Process for production of a water-in-oil polymer emulsion having an excellent fluidity using an acrylic monomer containing quarternary ammonium salt
Assignee: Sanyo Chemical Industries Ltd
•
Filing: 1977-12-22
•
Granted: 1979-05-01
•
Expires: 1997-12-22
Abstract
Abstract A water-in-oil polymer emulsion having an excellent fluidity can be obtained by a process which comprises dispersing an aqueous solution of at least one (meth)acrylic monomer containing a quaternary ammonium salt or a tertiary amine salt in a hydrophobic organic liquid in the presence of an oil-in-water type nonionic surfactant, and heating the resulting dispersion to a temperature of at least 40° C. to polymerize the monomer mixture.
Inventors
- 👤 Yasuo Shibahara
- 👤 Masashi Okada
- 👤 Kimihiko Noda
- 👤 Yasuo Osuga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:01
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/34; D21H17/41; D21H17/44; D21H17/45; D21H17/455; C; C02; C02F; C02F1/00; C02F1/52; C02F1/54; C08; C08F; C08F2/00; C08F2/32
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
269 words
A process for producing a water-in-oil polymer emulsion comprising forming a dispersion of 30 to 70% by weight of (a) an aqueous solution of at least one ethylenically unsaturated monomer and (b) 70 to 30% by weight of a hydrophobic organic liquid in the presence of a nonionic oil-in-water surfactant, present in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, said monomer comprising: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR2## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms; and X - is an anion, (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer, and heating the resulting dispersion at a temperature of at least 40° C. whereby said monomer is polymerized to obtain a water-in-oil polymer emulsion, a 1% aqueous solution of which has a viscosity of at least 100 cps, wherein a 30% by weight resulting polymer emulsion has an apparent viscosity of at most 100 cps at 30° C. measured by Brookfield viscometer using No. 1 rotor at 60 r.p.m.
Claim 2
Dependent Claim
269 words
A process for producing a water-in-oil polymer emulsion comprising forming a dispersion of 30 to 70% by weight of (a) an aqueous solution of at least one ethylenically unsaturated monomer and (b) 70 to 30% by weight of a hydrophobic organic liquid in the presence of a nonionic oil-in-water surfactant, present in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, said monomer comprising: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR2## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms; and X - is an anion, (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer, and heating the resulting dispersion at a temperature of at least 40° C. whereby said monomer is polymerized to obtain a water-in-oil polymer emulsion, a 1% aqueous solution of which has a viscosity of at least 100 cps, wherein a 30% by weight resulting polymer emulsion has an apparent viscosity of at most 100 cps at 30° C. measured by Brookfield viscometer using No. 1 rotor at 60 r.p.m.
Claim 3
Dependent Claim
21 words
The process of claim 1, wherein said nonionic surfactant is a nonionic surfactant having an HLB value of at least 7.
Claim 4
Dependent Claim
14 words
The process of claim 1, wherein said nonionic surfactant is a polyoxyethylene nonionic surfactant.
Claim 5
Dependent Claim
39 words
The process of claim 3, wherein said polyoxyethylene nonionic surfactant is a polyoxyethylene derivative of a higher aliphatic alcohol; a higher fatty acid, or an ester of a higher fatty acid with a polyhydric alcohol or an alkyl phenol.
Claim 6
Dependent Claim
34 words
The process of claim 1, wherein said nonionic surfactant is a polyoxyethylene derivative of a C 8 -C 24 aliphatic alcohol or a polyethylene glycol ester of a C 8 -C 24 fatty acid.
Claim 7
Dependent Claim
21 words
The process of claim 1, wherein said nonionic surfactant is a polyoxyethylene derivative of a C 8 -C 24 aliphatic alcohol.
Claim 8
Dependent Claim
44 words
The process of claim 1, wherein said nonionic surfactant has an HLB value satisfying the following equation: 1.3/100b+7≦a≦1.3/100b+11 wherein a is the HLB of the nonionic surfactant and b is the mol % of the monomer having formula (I) based on the total monomer.
Claim 9
Dependent Claim
101 words
The process of claim 1, wherein said monomer has the formula (II): ##STR3## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms; a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms and X - is an anion.
Claim 10
Dependent Claim
27 words
The process of claim 1, wherein said monomer is selected from the group consisting of acryloyloxyalkyltrialkylammonium salts, methacryloyloxyalkyltrialkylammonium salts, salts of dialkylaminoalkylacrylates, and salts of dialkylaminoalkyl methacrylates.
Claim 11
Dependent Claim
15 words
The process of claim 1, wherein said monomer is an acryloyloxyalkyltrialkylammonium salt or methacryloyloxyalkyltrialkylammonium salt.
