only said bonded web portions to said creping surface with said bonding material, and creping said web from said creping surface to form said sheet material.
Claim 59
Independent Claim
248 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: (i) providing a web which comprises a matrix of cellulosic fibers, said web being characterized by such reduced interfiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily cellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material including a curable component and penetrating said web at least part way through the thickness of said web, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type, and (v) curing said curable component in said bonding material after creping said web.
Claim 60
Independent Claim
248 words
A method of forming a strong, soft, fibrous sheet material having substantial stretch in all directions in its own plane, comprising: (i) providing a web which comprises a matrix of cellulosic fibers, said web being characterized by such reduced interfiber bonding strength as to have inadequate structural integrity for sanitary wiping purposes, and said web being primarily cellulosic fibers having a length of less than 1/4 inch and having a basis weight of from about 5 to about 55 lbs. per ream of 2880 square feet, (ii) applying an interfiber bonding amount of bonding material to one surface of said web in a fine pattern which leaves a substantial portion of said surface of said web free from said bonding material, to form bonded portions in said sheet material in which fibers are bonded together by said bonding material to contribute to the strength of said sheet material and impart structural integrity thereto, said bonding material including a curable component and penetrating said web at least part way through the thickness of said web, (iii) adhering with said bonding material said bonded portions of said web to a creping surface, (iv) differentially creping said web from said creping surface to form said sheet material having structural integrity imparted by said bonding material, which interfiber bonding amount of bonding material effects formation of essentially no hard or brittle interfiber bonds of natural interfiber bonding type, and (v) curing said curable component in said bonding material after creping said web.
References Cited (Backward Citations)
USRE17633E
Cited
US2161092A
Cited
US2143911A
Cited
US2610935A
Cited
US3047444A
Cited
US2996424A
Cited
US3009822A
Cited
US3059313A
Cited
US2960089A
Cited
US3255064A
Cited
US3395708A
Cited
US3597306A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-18 | 1982-12-18 | 1983-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-18 | 1986-12-18 | 1987-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-18 | 1990-12-18 | 1991-06-19 | $7700.00 | Window Closed / Lapsed |