Method of making particles useful for removal of alkali and alkaline earth metals from light metal melts
Assignee: Rio Tinto Switzerland AG
•
Filing: 1976-01-14
•
Granted: 1979-05-01
•
Expires: 1996-01-14
Abstract
Abstract Alkali and alkaline earth metals are removed from light metal melts by causing the melt to flow through a bed consisting of granules of a mechanically resistant and chemically inert carrier particles which have a coating of carbon. A suitable granule is prepared by mixing particles of inert carrier material with a cokable carbonaceous material and heating the mixture in a closed reaction vessel to the carbonaceous material and produce an adherent coating of carbon on the carrier particles of the granulate. The density of the coated granules is greater than 2.5 g/cm3.
Inventors
- 👤 Alfred Steinegger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:35
CPC Classifications
C; C22; C22B; C22B21/00; C22B21/06; C22B21/066; C22B9/00; C22B9/05; C22B9/055
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
115 words
A method for manufacturing carbon-coated particles useful for the removal of alkali and alkaline earth metal from molten primary aluminum which comprises the steps of: heating mechanically resistant, chemically inert carrier particles between 0.5 cm. and 25 cm. in diameter, with particles of cokable carbonaceous material, less than 5 mm. in diameter, wherein the carrier particles and the cokable particles are arranged in a plurality of horizontal, superimposed, alternate layers, for two to twelve hours at a coking temperature in the range of 750° C. to 1,200° C., under the exclusion of air, until a hard adherent coating of carbon, 0.1 mm. to 10 mm. thick, has formed on the granules of said carrier particles.
Claim 2
Independent Claim
115 words
A method for manufacturing carbon-coated particles useful for the removal of alkali and alkaline earth metal from molten primary aluminum which comprises the steps of: heating mechanically resistant, chemically inert carrier particles between 0.5 cm. and 25 cm. in diameter, with particles of cokable carbonaceous material, less than 5 mm. in diameter, wherein the carrier particles and the cokable particles are arranged in a plurality of horizontal, superimposed, alternate layers, for two to twelve hours at a coking temperature in the range of 750° C. to 1,200° C., under the exclusion of air, until a hard adherent coating of carbon, 0.1 mm. to 10 mm. thick, has formed on the granules of said carrier particles.
Claim 3
Independent Claim
105 words
A method for manufacturing carbon-coated particles useful for the removal of akali and alkaline earth metal from molten primary aluminum, which comprises the steps of distributing mechanically resistant, chemically inert carrier particles between 0.5 cm. and 25 cm. in diameter in substantial proximity to particles of cokable carbonaceous material less than 5 mm. in diameter, heating said particles for two to twelve hours at a coking temperature in the range of 750° C. to 1,200° C., under exclusion of air, until a hard and adherent coating of carbon 0.1 mm. to 10 mm. thick has formed on each of the resulting granules of carrier particles.
Claim 4
Independent Claim
105 words
A method for manufacturing carbon-coated particles useful for the removal of akali and alkaline earth metal from molten primary aluminum, which comprises the steps of distributing mechanically resistant, chemically inert carrier particles between 0.5 cm. and 25 cm. in diameter in substantial proximity to particles of cokable carbonaceous material less than 5 mm. in diameter, heating said particles for two to twelve hours at a coking temperature in the range of 750° C. to 1,200° C., under exclusion of air, until a hard and adherent coating of carbon 0.1 mm. to 10 mm. thick has formed on each of the resulting granules of carrier particles.
Claim 5
Dependent Claim
29 words
A method according to claim 1, in which the cokable carbonaceous material comprises a material selected from the group consisting of coal tar pitch, pulverised coal, and petroleum coke.
Claim 6
Dependent Claim
23 words
A method according to claim 1, including, before the reaction, mixing the carrier wetted and wetted carbonaceous particles together as thoroughly as possible.
Claim 7
Dependent Claim
23 words
A method according to claim 1, wherein said carrier particles are recycled carbon coated particles produced by a process according to claim 1.
Claim 8
Dependent Claim
20 words
A method according to claim 1, in which the coated granulate has a density greater than 2.5 g/cm 3 .
Claim 9
Dependent Claim
17 words
A method according to claim 1, in which the inert carrier material is an inert ceramic material.
Claim 10
Dependent Claim
29 words
A method according to claim 1, in which the carrier material comprises a material selected from the group consisting of corundum, magnesite, zirconium oxide, zirconium silicate, basalt, and bauxite.
References Cited (Backward Citations)
CA672916A
Cited
US3172757A
Cited
US2626875A
Cited
US3305351A
Cited
US3528801A
Cited
US3790410A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |