Method of manufacturing semiconductor devices having isoelectronically built-in nitrogen and having the p-n junction formed subsequent to the deposition process
Assignee: US Philips Corp
•
Filing: 1977-05-19
•
Granted: 1979-05-15
•
Expires: 1997-05-19
Abstract
Abstract A method of manufacturing by liquid epitaxy III-V semiconductor crystals comprising a layer having isoelectronic nitrogen trapping centers. The method is characterized in that the deposition of the nitrogen-doped layer is succeeded by the deposition of a deep layer containing less nitrogen doping after which a p-n junction is formed in the first layer.
Inventors
- 👤 Daniel Diguet
- 👤 Bernard Legros
- 👤 Marc Mahieu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 03:08
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/40; H; H10; H10P; H10P14/00; H10P14/20; H10P14/26; H10P14/263; H10P14/265; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2909; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
136 words
A method of manufacturing an electroluminescent diode comprising the steps of: (a) providing a substrate; (b) epitaxially forming on said substrate a first layer containing at least one element of column III and at least one element of column V of the periodic table of elements and having a higher content of isolectronically incorporated nitrogen than said substrate; (c) providing on said first layer a second layer containing said elements of said first layer and having a lower content of isoelectronically incorporated nitrogen than said first layer; (d) during the formation of said first and second layers, providing thereto a first doping impurity type material; and (e) forming a p.n junction in said layers by introducing into said layers a second doping impurity which causes a portion of said layers to have an opposite conductivity type.
Claim 2
Independent Claim
136 words
A method of manufacturing an electroluminescent diode comprising the steps of: (a) providing a substrate; (b) epitaxially forming on said substrate a first layer containing at least one element of column III and at least one element of column V of the periodic table of elements and having a higher content of isolectronically incorporated nitrogen than said substrate; (c) providing on said first layer a second layer containing said elements of said first layer and having a lower content of isoelectronically incorporated nitrogen than said first layer; (d) during the formation of said first and second layers, providing thereto a first doping impurity type material; and (e) forming a p.n junction in said layers by introducing into said layers a second doping impurity which causes a portion of said layers to have an opposite conductivity type.
Claim 3
Dependent Claim
18 words
A method as in claim 1, wherein said second impurity is introduced locally via said second epitaxial layer.
Claim 4
Dependent Claim
17 words
A method as in claim 1, wherein said second doping impurity is introduced by a diffusion treatment.
Claim 5
Dependent Claim
22 words
A method as in claim 3, wherein said second impurity is introduced by an ion implantation thereof prior to the diffusion treatment.
Claim 6
Dependent Claim
37 words
A method as in claim 1, wherein the thickness of said first layer is greater than once the diffusion length of the minority carriers of the material in question and smaller than four times said diffusion length.
Claim 7
Dependent Claim
18 words
A method as in claim 1, wherein the thickness of said second layer is smaller than 10 μ.
Claim 8
Dependent Claim
17 words
A method as in claim 1, wherein said first and second layers consist essentially of gallium phosphide.
Claim 9
Dependent Claim
16 words
A method as in claim 1, wherein the atmosphere during the epitaxial deposition permanently contains hydrogen.
Claim 10
Dependent Claim
48 words
A method as in claim 1, wherein, during the deposition of said layers, the atmosphere consists of hydrogen-diluted hydrogen sulphide, the hydrogen sulphide content of which is such that the sulphur content in the resulting gallium phosphide has a content value of about 2×10 17 atoms per ccm.
Claim 11
Dependent Claim
51 words
A method as in claim 1, wherein, during the deposition of said layers, the atmosphere consists of hydrogen-diluted hydrogen sulphide, the hydrogen sulphide content of which is such that the sulphur content in the resulting gallium phosphide has a constant value of about 5×10 16 to 10 18 atoms per ccm.
Claim 12
Dependent Claim
25 words
A method as in claim 1, wherein, during the deposition of said nitrogen-doped layer, ammonia gas is added to the atmosphere which permanently contains hydrogen.
Claim 13
Dependent Claim
20 words
A method as in claim 11, wherein the ammonia partial pressure is about between 0.05 and 5 parts per 1000.
Claim 14
Dependent Claim
20 words
A method as in claim 12, wherein the ammonia partial pressure is about between 0.1 and 3 parts per 1000.
Claim 15
Dependent Claim
21 words
A method as in claim 11, wherein the overall pressure of the atmosphere containing ammonia is between 1 and 1.3 atmosphere.
Claim 16
Dependent Claim
57 words
A method as in claim 1, wherein said epitaxy is carried out in a vertical device starting from a given quantity of gallium phosphide dissolved in a given volume of gallium and, after adjusting the contact between said solution and the seed, the epitaxial deposition of the various layers is carried out by continuously cooling said volume.
Claim 17
Dependent Claim
20 words
A method as in claim 1, comprising the steps of forming a junction by zinc diffusion after the epitaxial method.
References Cited (Backward Citations)
US3462320A
Cited
US3893875A
Cited
US3646406A
Cited
US3725749A
Cited
US3964940A
Cited
US3935039A
Cited
US3931631A
Cited
US3984263A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |