Galvanized ferrous article for later application of paint coating
Assignee: Nippon Steel Corp
•
Filing: 1977-09-14
•
Granted: 1979-05-01
•
Expires: 1997-09-14
Abstract
Abstract A galvanized ferrous article having an adherent, ductile and highly corrosion resistant coating of galvanizing alloy which presents a matted surface which is free or substantially free of spangle and which is capable, upon application of a paint coating thereon, of strongly anchoring the paint coating to the galvanized coating, said galvanizing alloy comprising a zinc base alloy containing 3-10% preferably 3.5-10% by weight of aluminum and one or more elements of magnesium, calcium, beryllium, titanium and copper in amounts within the range specified in terms of the total weight of the lead and tin contained in the galvanizing alloy.
Inventors
- 👤 Misao Ohbu
- 👤 Kazuhiro Tano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:13
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; C; C23; C23C; C23C2/00; C23C2/04; C23C2/06; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12799; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
140 words
A method of producing galvanized ferrous strip having a zinc base alloy coating adapted for the later application of a paint coating on the surface thereof which comprises: moving a continuous ferrous strip through a molten zinc base alloy galvanizing bath and delivering galvanized strip from the molten galvanizing bath, said zinc base alloy galvanizing bath containing 4.85-10% by weight of aluminum, 0.007-0.10% by weight of lead, 0.005-0.02% by weight of tin, and one or more members selected from the group consisting of magnesium in an amount of 0.01-0.5% by weight, calcium in an amount of 0.01-0.3% by weight, beryllium in an amount of 0.01-0.2% by weight, titanium in an amount of 0.01-0.2% by weight and copper in an amount of 0.1-1.0% by weight, and the total weight of the other elements being limited to less than 0.5% by weight.
Claim 2
Independent Claim
140 words
A method of producing galvanized ferrous strip having a zinc base alloy coating adapted for the later application of a paint coating on the surface thereof which comprises: moving a continuous ferrous strip through a molten zinc base alloy galvanizing bath and delivering galvanized strip from the molten galvanizing bath, said zinc base alloy galvanizing bath containing 4.85-10% by weight of aluminum, 0.007-0.10% by weight of lead, 0.005-0.02% by weight of tin, and one or more members selected from the group consisting of magnesium in an amount of 0.01-0.5% by weight, calcium in an amount of 0.01-0.3% by weight, beryllium in an amount of 0.01-0.2% by weight, titanium in an amount of 0.01-0.2% by weight and copper in an amount of 0.1-1.0% by weight, and the total weight of the other elements being limited to less than 0.5% by weight.
Claim 3
Independent Claim
111 words
A method of producing galvanized ferrous strip having a Zn-Al alloy coating adapted for the later application of a paint coating on the surface thereof which comprises: moving a continuous ferrous strip through a molten Zn-Al alloy galvanizing bath and delivering galvanized strip from the molten galvanizing bath, said zinc base alloy galvanizing bath containing 4.85-10% by weight of aluminum, more than 0.10% by weight of lead, more than 0.02% of tin and one or more members selected from the group consisting of Mg, Ca, Be, Ti and Cu in amounts specified below in terms of the total weight of the lead and tin: 0.4A≦Mg≦0.5% 0.3A≦Ca≦0.3% 0.3A≦Be≦0.2% 0.3A≦Ti≦0.2% 1.5A≦Cu≦1.0% (wherein A=Pb(%)+5×Sn(%)).
Claim 4
Independent Claim
111 words
A method of producing galvanized ferrous strip having a Zn-Al alloy coating adapted for the later application of a paint coating on the surface thereof which comprises: moving a continuous ferrous strip through a molten Zn-Al alloy galvanizing bath and delivering galvanized strip from the molten galvanizing bath, said zinc base alloy galvanizing bath containing 4.85-10% by weight of aluminum, more than 0.10% by weight of lead, more than 0.02% of tin and one or more members selected from the group consisting of Mg, Ca, Be, Ti and Cu in amounts specified below in terms of the total weight of the lead and tin: 0.4A≦Mg≦0.5% 0.3A≦Ca≦0.3% 0.3A≦Be≦0.2% 0.3A≦Ti≦0.2% 1.5A≦Cu≦1.0% (wherein A=Pb(%)+5×Sn(%)).
References Cited (Backward Citations)
US1764132A
Cited
US3320040A
Cited
GB1127407A
Cited
US3325282A
Cited
US3505043A
Cited
US4056657A
Cited
US4056366A
Cited
US4029478A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |