Stabilized insulating latex paint composition and method of manufacture
Assignee: Individual
•
Filing: 1978-02-07
•
Granted: 1979-05-22
•
Expires: 1998-02-07
Abstract
Abstract Disclosed herein is a latex coating composition containing from 10 to 30% by weight of a porous particulate material such as perlite and from 2 to 4% by weight of a stabilizer blend comprising from 20 to 65% by weight of said blend of a biosynthetic polysaccharide, from 35 to 80% by weight of said blend of a finely divided inorganic filler and from 0 to 35% by weight of a cellulosic agent. The coating composition exhibits excellent insulating properties and does not shrink during storage. The method of preparing the paint composition is also disclosed.
Inventors
- 👤 George W. Hetson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 01:03
CPC Classifications
C; C09; C09D; C09D105/00; C08; C08K; C08K3/00; C08K3/34; C08K7/00; C08K7/22; C08K7/24; C08K7/26; C08L; C08L1/00; C08L1/08; C08L1/26; C08L1/28; C08L1/284; C08L5/00
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
37 words
A textured insulating latex paint composition comprising water, a film-forming binder, a porous solid material uniformly dispersed in said composition and a stabilizer blend, said stabilizer blend comprising a polysaccharide and a finely divided inorganic thixotropic additive.
Claim 2
Dependent Claim
37 words
A textured insulating latex paint composition comprising water, a film-forming binder, a porous solid material uniformly dispersed in said composition and a stabilizer blend, said stabilizer blend comprising a polysaccharide and a finely divided inorganic thixotropic additive.
Claim 3
Dependent Claim
14 words
The paint composition of claim 1 wherein said stabilizer blend comprises a cellulosic agent.
Claim 4
Dependent Claim
21 words
The paint composition of claim 1 wherein said stabilizer blend comprises from 2 to 4% by weight of said paint composition.
Claim 5
Dependent Claim
24 words
The paint composition of claim 3 wherein said porous solid material comprises from about 10 to about 30% by weight of said paint composition.
Claim 6
Dependent Claim
45 words
The paint composition according to claim 4 wherein said stabilizer blend comprises from about 20 to about 65% by weight of said polysaccharide, from 35 to about 80% by weight of said inorganic additive and from 0 to 35% by weight of a cellulosic agent.
Claim 7
Dependent Claim
25 words
The paint composition of claim 5 wherein said polysaccharide comprises a hetero polysaccharide containing D-glucose, D-mannose and D-glucuronate in the molar ratio of about 2.8:2.0:2.0.
Claim 8
Dependent Claim
14 words
The paint composition of claim 6 wherein said cellulosic agent is hydroxy propymethyl cellulose.
Claim 9
Dependent Claim
15 words
The paint composition of claim 7 wherein said inorganic additive is colloidal magnesium aluminum silicate.
Claim 10
Dependent Claim
36 words
The paint composition of claim 8 wherein said stabilizer blend comprises 25% by weight of said hetero polysaccharide, 27% by weight of said hydroxy propylmethyl cellulose and 48% by weight of said colloidal magnesium aluminum silicate.
Claim 11
Dependent Claim
13 words
The paint composition according to claim 9 wherein said porous material is perlite.
Claim 12
Dependent Claim
20 words
The paint composition according to claim 10 wherein said film-forming binder is a copolymer of butyl acrylate and vinyl acetate.
Claim 13
Dependent Claim
24 words
The paint composition according to claim 11 wherein said stabilizer blend comprises from about 2.5 to about 3.5% by weight of said paint composition.
Claim 14
Dependent Claim
17 words
The paint composition of claim 12 wherein said stabilizer blend comprises 3.2% by weight of said composition.
Claim 15
Dependent Claim
79 words
A textured insulating paint composition comprising a film-forming resin binder, water, a pigment, approximately 20% by weight of perlite, 3.2% by weight of said paint composition of a stabilizer blend comprising 25% by weight of a biosynthetic hetero polysaccharide containing D-glucose, D-mannose and D-glucuronate in the molar ratio of 2.8:2.0:2.0, 27% by weight of hydroxy methyl propyl cellulose, and 48% by weight of colloidal magnesium aluminum silicate said composition having a density of less than 9 pounds per gallon.
Claim 16
Dependent Claim
79 words
A textured insulating paint composition comprising a film-forming resin binder, water, a pigment, approximately 20% by weight of perlite, 3.2% by weight of said paint composition of a stabilizer blend comprising 25% by weight of a biosynthetic hetero polysaccharide containing D-glucose, D-mannose and D-glucuronate in the molar ratio of 2.8:2.0:2.0, 27% by weight of hydroxy methyl propyl cellulose, and 48% by weight of colloidal magnesium aluminum silicate said composition having a density of less than 9 pounds per gallon.