Claim 12
Dependent Claim
14 words
The process of claim 1, wherein said hydrophilic comonomer is a nonionic vinyl monomer.
Claim 13
Dependent Claim
24 words
The process of claim 11, wherein said nonionic vinyl monomer is selected from the group consisting of acrylamide, methacrylamide, hydroxyethyl acrylate, and hydroxyethyl methacrylate.
Claim 14
Dependent Claim
12 words
The process of claim 11, wherein said nonionic vinyl monomer is acrylamide.
Claim 15
Dependent Claim
32 words
The process of claim 1, wherein the amount of the monomer having the formula (I) is 5 to 100% by weight and the amount of the hydrophilic comonomer is 0-95% by weight.
Claim 16
Dependent Claim
32 words
The process of claim 1, wherein the amount of the monomer having the formula (I) is 20 to 100% by weight and the amount of the hydrophilic comonomer is 0-80% by weight.
Claim 17
Dependent Claim
23 words
The process of claim 1, wherein the amount of the nonionic surfactant is 10 to 19% by weight of the hydrophobic organic liquid.
Claim 18
Dependent Claim
23 words
The process of claim 1, wherein the amount of the nonionic surfactant is 15 to 19% by weight of the hydrophobic organic liquid.
Claim 19
Dependent Claim
20 words
The process of claim 1, wherein said aqueous solution contains the monomer in concentration of 10 to 80% by weight.
Claim 20
Dependent Claim
205 words
A water-in-oil polymer emulsion obtained by heating a dispersion of 30 to 70% by weight of an aqueous solution of an ethylenically unsaturated monomer component and 70 to 30% by weight of a hydrophobic organic liquid containing a nonionic oil-in-water surfactant in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, to a temperature of at least 40° C. to polymerize said monomer component, wherein said monomer component comprises: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR4## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms and X - is an anion, (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer.
Claim 21
Dependent Claim
205 words
A water-in-oil polymer emulsion obtained by heating a dispersion of 30 to 70% by weight of an aqueous solution of an ethylenically unsaturated monomer component and 70 to 30% by weight of a hydrophobic organic liquid containing a nonionic oil-in-water surfactant in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, to a temperature of at least 40° C. to polymerize said monomer component, wherein said monomer component comprises: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR4## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms and X - is an anion, (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer.
Claim 22
Dependent Claim
38 words
The emulsion of claim 19, wherein said emulsion, when it contains 30% polymer by weight, has an apparent viscosity of at most 100 cps. at 30° C. measured by Brookfield viscometer using rotor No. 1 at 60 r.p.m.
Claim 23
Independent Claim
235 words
A method for separating finely divided solids from an aqueous suspension thereof which comprises treating the suspension by adding thereto a sufficient amount to promote flocculation of the suspension of a water-in-oil polymer emulsion, obtained by heating a dispersion of 30 to 70% by weight of an aqueous solution of an ethylenically unsaturated monomer component and 70 to 30% by weight of a hydrophobic organic liquid containing a nonionic oil-in-water surfactant in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, to a temperature of at least 40° C. to polymerize said monomer component, wherein said monomer component comprises: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR5## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms and X - is an anion; (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer.
Claim 24
Independent Claim
235 words
A method for separating finely divided solids from an aqueous suspension thereof which comprises treating the suspension by adding thereto a sufficient amount to promote flocculation of the suspension of a water-in-oil polymer emulsion, obtained by heating a dispersion of 30 to 70% by weight of an aqueous solution of an ethylenically unsaturated monomer component and 70 to 30% by weight of a hydrophobic organic liquid containing a nonionic oil-in-water surfactant in an amount of at least 8% and less than 20% by weight of the hydrophobic organic liquid, to a temperature of at least 40° C. to polymerize said monomer component, wherein said monomer component comprises: (1) 1 to 100% by weight of a monomer having the formula (I) ##STR5## wherein R 1 is H or CH 3 ; R 2 and R 3 are independently an alkyl group having 1 to 4 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms; R 4 is H, an alkyl group having 1 to 4 carbon atoms, a hydroxyalkyl group having 2 to 4 carbon atoms or a benzyl group; A is O or NH; B is an alkylene group having 1 to 4 carbon atoms or a hydroxyalkylene group having 2 to 4 carbon atoms and X - is an anion; (2) 0 to 99% by weight of another hydrophilic comonomer and (3) 0 to 30% by weight of a hydrophobic comonomer.
References Cited (Backward Citations)
US3284393A
Cited
US3372149A
Cited
DE2446584A1
Cited
GB1468587A
Cited
US4064091A
Cited
US3957739A
Cited
US4038233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |