Method of fabricating a high electrical frequency infrared detector by vacuum deposition
Assignee: United States Department of the Navy
•
Filing: 1978-06-22
•
Granted: 1979-06-12
•
Expires: 1998-06-22
Abstract
Abstract A thin-film single-crystal infrared detector exhibiting an increased frequency of response. A closed transverse junction, formed by diffusing a central electrode of an impurity rich metal into a lead-salt film epitaxially grown on an insulating substrate, provides an effective optical area in excess of the junction surface. An ohmic contact is spaced apart from the central electrode. Junction capacitance, a limitation upon the electrical response, is diminished by the detector geometry while detectivity is enhanced. In an alternative embodiment the detector may be segmented to provide directional detection.
Inventors
- 👤 Richard B. Schoolar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:22
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/12; H10F77/127; Y; Y10; Y10S; Y10S438/00; Y10S438/93
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
135 words
A method of making a photovoltaic detector, comprising the steps of: depositing in a vacuum chamber at an elevated temperature an epitaxial layer of semiconductor material having a first type conductivity upon an electrically insulating crystalline substrate, whereby the epitaxial layer has two major opposed surfaces being respectively, the top and the substrate-mating surfaces; the material being selected from the Group consisting of: lead salts, lead tin salts, lead cadmium salts, cadmium salts, or alloys thereof; cooling the crystalline substrate and epitaxial layer; depositing upon an undefined portion of the top surface a non-ohmic electrical contact of a metal rich in a second and opposite type conductivity impurity; and, thermally treating the resulting product to bring about diffusion of said second and opposite type conductivity impurities through to the substrate-mating surface of said epitaxial layer.
Claim 2
Independent Claim
135 words
A method of making a photovoltaic detector, comprising the steps of: depositing in a vacuum chamber at an elevated temperature an epitaxial layer of semiconductor material having a first type conductivity upon an electrically insulating crystalline substrate, whereby the epitaxial layer has two major opposed surfaces being respectively, the top and the substrate-mating surfaces; the material being selected from the Group consisting of: lead salts, lead tin salts, lead cadmium salts, cadmium salts, or alloys thereof; cooling the crystalline substrate and epitaxial layer; depositing upon an undefined portion of the top surface a non-ohmic electrical contact of a metal rich in a second and opposite type conductivity impurity; and, thermally treating the resulting product to bring about diffusion of said second and opposite type conductivity impurities through to the substrate-mating surface of said epitaxial layer.
Claim 3
Dependent Claim
70 words
The method set forth in claim 1 wherein the semiconductor material is selected from the group consisting of: lead telluride (PbTe), lead selenide (PbSe), lead sulfide (PbS), cadmium sulfide (CdS), cadmium selenide (CdSe), lead cadmium sulfide (PbCdS), lead tin telluride (Pb x Sn 1-x Te), lead tin selenide (Pb y Sn 1-y Se), lead tin sulfide (Pb z Sn 1-z S), or alloys thereof, where: ≦ x≦1, 0.4≦y≦1, and 0.8≦z≦1.
Claim 4
Dependent Claim
28 words
The method set forth in claim 1, further comprising: ceasing deposition of the semiconductor material before the epitaxial layer attains a thickness greater than twelve hundred angstrom units.
Claim 5
Dependent Claim
21 words
The method set forth in claim 1 further comprising: depositing the electrical contact when the epitaxial layer is at room temperature.
Claim 6
Dependent Claim
28 words
The method set forth in claim 1, further comprising: ceasing deposition of the semiconductor material before the epitaxial layer attains a thickness greater than five hundred angstrom units.
Claim 7
Dependent Claim
21 words
The method set forth in claim 5, further comprising: depositing the electrical contact when the epitaxial layer is at room temperature.
References Cited (Backward Citations)
US3146138A
Cited
US3502517A
Cited
US3433677A
Cited
US3515957A
Cited
US3454847A
Cited
US3614661A
Cited
US3616527A
Cited
US3716424A
Cited
US3904879A
Cited
US3961998A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-11 | 1982-12-11 | 1983-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-11 | 1986-12-11 | 1987-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-11 | 1990-12-11 | 1991-06-12 | $7700.00 | Window Closed / Lapsed |