Claim 17
Independent Claim
89 words
A method of preparing a textured, insulating surface coating which comprises mixing water with one or more surface tension lowering agents to reduce the surface tension of said water to a predetermined value, forming a slurry with said low surface tension water and a porous particulate solid, mixing said slurry to permit said water to penetrate throughout the pores of said solid, combining said slurry with a stabilizing composition comprising a polysaccharide and a finely divided thixotropic thickening material, combining said stabilized aqueous solution with a paint film-forming binder.
Claim 18
Independent Claim
89 words
A method of preparing a textured, insulating surface coating which comprises mixing water with one or more surface tension lowering agents to reduce the surface tension of said water to a predetermined value, forming a slurry with said low surface tension water and a porous particulate solid, mixing said slurry to permit said water to penetrate throughout the pores of said solid, combining said slurry with a stabilizing composition comprising a polysaccharide and a finely divided thixotropic thickening material, combining said stabilized aqueous solution with a paint film-forming binder.
Claim 19
Dependent Claim
13 words
The method of claim 15 wherein said stabilizing blend includes a cellulosic agent.
Claim 20
Dependent Claim
28 words
The method of claim 16 which comprises forming said stabilizing blend, in situ, in said aqueous slurry by sequentially adding the components of said blend to said slurry.
Claim 21
Dependent Claim
25 words
The method of claim 16 which comprises combining the constituents of said stabilizing blend separately and prior to admixing said blend with said aqueous slurry.
Claim 22
Dependent Claim
48 words
The method according to claim 17 wherein said stabilizing blend comprises from about 20 to about 65% by weight of said polysaccharide, from about 35 to about 80% by weight of said finely divided thixotropic solid, and from 0 to about 35% by weight of said cellulosic agent.
Claim 23
Independent Claim
89 words
A method of stabilizing the density of a latex paint composition containing a porous finely divided solid material dispersed in a composition comprising a film-forming binder, water and a pigment which comprises incorporating in said composition a stabilizing blend containing from about 20 to about 65% by weight of said blend of a xanthan polysaccharide, from about 35 to about 80% by weight of said blend of a finely divided inorganic thixotropic particulate solid, and between 0 and about 35% by weight of said blend of a cellulosic agent.
Claim 24
Independent Claim
89 words
A method of stabilizing the density of a latex paint composition containing a porous finely divided solid material dispersed in a composition comprising a film-forming binder, water and a pigment which comprises incorporating in said composition a stabilizing blend containing from about 20 to about 65% by weight of said blend of a xanthan polysaccharide, from about 35 to about 80% by weight of said blend of a finely divided inorganic thixotropic particulate solid, and between 0 and about 35% by weight of said blend of a cellulosic agent.
Claim 25
Dependent Claim
51 words
A stabilizer blend for a latex paint composition containing porous particulate materials which comprises from about 20 to about 65% by weight of a xanthan polysaccharide, from about 35 to about 80% by weight of a finely divided thixotropic solid, and 0 to about 35% by weight of a cellulosic agent.
Claim 26
Dependent Claim
51 words
A stabilizer blend for a latex paint composition containing porous particulate materials which comprises from about 20 to about 65% by weight of a xanthan polysaccharide, from about 35 to about 80% by weight of a finely divided thixotropic solid, and 0 to about 35% by weight of a cellulosic agent.
Claim 27
Dependent Claim
13 words
The paint composition according to claim 9 wherein said porous material is vermiculite.
Claim 28
Dependent Claim
31 words
The paint composition according to claim 1 wherein said porous material comprises finely divided particles of a water insoluble material having a particle size between 200 mesh and about 1/8 inch.
Claim 29
Dependent Claim
15 words
The paint composition according to claim 1 wherein said porous material comprises expanded resin beads.
Claim 30
Dependent Claim
12 words
The paint composition according to claim 5 which further comprises a pigment.
Claim 31
Dependent Claim
21 words
The paint composition of claim 5 wherein said film forming binder comprises a water soluble or water dispersible film forming resin.
References Cited (Backward Citations)
US3067153A
Cited
US3652313A
Cited
US3429840A
Cited
US3477969A
Cited
US4059547A
Cited
US3870664A
Cited
US3985692A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-21 | 1982-11-20 | 1983-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-21 | 1986-11-20 | 1987-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-21 | 1990-11-20 | 1991-05-22 | $7700.00 | Window Closed / Lapsed |