Abstract Uniaxial hot-pressing of ceramic powders to produce monolithic shapes of non-uniform thickness is accomplished by employing a form, preformed to a shape which when properly oriented and uniaxially compressed to final density will deform orderly to assume the final desired shape, and hot-pressing it in a mold against preformed parts having surfaces exactly mating with the surfaces of the preform. Such mold parts have the same compaction ratio as the preform, and a coefficient of thermal expansion substantially equal to that of the preform, and are formed of a powdered composition which is non-reactive with the preform material under hot-pressing conditions. Suitable compositions for the mold part preforms are temporarily bonded mixtures of carbon or graphite powder and a powder material of the preform. The shapes may be slip cast or cold pressed and temporary binders of organic or inorganic material may be employed to give green strength to the parts.
A method of hot-pressing a refractory powder to a desired final shape of non-uniform thickness in cross-section by (1) making a first article preform of the powder temporarily bonded to a first shape having a surface contour which when oriented in a mold and uniaxially compressed to final density will deform in a predetermined manner to assume a final predetermined shape having a surface contour different from the shape of said first article preform; (2) hot-pressing said preform in a mold including a preformed matrix mold part having a surface exactly mating with a surface of the article preform, a compaction ration the same as that of the article preform, a coefficient of thermal expansion substantially equal to or greater than that of the article preform, and non-reactive with the article preform under hot-pressing conditions, such that upon completion of molding the article can be effectively separated from the matrix mold element, and the part has achieved its predetermined shape.
Claim 2
Independent Claim
160 words
A method of hot-pressing a refractory powder to a desired final shape of non-uniform thickness in cross-section by (1) making a first article preform of the powder temporarily bonded to a first shape having a surface contour which when oriented in a mold and uniaxially compressed to final density will deform in a predetermined manner to assume a final predetermined shape having a surface contour different from the shape of said first article preform; (2) hot-pressing said preform in a mold including a preformed matrix mold part having a surface exactly mating with a surface of the article preform, a compaction ration the same as that of the article preform, a coefficient of thermal expansion substantially equal to or greater than that of the article preform, and non-reactive with the article preform under hot-pressing conditions, such that upon completion of molding the article can be effectively separated from the matrix mold element, and the part has achieved its predetermined shape.
Claim 3
Dependent Claim
66 words
A method as in claim 1 in which the article preform is made from temporarily bonded ceramic material selected from the group of powders consisting of metal oxides, carbides, borides, nitrides, and oxynitrides, and in which the matrix mold element is formed of a carbon powder mixed with a ceramic material selected from the group of powders consisting of metal oxides, carbides, borides, nitrides, and oxynitrides.